Polystyrene resin-based composite material and preparation method thereof

A polystyrene resin, composite material technology, applied in the field of composite materials, can solve the problems of poor thermal conductivity, easy cracking, cracking, etc.

Inactive Publication Date: 2015-11-11
SUZHOU ZHENZHAN TECHCAL MATERIAL CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the composite material solves the problem of poor thermal conductivity of ordinary polystyrene resin, it still has cold resistance (the embrittlement temperature is high, and the performance drops more seriously in low temperatur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polystyrene resin-based composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The polystyrene resin-based composite material is composed of 45 parts by weight of polystyrene resin, 14 parts of epichlorohydrin rubber, 5.5 parts of calcium chrome garnet powder, 6.5 parts of MRP, 3263 parts of UV-3263 parts, quaternary ammonium salt type cationic anti- 1.4 parts of static agent, 3 parts of glycerin, 2.5 parts of PE wax, 1.5 parts of rare earth stabilizer, 5 parts of polyolefin elastomer, 0.4 part of organic phosphate nucleating agent.

[0028] The steps of its preparation method are as follows:

[0029] (1) Dissolve CTMAB in water and disperse evenly to prepare a CTMAB aqueous solution with a mass fraction of 10%. Add the garnet to the CTMAB aqueous solution after crushing, stir at a constant temperature of 50°C for 30 minutes, and place in an ultrasonic oscillator for ultrasonic oscillation for 2 hour, after standing for 1 hour, filter, wash, and dry to obtain garnet powder;

[0030] (2) dissolving the titanate coupling agent in absolute ethanol a...

Embodiment 2

[0034] Polystyrene resin-based composite material, its weight parts are composed of: 55 parts of polystyrene resin, 10 parts of epichloride rubber, 7 parts of calcium chrome garnet powder, 5 parts of MRP, 2.5 parts of UV-326, quaternary ammonium salt type cationic antistatic agent 1.6 parts, 5 parts of glycerin, 2.1 parts of PE wax, 2.5 parts of rare earth stabilizer, 4 parts of polyolefin elastomer, 0.4 part of organic phosphate nucleating agent.

[0035] Its preparation method is with embodiment 1.

Embodiment 3

[0037] The polystyrene resin-based composite material is composed of 65 parts by weight of polystyrene resin, 12 parts of epichlorohydrin rubber, 6 parts of calcium chrome garnet powder, 5.5 parts of MRP, 4.5 parts of UV-3264, quaternary ammonium salt type cationic anti- 1.5 parts of static agent, 7 parts of glycerin, 2.8 parts of PE wax, 2 parts of rare earth stabilizer, 2.5 parts of polyolefin elastomer, 0.5 part of organic phosphate nucleating agent.

[0038] Its preparation method is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a polystyrene resin-based composite material. The polystyrene resin-based composite material comprises, by weight, 45 to 65 parts of polystyrene resin, 10 to 14 parts of chlorine ether rubber, 5 to 9 parts of uvarovite powder, 5 to 8 parts of a fire retardant, 2 to 5 parts of a light stabilizing agent, 1 to 2 parts of an antistatic agent, 2 to 7 parts of a plasticizer, 2 to 3 parts of a lubricant, 1 to 3 parts of a heat stabilizer, 2 to 5 parts of a compatilizer and 0.4 to 0.5 part of a nucleating agent. The invention further discloses a preparation method for the polystyrene resin-based composite material. The polystyrene resin-based composite material provided by the invention has good cold resistance, high temperature resistance, oxidizability and toughness.

Description

Technical field: [0001] The invention relates to a composite material, in particular to a polystyrene resin-based composite material and a preparation method thereof. Background technique: [0002] Polystyrene resin (Polystyrene, abbreviated as PS) refers to a polymer synthesized by free radical addition polymerization of styrene monomer, and is a colorless and transparent thermoplastic. Polystyrene includes ordinary polystyrene, expanded polystyrene (EPS), high impact polystyrene (HIPS) and syndiotactic polystyrene (SPS). Ordinary polystyrene resin is non-toxic, odorless, colorless transparent particles, glass-like brittle material, its products have extremely high transparency, light transmittance can reach more than 90%, good electrical insulation performance, easy to color, easy to process Good fluidity, good rigidity and good chemical corrosion resistance. Polystyrene can be widely used in the light industry market, daily decoration, lighting instructions and packagin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/06C08L71/03C08K13/06C08K9/04C08K3/34B29C47/92B29C48/92
Inventor 黄文成
Owner SUZHOU ZHENZHAN TECHCAL MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap