A kind of low temperature resistant flame retardant polyvinyl chloride cable material for automobile and preparation method thereof

A flame retardant polyvinyl chloride and low temperature resistant technology, which is applied to the low temperature resistant flame retardant polyvinyl chloride cable material for automobiles and its preparation field, can solve the problems of traffic accidents, loss of control of drivers, short circuit of cables, etc., and achieves enhanced flame retardancy, The effect of increasing flexibility

Inactive Publication Date: 2017-08-22
CHANGZHOU CITY WUJIN DISTRICT KAILIDA ELECTRONICS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the cold winter area in the north of our country, the sheath of the ordinary PVC cable is very easy to crack, causing short circuit, leakage, electric shock and other accidents. cause traffic accident

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A low-temperature-resistant flame-retardant polyvinyl chloride cable material for automobiles, which is prepared from the following raw materials in parts by weight (kg): polyvinyl chloride resin 80, polyolefin resin 10, ethylene-vinyl acetate copolymer 7, dodecacarbon Alcohol ester 2, dioctyl sebacate 8, nano kaolin 3, antimony trioxide 5, aluminum hydroxide 10, butyl stearate 5, microcrystalline graphite powder 7, mica powder 8, wollastonite 10, antimony Oxygen agent TPP 2, insoluble sulfur 1, dimethyl terephthalate 40, isobutyltriethoxysilane 5, rare earth carboxylate stabilizer 6, nano calcium carbonate 20, antioxidant 616 1, tetrabromophthalic anhydride 12. Emulsified silicone oil 7, isophorone 7.

[0017] A method for preparing a low-temperature-resistant flame-retardant polyvinyl chloride cable material for automobiles, comprising the following steps:

[0018] (1) Add nano-kaolin, antimony trioxide, aluminum hydroxide, butyl stearate, microcrystalline graphite p...

Embodiment 2

[0022] A low-temperature-resistant flame-retardant polyvinyl chloride cable material for automobiles, which is prepared from the following raw materials in parts by weight (kg): polyvinyl chloride resin 90, polyolefin resin 12, ethylene-vinyl acetate copolymer 8, dodecacarbon Alcohol ester 2.5, dioctyl sebacate 9, nano kaolin 4, antimony trioxide 8, aluminum hydroxide 12.5, butyl stearate 6.5, microcrystalline graphite powder 8, mica powder 10, wollastonite 13, antimony Oxygen agent TPP 2.5, insoluble sulfur 1.5, dimethyl terephthalate 45, isobutyltriethoxysilane 6, rare earth carboxylate stabilizer 7, nano calcium carbonate 25, antioxidant 616 1.5, tetrabromophthalic anhydride 13. Emulsified silicone oil 8, isophorone 7.5.

[0023] The preparation method is the same as in Example 1.

Embodiment 3

[0025] A low-temperature-resistant flame-retardant polyvinyl chloride cable material for automobiles, which is prepared from the following raw materials in parts by weight (kg): polyvinyl chloride resin 100, polyolefin resin 14, ethylene-vinyl acetate copolymer 9, dodecacarbon Alcohol ester 3, dioctyl sebacate 10, nano kaolin 5, antimony trioxide 10, aluminum hydroxide 15, butyl stearate 8, microcrystalline graphite powder 9, mica powder 12, wollastonite 15, antimony Oxygen agent TPP 3, insoluble sulfur 2, dimethyl terephthalate 50, isobutyltriethoxysilane 7, rare earth carboxylate stabilizer 8, nano calcium carbonate 30, antioxidant 616 2, tetrabromophthalic anhydride 14. Emulsified silicone oil, isophorone8.

[0026] The preparation method is the same as in Example 1.

[0027] The performance test results of the low-temperature-resistant flame-retardant polyvinyl chloride cable material for automobiles prepared in the above-mentioned embodiments 1-3 are shown in the followi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-temperature-resistant halogen-free flame-retardant polyvinyl chloride cable material used for automobiles and a preparation method of the low-temperature-resistant halogen-free flame-retardant polyvinyl chloride cable material. The low-temperature-resistant halogen-free flame-retardant polyvinyl chloride cable material is prepared from, by weight, 80 parts to 100 parts of polyvinyl chloride resin, 10 parts to 14 parts of polyolefin resin, 7 parts to 9 parts of ethylene vinyl acetate copolymer, 2 parts to 3 parts of 2,2,4-Trimethyl-1,3-pentanediolmono(2-methylpropanoate), 8 parts to 10 parts of dioctyl sebacate, 3 parts to 5 parts of nanometer kaolin, 5 parts to 10 parts of antimonous oxide, 10 parts to 15 parts of aluminium hydroxide, 5 parts to 8 parts of butyl stearate, 7 parts to 9 parts of microcrystalline graphite powder, 8 parts to 12 parts of mica powder, 10 parts to 15 parts of wollastonite, 2 parts to 3 parts of antioxidant TPP, 1 part to 2 parts of insoluble sulfur, 40 parts to 50 parts of dimethyl terephthalate, 5 parts to 7 parts of triethoxyisobutylsilane, 6 parts to 8 parts of rare earth carboxylate stabilizers, 20 parts to 30 parts of nanometer calcium carbonate, 1 part to 2 parts of antioxidant 616, 12 parts to 14 parts of tetrabromophthalic anhydride, 7 parts to 9 parts of silicone emulsion and 7 parts to 8 parts of isophorone. By means of the synergistic effect of added antimonous oxide and chlorine elements in the added polyvinyl chloride resin, the flame-retardant property of polyvinyl chloride is enhanced; by means of compound plasticizers such as the added dioctyl sebacate, flexibility of cables is improved while the cold-resistant performance of products is improved.

Description

[0001] field of invention [0002] The invention relates to a cable material, in particular to a low-temperature-resistant flame-retardant polyvinyl chloride cable material for automobiles and a preparation method thereof. Background technique [0003] Wire and cable are one of the important components of automotive electrical appliances. Taking advantage of the rapid development of the automotive industry, the automotive wire industry has developed rapidly. The interior of the car is a very complicated small environment, there are various complex conditions such as vibration, friction, ozone, oil pollution, high heat, cold and electromagnetic radiation. Performance, and with the continuous change of vehicle functions, the requirements for automotive wires are also increasing. [0004] Polyvinyl chloride cable material is a general term for cable materials made of polyvinyl chloride. As a traditional cable material, it has excellent physical and mechanical properties, electri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L23/00C08L23/08C08L83/04C08K13/02C08K5/12C08K3/34C08K3/22C08K5/101C08K3/04C08K3/06C08K5/54C08K5/098C08K3/26C08K5/09C08K5/13
CPCB29B9/06C08K2201/011C08L27/06C08L2201/02C08L2201/22C08L2203/202C08L2205/035H01B3/443H01B7/295C08L23/00C08L23/0853C08L83/04C08K13/02C08K5/12C08K3/346C08K3/2279C08K5/101C08K3/04C08K3/06C08K5/098C08K2003/265C08K5/11
Inventor 臧磊
Owner CHANGZHOU CITY WUJIN DISTRICT KAILIDA ELECTRONICS