Novel water pipe joint nanometer waterproof film

A technology of water pipe joints and waterproof membranes, applied in the direction of coating, etc., to achieve high hardness, reduce maintenance and replacement, and ensure waterproof and anti-seepage effects

Inactive Publication Date: 2015-12-16
RONGCHENG PIPE IND
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nano-waterproof technology has been applied to many fields such as clothing, electronic products, and construction equipment because of its long-lasting water resistance. Its dosage forms also include powder, mud, etc., and there is no patent to make it into a film for water pipe joints.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A novel nano-waterproof film for water pipe joints, the preparation process of which is as follows:

[0038] (1) Preparation of base membrane

[0039] ① 31 parts by mass of nano-silica, 26 parts by mass of nano-titanium dioxide and 12 parts by mass of nano-zinc oxide were stirred and mixed for 30 minutes at a speed of 150 r / min to obtain a nano-material;

[0040] ②Put 7 parts by mass of silicon-acrylic emulsion into a stirring tank, gradually add 4 parts by mass of butyl acrylate, control the temperature at 63°C, stir and mix at a speed of 160r / min for 45min to obtain a bottom solvent;

[0041] ③Take the main nanomaterial obtained in step (1)①, and gradually add it to the base solvent obtained in step (1)②, control the temperature at 55°C, stir and mix at a speed of 220r / min for 1.5h, and add 4 parts by mass of Sodium carboxymethyl cellulose and the organosilicon defoamer of 2 parts by mass are obtained as film raw materials;

[0042] ④ Molding the film raw material b...

Embodiment 2

[0050] A novel nano-waterproof film for water pipe joints, the preparation process of which is as follows:

[0051] (1) Preparation of base membrane

[0052] ① Stirring and mixing 30 parts by mass of nano-silica, 15 parts by mass of nano-titanium dioxide and 14 parts by mass of nano-zinc oxide at a speed of 130 r / min for 40 minutes to obtain the main nano-material;

[0053] ②Put 17 parts by mass of silicon-acrylic emulsion into a stirring tank, gradually add 7 parts by mass of butyl acrylate, control the temperature at 75°C, and stir and mix at a speed of 140r / min for 35min to obtain a bottom solvent;

[0054] ③Take the main nanomaterial obtained in step (1)①, and gradually add it to the bottom solvent obtained in step (1)②, control the temperature at 58°C, stir and mix at a speed of 180r / min for 1h, and add 5 parts by mass of carboxyl Sodium methyl cellulose and the organosilicon defoamer that mass parts are 2 parts, obtain film raw material;

[0055] ④ Molding the film raw...

Embodiment 3

[0062] A novel nano-waterproof film for water pipe joints, the preparation process of which is as follows:

[0063] (1) Preparation of base membrane

[0064] ① 22 parts by mass of nano-silica, 28 parts by mass of nano-titanium dioxide and 9 parts by mass of nano-zinc oxide, stirred and mixed at a speed of 130r / min for 25min to obtain a nano-material;

[0065] ②Put 18 parts by mass of silicon-acrylic emulsion into a stirring tank, gradually add 6 parts by mass of butyl acrylate, control the temperature at 70°C, and stir and mix at a speed of 150r / min for 45min to obtain a bottom solvent;

[0066] ③Take the main nanomaterial obtained in step (1)①, and gradually add it to the base solvent obtained in step (1)②, control the temperature at 48°C, stir and mix at a speed of 250r / min for 1h, and add 6 parts by mass of polymer Vinyl alcohol and the organosilicon defoamer of 3 parts by mass are obtained as film raw materials;

[0067] ④Molding the film raw material by a molding machine,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a novel water pipe joint nanometer waterproof film, which comprises, by mass, 20-35 parts of nanometer silica, 15-30 parts of nanometer titanium dioxide, 5-15 parts of nanometer zinc oxide, 10-25 parts of a silicone acrylic emulsion, 5-10 parts of butyl acrylate, 2-6 parts of a film aid, 1-4 parts of an organosilicon defoamer, 4-8 parts of octadecyl amine, 1-2 parts of imidazolinium salt ethylacrylamide salt, and 3-7 parts of graphite. According to the present invention, the nanometer waterproof technology is used, the new formula and the new dosage form are used, the use is convenient, the long-term use of the water pipe joint is effectively ensured, effects of water resistance and seepage resistance are provided, and the cost is reduced.

Description

technical field [0001] The invention relates to a nanometer waterproof technology, in particular to a novel nanometer waterproof film for water pipe joints. Background technique [0002] Drainage pipes are mainly responsible for the drainage of rainwater, sewage, farmland irrigation and drainage, and can be divided into concrete pipes and reinforced concrete pipes according to their materials. Due to the generally long distance required for water delivery, it is usually necessary to connect multiple drain pipes or elbows to complete the flow of water to the designated location. Mechanical cooperation is usually used between the drain pipe and the drain pipe, or between the drain pipe and the drain elbow. Waterproof tape is then used to complete the interconnection of the drainage pipes. However, due to the limitation of the working environment of the drainage pipes, this waterproof leakage method is easy to corrode and seep water when the sewage is infiltrated for a long tim...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F265/04C08F220/18C08F2/44C08K3/36C08K3/22C09D7/12
Inventor 朱加荣
Owner RONGCHENG PIPE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap