High-strength synchronous belt and manufacturing method thereof

A synchronous belt, high-strength technology, applied in belts, transmission belts, mechanical equipment, etc., can solve the problem of unsatisfactory shear strength, high temperature resistance, wear resistance, reduced transmission power and service life, low strength and elasticity of synchronous belts And other problems, to achieve the effect of good wear resistance, excellent dynamic fatigue performance, excellent oil resistance

Active Publication Date: 2015-06-03
NINGBO FULONG SYNCHRONOUS BELT
View PDF10 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, under the existing processing conditions, the strength and elasticity of the synchronous belt made of HNBR rubber are low, and there are inevitably microscopic defects such as microcracks, impurities, and microvoids inside; and the shear strength and High temperature resistance and wear resistance are not ideal, which may easily lead to problems such as tooth loss, tooth deformation, transmission power and service life reduction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength synchronous belt and manufacturing method thereof
  • High-strength synchronous belt and manufacturing method thereof
  • High-strength synchronous belt and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The high-strength synchronous belt of the present embodiment comprises a synchronous belt skeleton and a film pasted on the outside of the synchronous belt skeleton, and the raw material of the film includes the following components by weight:

[0041]

[0042] The above-mentioned carbon black is a mixture of high wear-resistant carbon black N330 and fast extrusion carbon black N550 at a ratio of 1:1.5 by weight.

[0043] The preparation method of above-mentioned high-strength synchronous belt comprises the following steps:

[0044] (1) Film preparation

[0045] Hydrogenated nitrile butadiene rubber and chloroprene rubber are respectively thinly passed 4 times on the open mill, then the hydrogenated nitrile butadiene rubber after mastication and neoprene are mixed and thinly passed through and beaten triangular bag 10 times;

[0046] Add plasticizer TOTM, antioxidant 4010, trans 1,4-polyisoprene, methacryloxysilane, aramid pulp, carbon black to the mixture of hydrog...

Embodiment 2

[0056] The high-strength synchronous belt of the present embodiment comprises a synchronous belt skeleton and a film pasted on the outside of the synchronous belt skeleton, and the raw material of the film includes the following components by weight:

[0057]

[0058] The above-mentioned carbon black is a mixture of high wear-resistant carbon black N330 and fast extrusion carbon black N550 at a ratio of 1:0.5 by weight.

[0059] The preparation method of above-mentioned high-strength synchronous belt comprises the following steps:

[0060] (1) Film preparation

[0061] Hydrogenated nitrile butadiene rubber and chloroprene rubber are thinly passed 5 times respectively on the open mill, then the hydrogenated nitrile butadiene rubber after mastication and neoprene are mixed and thinly passed through and beaten triangular bag 12 times;

[0062] Add plasticizer Thiokol TP-95, antioxidant MB, trans-1,4-polyisoprene, methacryloxysilane, aramid pulp to the above mixture of hydroge...

Embodiment 3

[0069] The high-strength synchronous belt of the present embodiment comprises a synchronous belt skeleton and a film pasted on the outside of the synchronous belt skeleton, and the raw material of the film includes the following components by weight:

[0070]

[0071]

[0072] The above-mentioned carbon black is a mixture of high wear-resistant carbon black N330 and fast extrusion carbon black N550 in a ratio of 1:2 by weight.

[0073] The preparation method of above-mentioned high-strength synchronous belt comprises the following steps:

[0074] (1) Film preparation

[0075] Hydrogenated nitrile butadiene rubber and chloroprene rubber are thinly passed 6 times respectively on the open mill, then the hydrogenated nitrile butadiene rubber after mastication and neoprene are mixed and thinly passed through and beaten triangular bag 11 times;

[0076] Add plasticizer Adiksizer C-9N, antioxidant Naugard445, trans 1,4-polyisoprene, methacryloxysilane, aramid pulp to the mixtu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-strength synchronous belt. The synchronous belt comprises a synchronous belt framework and an adhesive piece attached to the outer side of the synchronous belt frame. The adhesive piece comprises the following components in parts by weight: 70-90 parts of hydrogenated butadiene-acrylonitrile rubber, 10-30 parts of chloroprene rubber, 14-25 parts of trans 1, 4-polyisoprene, 4-8 parts of methylacryloyl silane, 5-15 parts of aramid pulp, 10-20 parts of reinforced fiber SP-6701, 20-40 parts of carbon black, 4-7 parts of peroxide crosslinking agent, 1-4 parts of assistant crosslinking agent, 0.5-1.5 parts of hexamine, 2-5 parts of plasticizer and 1-3 parts of antiaging agent. The invention also relates to a manufacturing method of the synchronous belt. According to the high-strength synchronous belt and the manufacturing method thereof, the hydrogenated butadiene-acrylonitrile rubber and the chloroprene rubber are used together, so that the performances of the hydrogenated butadiene-acrylonitrile rubber and the chloroprene rubber are complementary, and thus the wear resistance and the heat resistance of the adhesive piece of the synchronous belt can be effectively improved; the shear strength and the quality stability of the synchronous belt are improved by use of the trans 1, 4-polyisoprene, the methylacryloyl silane and the aramid pulp.

Description

technical field [0001] The invention relates to the technical field of synchronous belts, specifically a high-strength synchronous belt with good mechanical properties, and also relates to a preparation method of the high-strength synchronous belt. Background technique [0002] The synchronous belt is an endless belt with equally spaced teeth on the inner peripheral surface. When rotating, the power is transmitted through the meshing of the belt teeth and the gear teeth. The synchronous belt combines the advantages of belt drive, chain drive and gear drive, and has the advantages of high transmission efficiency, accurate transmission ratio, large transmission ratio range, stable transmission, small force on the shaft, low noise, and energy saving. [0003] The main body of early synchronous belts was mostly made of polyurethane rubber. Polyurethane rubber has the advantages of general liquid rubber, good wear resistance, simple process, and convenient molding. However, polyu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F16G1/28C08L15/00C08L11/00C08L47/00C08K13/02C08K5/14C08K3/04C08K5/3492C08K5/17D01F6/54D01F1/10B29D29/08B29C35/02
CPCB29D29/08C08K2201/014C08L15/00C08L2201/08C08L2205/035C08L2205/16D01F1/10D01F6/18C08L11/00C08L47/00C08L77/10C08K13/02C08K5/14C08K3/04C08K5/3492
Inventor 林胤邓樱周云沈光辉
Owner NINGBO FULONG SYNCHRONOUS BELT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap