An artificial stone and high-gloss technology, which is applied in the field of high-gloss flame-retardant, heat-resistant and wear-resistant artificial stone, can solve the problems of poor flame-retardant and heat-resistant performance, low strength, and poor surface gloss, so as to improve wear resistance, Improve flame retardant and heat resistance, increase hardness and bending resistance

Inactive Publication Date: 2015-08-19
新疆东方环宇投资(集团)工业建材有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current artificial stone still has the disadvantages of low strength, poor surface abrasion resistance, weak flame retardancy and heat resistance, and poor surface gloss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A high-gloss flame-retardant, heat-resistant and wear-resistant artificial stone is composed of the following ingredients in parts by weight:

[0040] Talcum powder 20 parts

[0041] Montmorillonite 70 parts

[0042] Barium sulfate 10 parts

[0043] Quartz 30 parts

[0044] Wollastonite 20 parts

[0045] 20 parts fine sand

[0046] 6 parts polyimide fiber

[0047] 15 parts of p-diazodiphenylamine paraformaldehyde condensate

[0048] Polyisocyanate block 5 parts

[0049] Silicone modified polyurethane resin 12 parts

[0050] Benzyldimethylamine 10 parts

[0051] Dimethyl styrylpyridine sulfate 3 parts

[0052] 2 parts valeraldehyde

[0053] Curing agent 6 parts

[0054] Dipropylene glycol dimethyl ether 1 part

[0055] 1 part polyvinyl alcohol acetaldehyde

[0056] Cadmium Sulfur Selenide 4 parts

[0057] 1 part of N-methylpyrrolidone

[0058] Bismuth vanadate 6 parts

[0059] Perylene 8 parts

[0060] 6 parts quinophthalone pigment

[0061] Acetophenon...

Embodiment 2

[0068] A high-gloss flame-retardant, heat-resistant and wear-resistant artificial stone is composed of the following ingredients in parts by weight:

[0069] Talcum powder 50 parts

[0070] Montmorillonite 100 parts

[0071] Barium sulfate 15 parts

[0072] Quartz 80 parts

[0073] Wollastonite 60 parts

[0074] 25 parts fine sand

[0075] 20 parts polyimide fiber

[0076]20 parts of p-diazodiphenylamine paraformaldehyde condensate

[0077] Polyisocyanate block 15 parts

[0078] Silicone modified polyurethane resin 25 parts

[0079] 20 parts of benzyldimethylamine

[0080] Dimethyl styrylpyridine sulfate 9 parts

[0081] 8 parts valeraldehyde

[0082] Curing agent 12 parts

[0083] Dipropylene glycol dimethyl ether 5 parts

[0084] 4 parts polyvinyl alcohol acetaldehyde

[0085] Cadmium sulfur selenide 15 parts

[0086] 4 parts of N-methylpyrrolidone

[0087] Bismuth vanadate 10 parts

[0088] Perylene 10 parts

[0089] Quinophthalone pigment 10 parts

[0090...

Embodiment 3

[0097] A high-gloss flame-retardant, heat-resistant and wear-resistant artificial stone is composed of the following ingredients in parts by weight:

[0098] Talcum powder 40 parts

[0099] Montmorillonite 90 parts

[0100] Barium sulfate 12 parts

[0101] Quartz 60 parts

[0102] Wollastonite 50 parts

[0103] 22 parts fine sand

[0104] 10 parts polyimide fiber

[0105] 18 parts of p-diazodiphenylamine paraformaldehyde condensate

[0106] Polyisocyanate block 10 parts

[0107] Silicone modified polyurethane resin 20 parts

[0108] Benzyldimethylamine 15 parts

[0109] Dimethyl styrylpyridine sulfate 6 parts

[0110] 6 parts valeraldehyde

[0111] Curing agent 10 parts

[0112] Dipropylene glycol dimethyl ether 3 parts

[0113] 2 parts polyvinyl alcohol acetaldehyde

[0114] Cadmium Sulfur Selenide 9 parts

[0115] N-Methylpyrrolidone 2 parts

[0116] Bismuth vanadate 9 parts

[0117] Perylene 9 parts

[0118] 9 parts quinophthalone pigment

[0119] Acetophe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-gloss flame-retardant heatproof wear-resistant artificial stone block, comprising the following components: talcum powder, montmorillonite, quartz, wollastonite, fine sand, polyimide fiber, a p-diazo-diphenylamine paraformaldehyde condensation product, a polyisocyanate block, organosilicon modified polyurethane resin, benzyldimethylamine, phenylvinylpyridine dimethyl sulphate, pentanal, a curing agent, dipropylene glycol dimethyl ether, polyvinyl alcohol glycolaldehyde, cadmium sulfoselenide, N-methyl-2-pyrrolidone, bismuth vanadate, perylene, acetophenone, 3-pentanone, methyl methacrylate, barium sulfate, N-isopropyl-N'-phenyl-p-phenylenediamine, zirconium sulfate and deionized water. The high-gloss flame-retardant heatproof wear-resistant artificial stone block has high hardness, metallic luster on its surface, high wear resistance and the characteristics of flame retardation performance and heat resistance.

Description

technical field [0001] The invention relates to a high-gloss flame-retardant, heat-resistant and wear-resistant artificial stone. Background technique [0002] With the improvement of people's living standards and living conditions, the interior decoration industry is developing rapidly, and the amount of decoration building materials is huge. Among them, stone is one of the most commonly used and most basic building materials, widely used in floors, walls and The paving of the countertop. The mining cost of natural stone is high, the pollution is large, and it contains a large amount of natural radioactive substances, which is harmful to human health. With the continuous development of the material field, the performance of artificial stone has been gradually improved, approaching or even surpassing natural stone, and it is more and more accepted by the market and users. However, the current artificial stone still has the disadvantages of low strength, poor surface abrasi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/32
Inventor 李凤燕
Owner 新疆东方环宇投资(集团)工业建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap