Self-supported silicon base anode material with multilayer thin film of lithium ion battery and preparation method thereof

A technology for silicon-based negative electrode materials and lithium-ion batteries, applied in battery electrodes, secondary batteries, electrode carriers/collectors, etc., can solve problems such as low area specific capacity and complicated preparation process, achieve high area specific capacity, improve The effect of mass ratio capacity and dense arrangement

Active Publication Date: 2015-06-03
ZHEJIANG UNIV
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of its preparation process is very complicated, and the area specific capacity is low; and the current research is to optimize the structural design at the microstructure level, and no one has done the work of synergistically optimizing the material structure and composition at the macroscopic and microscopic levels.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-supported silicon base anode material with multilayer thin film of lithium ion battery and preparation method thereof
  • Self-supported silicon base anode material with multilayer thin film of lithium ion battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The preparation method of the lithium-ion battery self-supporting silicon-based negative electrode material of multilayer thin film comprises the following steps:

[0025] 1) Disperse the high molecular polymer in an organic solvent, magnetically stir for 18 to 48 hours and then ultrasonically treat it for 30 to 60 minutes to obtain a 5 to 15wt% high molecular polymer solution;

[0026] 2) Disperse the high molecular polymer and nano-silica powder with a mass ratio of 1:1~12:1 in the same organic solvent, magnetically stir for 18~48 hours, and ultrasonically treat for 30~60 minutes to obtain the high molecular polymer and Nano silicon powder dispersion;

[0027] 3) Electrospinning is carried out using a coaxial spinning device. The inner tube is a dispersion of high molecular polymer and nano-silica powder, and the outer tube is a high molecular polymer solution. First, inject the high molecular polymer solution for 40 minutes. Stop the injection, start injecting the h...

Embodiment 1

[0031] 1) Dissolve 1.5g of polyacrylonitrile in dimethyl diamide, stir it magnetically for 24 hours and then sonicate it for 30 minutes to obtain an 8wt% polymer solution;

[0032] 2) Disperse nano-silica powder and polyacrylonitrile in the same organic solvent, magnetically stir for 24 hours, and then ultrasonically treat for 30 minutes to obtain a dispersion of high molecular polymer and nano-silica powder;

[0033]3) Prepare multi-layer films by spinning with an electrospinning machine: adjust and set appropriate positive high voltage 18Kv, negative high voltage -2kV, ambient temperature 30 o C, the humidity is 40%, and the high-speed directional attachment is selected as the receiving device. Using a coaxial spinning device, the inner tube is a high molecular polymer and nano silicon powder dispersion, and the outer tube is a high molecular polymer solution. The distance from the nozzle of the coaxial spinning device to the receiving device is 15 cm. First inject...

Embodiment 2

[0038] 1) Dissolve 1.5g of polyvinylpyrrolidone in dimethyl diamide, stir it magnetically for 24 hours and then sonicate it for 30 minutes to obtain a 5wt% polymer solution;

[0039] 2) Disperse nano-silica powder and polyvinylpyrrolidone in the same organic solvent, magnetically stir for 24 hours, and then ultrasonically treat for 30 minutes to obtain a dispersion of high molecular polymer and nano-silica powder;

[0040] 3) Prepare multi-layer films by spinning with an electrospinning machine: adjust and set appropriate positive high voltage 15Kv, negative high voltage -2kV, ambient temperature 40 o C, the humidity is 40%, and the high-speed directional attachment is selected as the receiving device. Using a coaxial spinning device, the inner tube is a high molecular polymer and nano silicon powder dispersion, and the outer tube is a high molecular polymer solution. The distance from the nozzle of the coaxial spinning device to the receiving device is 10 cm. Fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a self-supported silicon base anode material with a multilayer thin film of a lithium ion battery and a preparation method of the anode material. The silicon base anode material with the multilayer thin film of the lithium ion battery is formed by compounding silicon nanoparticles and carbon nanofibers, the mass ratio of silicon to carbon is 1:(0.5 to 1:6), and the thickness ratio of a carbon fiber layer to a silicon-carbon compound fiber layer is 1:1 to 1:5. The preparation method comprises the following steps: at first, respectively dispersing a mixture formed by the silicon nanoparticles and an organic macromolecule polymer and the organic macromolecule polymer into an organic solvent, and fully stirring to obtain uniform suspension and solution respectively; then, controlling electrostatic spinning injection quantity and time to obtain a multilayer periodic structure of carbon-silicon-carbon compound-carbon-silicon-carbon compound......carbon; carrying out carbonization treatment in a protective atmosphere to prepare the self-supported silicon base anode material with the multilayer thin film of the lithium ion battery. The self-supported silicon base anode material disclosed by the invention has the advantages of self support, high capacity, good cycling stability, simple preparation and so on.

Description

technical field [0001] The invention relates to a multilayer film lithium ion battery self-supporting silicon-based negative electrode material and a preparation method thereof, belonging to the field of energy materials. Background technique [0002] With the widespread application of electric vehicles, hybrid vehicles, and solar and wind power generation, high-performance storage devices have become increasingly important. Lithium-ion batteries have the advantages of high energy density, good cycle performance, high specific energy, and little environmental pollution, so they are currently one of the most important energy storage devices. [0003] Lithium-ion battery refers to a rechargeable and dischargeable high-energy battery in which Li+ is intercalated and extracted from positive and negative electrode materials. At present, the positive electrode materials generally use lithium intercalation compounds, such as LiCoO 2 , LiNiO 2 , LiMnO 2 etc.; its ne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/134H01M4/1395H01M4/66
CPCH01M4/134H01M4/1395H01M4/366H01M4/386H01M4/62H01M4/628H01M10/0525Y02E60/10
Inventor 姜银珠王宝琦刘杨崔迪严密
Owner ZHEJIANG UNIV