Flame retardant enhanced PET material having high glowing filament temperature and preparation method of material

A high-glow wire and flame retardant technology, which is applied in the field of flame-retardant reinforced PET materials and its preparation, can solve the problems of toughness of thin-walled materials that are difficult to guarantee, can't prevent spontaneous combustion, and difficult to add disasters, etc., to achieve good toughness , Toughness improvement, high safety effect

Inactive Publication Date: 2015-06-03
SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Prolonged contact will cause its appearance to ignite spontaneously due to excessive temperature and cause fire, which will bring disasters that are difficult to add to the masses.
At present, the simple flame retardant modification of PET through flame retardants can only simply prevent the burning of the m

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame retardant enhanced PET material having high glowing filament temperature and preparation method of material
  • Flame retardant enhanced PET material having high glowing filament temperature and preparation method of material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) 45 parts of PET, 0.3 part of silicone, 0.1 part of antioxidant 1010, 0.2 part of antioxidant 1076, 0.2 part of ionomer of nucleating agent ethylene / methacrylic acid copolymer, 20 parts of red phosphorus, 5 Toughening agent ethylene-acrylic acid ester-glycidyl acrylate terpolymer, mixed at high speed with a high-speed mixer, the rotating speed is 800rpm, normal temperature, and the mixing time is 6min;

[0030] (2) Pour the mixture obtained in step (1) into the main feed port of the screw extruder, and then add 30 parts of continuous glass fiber (12 μm in diameter) through the glass fiber inlet at the rear end to control the temperature of the extruder At 260-280°C, the mixed material is pelletized through a twin-screw extruder to obtain a flame-retardant reinforced PET material with a high glow wire temperature. The relevant performance tests of the product are shown in Table 1.

Embodiment 2

[0032] (1) Mix 72 parts of PET, 0.3 parts of lubricant PETS, 0.2 parts of antioxidant 1010, 0.4 parts of antioxidant 1076, 0.5 parts of nucleating agent saturated carboxylic acid sodium salt, 10 parts of decabromodiphenylethane and 5 parts Antimony trioxide (the weight ratio of decabromodiphenylethane to antimony trioxide is 2:1), 3 parts of ethylene-acrylate-glycidyl acrylate are mixed at high speed with a high-speed mixer at a speed of 1000rpm, at room temperature, mixed The time is 3 minutes;

[0033] (2) Pour the mixture obtained in step (1) into the main feed port of the screw extruder, and then add 10 parts of continuous glass fiber (12 μm in diameter) through the glass fiber inlet at the rear end to control the temperature of the extruder At 260-280°C, the mixed material is pelletized through a twin-screw extruder to obtain a flame-retardant reinforced PET material with a high glow wire temperature.

Embodiment 3

[0035] (1) Mix 60 parts of PET, 0.3 parts of stearyl alcohol, 0.5 parts of antioxidant P262, 0.7 parts of saturated carboxylic acid sodium salt, 20 parts of red phosphorus, and 5 parts of ethylene-acrylate-glycidyl acrylate with a high-speed mixer Mixing, rotating speed is 800rpm, room temperature, mixing time is 6min;

[0036] (2) Pour the mixture obtained in step (1) into the main feed port of the screw extruder, and then add 15 parts of continuous glass fiber (12 μm in diameter) through the glass fiber inlet at the rear end to control the temperature of the extruder At 260-280 ° C, the mixed material is drawn and pelletized by a twin-screw extruder to obtain a flame-retardant reinforced PET material with a high glow wire temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of high polymer materials and relates to a flame retardant enhanced PET material having a high glowing filament temperature and a preparation method of the material. The material is prepared from the following components in parts by weight: 45-72 parts of PET, 10-30 parts of glass fibers, 0.3-0.6 part of lubricant, 0.3-0.6 part of antioxidant, 0.2-0.7 part of nucleating agent, 15-20 parts of flame retardant and 3-5 parts of flexibilizer. The material has the characteristics of high strength, good flame retardancy, high glowing filament temperature, high temperature resistance, easy molding and the like, and has a wide application prospect in the household appliance industry.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a flame-retardant reinforced PET material with high glow wire temperature and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET) is an engineering plastic with excellent comprehensive properties. PET has excellent mechanical properties, high rigidity, high hardness, good toughness, impact resistance, friction resistance and creep resistance. Good chemical resistance, soluble in cresol, concentrated sulfuric acid, nitrobenzene, trichloroacetic acid, chlorophenol, insoluble in methanol, ethanol, acetone, alkanes, etc. It itself is mainly blown into various bottles, used as containers, and spun into fibers and other applications. As an engineering plastic, it can replace nylon and polybutylene terephthalate in the electronic appliances and automobile industries. [0003] At present, there are many flame retardant literatures on PE...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L23/08C08K13/04C08K7/14C08K5/098C08K5/03C08K3/22C08K3/02B29B9/06B29C47/92B29C48/92
Inventor 杨桂生孙鹏
Owner SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap