High-temperature-resistant coating structure for steel structure surface and applications thereof

A technology of high temperature resistance and coating, which is applied in the direction of layered products, metal layered products, synthetic resin layered products, etc., can solve the problems of no relevant reports on the launch pad, the inability to move the launch pad, and heavy weight, etc., to achieve Good thermal insulation performance, reduced back temperature, reduced thermal ablation and thermal shock effects

Inactive Publication Date: 2015-09-23
DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In foreign countries, the Ariane rocket launch platform of the European Space Agency in Guyana, South America is a concrete launch platform. This type of launch platform constructed of inorganic non-metallic materials has better gas purging and ablation resistance than organic ablation coatings, but the disadvantage is that it is thick. , heavy, and the launch pad cannot be moved
[0003] The rocket launch pad can be thermally protected by using special high-temperature-resistant coating materials and structures, but at present, there are no relevant reports on the technology for thermal protection of the launch pad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant coating structure for steel structure surface and applications thereof
  • High-temperature-resistant coating structure for steel structure surface and applications thereof
  • High-temperature-resistant coating structure for steel structure surface and applications thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The preparation of embodiment 1 high temperature resistant coating

[0020] like image 3 Shown:

[0021] 1. Preparation of the first organic layer: mix epoxy resin SM828, curing agent polyamide 650, and toughening agent liquid rubber according to the mass ratio of 7:2:1, and coat it on the rust-removed 190×120×5mm On the surface of one side of the steel plate, the coating thickness is 2mm.

[0022] 2. Preparation of shaped refractory brick layer: Clay refractory brick (NZ)-2 with a thickness of 5 mm was pasted on the organic layer.

[0023] 3. Preparation of the second organic layer: mix epoxy resin SM828, curing agent polyamide 650, and toughening agent liquid rubber according to the mass ratio of 7:2:1, and then coat it on the clay refractory brick. is 2mm.

[0024] 4. Preparation of unshaped refractory layer: First, mix 6-35M and 100-325M burnt stones evenly according to the mass ratio of 1:1, and then mix the mixed burnt stones with cordierite, aluminate cement...

Embodiment 2

[0027] Embodiment 2 Preparation of high temperature resistant coating structure

[0028] like image 3 Shown:

[0029] 1. Preparation of the first organic layer: mix epoxy resin SM828, curing agent polyamide 650, and toughening agent liquid rubber according to the mass ratio of 7:2:1, and coat it on the rust-removed 190×120×5mm On the surface of one side of the steel plate, the coating thickness is 4mm.

[0030] 2. Preparation of shaped refractory brick layer: Clay refractory brick (NZ)-2 with a thickness of 15mm was pasted on the organic layer.

[0031] 3. Preparation of the second organic layer: mix epoxy resin SM828, curing agent polyamide 650, and toughening agent liquid rubber according to the mass ratio of 7:2:1, and then coat it on the clay refractory brick. is 2mm.

[0032] 4. Preparation of unshaped refractory layer: First, mix 6-35M and 100-325M burnt stones evenly according to the mass ratio of 1:1, and then mix the mixed burnt stones with cordierite, aluminate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flame retardantaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a structure and applications of a high-temperature-resistant coating material for steel structure surface. The high-temperature-resistant coating material is composed of an organic layer, a shaped firebrick layer, an organic layer, and an amorphous refractory material layer. The two organic layers have the same components and are composed of epoxy resin, a polyamide curing agent, and a toughening agent (liquid rubber). The firebrick is clay-based firebrick. The amorphous refractory material is composed of flint clay, cordierite, aluminate cement, and silica fume. The adhesion force of the provided high-temperature-resistant coating material is strong, which can sustain the washing of rocket imitated combustion-gas stream. The metal backside temperature does not exceed 120 DEG C, and the coating has an excellent performance on resisting high-temperature combustion-gas stream brushing and thermal insulation property.

Description

technical field [0001] The invention relates to a high-temperature-resistant coating structure on the surface of a steel structure, in particular to a high-temperature-resistant coating structure used for coating the surface of a rocket launcher to reduce the back temperature of the launcher and protect the surface of the steel structure of the rocket launcher. The application belongs to the field of high temperature resistance and heat insulation protection. Background technique [0002] With the development of aerospace and aerospace industry, high temperature resistant coatings have opened up new application fields. In addition to the thermal protection of the aircraft itself, thermal protection measures have also been added to ground facilities such as rocket launch pads in China. If the launch pad is coated with high-temperature resistant coatings, it can insulate the metal surface, reduce thermal ablation and thermal shock, and prevent thermal fatigue, thermal crackin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/092B32B27/06
Inventor 马磊张巍王国鹏臧红张涛
Owner DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap