Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of composite separator for secondary nickel-zinc battery and preparation method thereof

A technology of composite diaphragm and nickel-zinc battery, which is applied in the direction of nickel storage battery, alkaline storage battery, battery pack components, etc., can solve the problems of battery performance such as partial dislocation of the diaphragm, and achieve the simple and easy assembly process of the battery, which is not easy to wrinkle and maintain smooth effect

Active Publication Date: 2018-02-27
HENAN KEGAO RADIATION CHEM TECH
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a composite diaphragm for secondary nickel-zinc battery and its preparation method, so as to overcome the shortcomings of the diaphragm in the prior art that are prone to local dislocation, wrinkles, etc., which affect the performance of the battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A preparation method for a composite diaphragm for a secondary nickel-zinc battery, comprising the following steps: ① placing a polypropylene microporous membrane with a thickness of 10 µm on a surface density of 30 g / m 2 The underside of the non-woven fabric containing ultrafine polyolefin fibers is bonded together by a heat sealing machine at a temperature of 130°C to form a diaphragm substrate; ②The diaphragm substrate prepared in step ① is continuously passed through an electronic Accelerator irradiation, control the beam flow rate of the electron accelerator and the transmission speed of the diaphragm substrate, so that the absorbed dose accepted by the diaphragm substrate is 40kGy; the diaphragm substrate after the radiation is packed into the grafting reactor, sealed, vacuumized, and then Grafting liquid (the grafting liquid in the described step ② is measured by mass percentage, comprises the following components: sodium lauryl sulfate 0.5%, acrylic acid 1.8%, so...

Embodiment 2

[0022] A preparation method for a composite diaphragm for a secondary nickel-zinc battery, comprising the following steps: ① placing a polypropylene microporous membrane with a thickness of 45 µm on a surface density of 50 g / m 2 The underside of the non-woven fabric containing ultrafine polyolefin fibers is bonded together by a heat sealing machine at a temperature of 150°C to form a diaphragm substrate; ②The diaphragm substrate prepared in step ① is continuously passed through the electronic Accelerator irradiation, control the beam flow rate of the electron accelerator and the transmission speed of the diaphragm substrate, so that the absorbed dose accepted by the diaphragm substrate is 30kGy; the diaphragm substrate after the radiation is packed into the grafting reactor, sealed, vacuumized, and then The grafting liquid (the grafting liquid in the described step ② is calculated by mass percentage, includes the following components: sodium alkylbenzene sulfonate 3.0%, acrylic...

Embodiment 3

[0026] A preparation method for a composite diaphragm for a secondary nickel-zinc battery, comprising the steps of: ① placing a polypropylene microporous membrane with a thickness of 25 µm on a surface density of 40 g / m 2 The underside of the non-woven fabric containing ultrafine polyolefin fibers is combined by a heat sealing machine at a temperature of 140°C to form a diaphragm substrate; ②The diaphragm substrate prepared in step ① is continuously passed through the electronic Accelerator irradiation, control the beam flow rate of the electron accelerator and the transmission speed of the diaphragm substrate, so that the absorbed dose accepted by the diaphragm substrate is 15kGy; the diaphragm substrate after the radiation is packed into the grafting reactor, sealed, vacuumized, and then The grafting liquid (the grafting liquid in the described step ② is measured by mass percentage, includes the following components: 1.0% of alkyl alcohol polyoxyethylene ether, 2.5% of acryli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to a composite separator for a secondary nickel-zinc battery: the composite separator has a two-layer composite structure, one layer is a polypropylene microporous membrane, and the other layer is a non-woven fabric containing ultrafine polyolefin fibers; The surface density of the composite diaphragm is 38g / m2~80g / m2; the thickness is 0.1mm~0.2mm. The composite diaphragm used in the secondary nickel-zinc battery in the present invention makes the battery assembly process simple and easy, and there will be no dislocation and wrinkles between the two layers; the diaphragm base cloth is not easy to produce wrinkles during the radiation grafting process, It is beneficial to maintain the flatness of the diaphragm; through radiation grafting of acrylic acid and (or) sodium styrene sulfonate, the inner and outer surfaces of the composite diaphragm are endowed with carboxyl groups and (or) sulfonic acid group hydrophilic functional groups, with permanent hydrophilicity.

Description

technical field [0001] The invention belongs to the technical field of battery separators, and in particular relates to a composite separator for a secondary nickel-zinc battery and a preparation method thereof. Background technique [0002] Nickel-zinc battery is a kind of battery that has been paid attention to for a long time. Its advantages lie in high voltage (theoretical voltage is 1.8V, working voltage is 1.6V) and low cost. Its disadvantage comes from the fact that the zinc electrode is prone to produce zinc oxide dendrites to penetrate the separator and cause a short circuit of the battery, which affects the cycle life of the battery. Therefore, nickel-zinc batteries have not been well developed so far. In order to solve the problem of zinc oxide dendrites in nickel-zinc batteries, one of the main methods used by people is to improve the anti-dendrite ability of the separator. One of the effective methods commonly used is to use polypropylene microporous membranes ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/16H01M10/30H01M50/403H01M50/417H01M50/489
CPCH01M10/30H01M50/409Y02E60/10
Inventor 崔国士党从军赵红英崔攀
Owner HENAN KEGAO RADIATION CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com