Antistatic antifouling powder coating for valves

A technology of powder coating and production method, which is applied in the direction of powder coating, conductive coating, coating, etc., can solve the problems of valve application limitation, severe orange peel, rough surface, etc., and achieve the ability to reduce dust absorption and excellent antifouling performance , Good compatibility effect

Inactive Publication Date: 2015-11-11
ANHUI RONGDA VALVE
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the valve body is a casting or forging, its surface is rough, and the current functional powder coating technology for valve surface treatment in the existing technology still has certain defects, resulting in defects suc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] The antistatic valve antifouling powder coating is characterized in that it is made of the following raw materials in parts by weight: high hydroxyl polyester resin 63, hydroxyl acrylic resin 24, HDI trimer 5, polyvinylidene fluoride 11 , Nano titanium dioxide 2.5, nano antimony-doped tin dioxide 0.8, methyl isobutyl ketone 9, hexafluorobutyl acrylate 15, montmorillonite 7, ferrocene 0.7, low molecular weight polyethylene wax 6, dimethyl dichlorosilane 3. Dimethylacetamide 27.

[0013] The production method includes the following steps:

[0014] (1) Stir and mix methyl isobutyl ketone and hexafluorobutyl acrylate, heat up to 75-95 °C, add montmorillonite, fully stir and condense and reflux for 2-4 hours, ultrasonically disperse uniformly, and spray dry to obtain modified montmorillonite;

[0015] (2) calcining nano titanium dioxide at a high temperature of 670-740 ℃ for 30-50 minutes, cooling to room temperature with ultrasonic vibration for 20-40 minutes, adding dime...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antistatic antifouling powder coating for valves. High hydroxyl polyester resin and hydroxy acrylic resin are chosen as main film-forming materials, HDI trimer serves as a curing agent, modified polyvinylidene fluoride is added to improve the high-low temperature resistance of the antistatic antifouling powder coating, meanwhile, other effective additives are added, and the mixture is modified to achieve good intermiscibility, can quickly float to the surface of a paint film and is fixed on the surface of the paint film through reaction between hydroxy and -NCO, so that pollutants cannot be easily adhered to the surface of the paint film, and accordingly, the paint film has enduring dirt-adhering resisting and self-cleaning properties. The produced antistatic antifouling powder coating for valves is solvent-free and environment-friendly, the paint film is even and smooth in surface, an antistatic role can be played, the dust adsorption capability is reduced, the process is simple and the antifouling performance is superior.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an antistatic valve antifouling powder coating and a preparation method thereof. Background technique [0002] In recent years, the application of powder coatings has surpassed water-based coatings and high-solid coatings in the coatings industry, and has become one of the most widely used coatings in the industry. The powder coating process solves the problems of flammability, explosion and environmental pollution in the traditional paint coating process, and its coating has superior performance, the raw materials can be recycled and reused, and the coating process is simple. It can be widely used in the coating of valve shells. Since the valve body is a casting or forging, its surface is rough, and the current functional powder coating technology for valve surface treatment in the existing technology still has certain defects, resulting in defects such as shrinkage cavities, pinholes, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/06C09D127/16C09D5/03C09D5/24C09D7/12
Inventor 胡光荣
Owner ANHUI RONGDA VALVE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap