Degradable seedling culturing bowl prepared with straw and preparation method thereof

A seedling pot and straw technology, which is applied in the field of degradable seedling pot and its preparation, can solve the problems of affecting the health of eaters, excessive pesticide residues in vegetables, etc., and achieve a pot with moderate wall strength, convenient pot seedling transportation, and good water storage performance. Effect

Inactive Publication Date: 2015-08-12
东营市康森秸秆制品有限公司
View PDF11 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the seedling pot is made of biological pesticide residues, it is easy to cause excessive pesticide residues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A degradable seedling pot prepared from straw, prepared from the following raw materials in parts by weight:

[0032] 75 parts of sweet potato straw, 75 parts of wheat straw, 75 parts of soybean straw, 75 parts of cotton straw, 7.5 parts of astragalus dregs, 2.5 parts of isatidis residue, and 0.8 parts of additives.

[0033] The preparation method of the degradable seedling pot prepared from straws comprises the following steps:

[0034] (1) Radix Astragali residues and Radix Radix Radix residues are naturally air-dried until the water content is 15-25wt%, crushed to a particle size of 100 mesh, and set aside;

[0035] (2) Sweet potato stalks, wheat stalks, soybean stalks, and cotton stalks are crushed to 100 mesh, and the moisture content is kept less than 3wt%;

[0036] (3) Astragalus residues and Radix Radix residues are added to the straw powder, mixed together, and an aqueous solution of polyvinyl alcohol additive with a mass fraction of 10% is added;

[0037] (4...

Embodiment 2

[0040] A degradable seedling pot prepared from straw, prepared from the following raw materials in parts by weight:

[0041] 90 parts of sweet potato stalks, 60 parts of wheat stalks, 90 parts of soybean stalks, 60 parts of cotton stalks, 6 parts of astragalus residues, 3 parts of isatidis residues, 0.4 parts of additives.

[0042] The preparation method of the degradable seedling pot prepared from straws comprises the following steps:

[0043] (1) Radix Astragali residues and Radix Radix Radix residues are naturally air-dried until the water content is 15-25wt%, crushed to a particle size of 100 mesh, and set aside;

[0044] (2) Sweet potato stalks, wheat stalks, soybean stalks, and cotton stalks are crushed to 60 meshes, and the moisture content is kept less than 3wt%;

[0045] (3) Astragalus residues and Radix Radix residues are added to the straw powder, mixed evenly, and a 25% hydroxypropylmethylcellulose aqueous solution is added;

[0046] (4) Extrude under the pressur...

Embodiment 3

[0049] A degradable seedling pot prepared from straw, prepared from the following raw materials in parts by weight:

[0050] 60 parts of sweet potato stalks, 90 parts of wheat stalks, 60 parts of soybean stalks, 90 parts of cotton stalks, 9 parts of astragalus residues, 3 parts of isatidis residues, 1 part of additives.

[0051] The preparation method of the degradable seedling pot prepared from straws comprises the following steps:

[0052] (1) Radix Astragali residues and Radix Radix Radix residues are naturally air-dried until the water content is 15-25wt%, crushed to a particle size of 100 mesh, and set aside;

[0053] (2) Sweet potato stalks, wheat stalks, soybean stalks, and cotton stalks are crushed to 80 meshes, and the water content is kept less than 3wt%;

[0054](3) Astragalus residues and Radix Radix residues are added to the straw powder, mixed together, and an aqueous solution of polyvinyl alcohol with a mass fraction of 10% is added;

[0055] (4) Extrude under...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Grinding particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of agricultural waste cyclic utilization, in particular to a degradable seedling culturing bowl prepared with straw and a preparation method thereof. The degradable seedling culturing bowl prepared with the straw is prepared with, by weight, 50-100 parts of sweet potato straw, 50-100 parts of wheat straw, 50-100 parts of soybean straw, 50-100 parts of cotton straw, 5-10 parts of astragalus membranaceus herb residues, 1-5 parts of isatis root residues and 0.2-2 parts of addition agents. The seedling culturing bowl is good in water storage performance and medium in blow wall strength, unshelling is not needed after seedlings culturing is completed, the bowl is not harmful to roots and seedlings, the seedlings in the bowl are convenient to transport, integrated transplantation is facilitated, the bowl can decompose in soil naturally, no pollution is caused to the soil, and a certain fertilizing effect is achieved.

Description

technical field [0001] The invention belongs to the field of recycling agricultural waste, and in particular relates to a degradable seedling pot prepared from straw and a preparation method thereof. Background technique [0002] Straw fiber is one of the huge regenerative biopolymer resources in nature. The annual output of straw fiber in the world is about 40×10 tons, and the annual output of straw resources in China reaches 790 million tons. People pay more and more attention to the huge waste of resources and serious environmental pollution caused by burning or burying straw. At present, there have been many reports on the utilization of straw, such as fertilizer, new energy, animal feed, degradable material, base material for cultivating edible fungi, and building material. [0003] Patent CN104025945A discloses a degradable seedling pot and a production method thereof. The seedling pot uses biopesticide fermentation residue as the main raw material, adds some straw p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A01G9/10
CPCA01G9/0291A01G24/00A01G24/60
Inventor 王保辉刘玉峰杨国岗
Owner 东营市康森秸秆制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap