Environmentally-friendly multi-effect nanometer water-based paint

A water-based paint, environmentally friendly technology, applied in the direction of anti-fouling/underwater paint, coating, paint containing biocide, etc., can solve the problems of seamless waterproof, low tensile strength, easy cracking, etc. Achieve the effects of strong surface activity and adsorption capacity, high hardness and scrub resistance, efficient decomposition and elimination

Inactive Publication Date: 2015-12-23
ZIBO KUAKE MEDICINE TECH
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are problems such as high-temperature flow, low-temperature embrittlement, low tensile strength, low elongation, and poor adhesion. At the same time, the colors of the three materials are all black, so these products have strong heat absorption, easy cracking, aging and pollute the environment, etc.
Moreover, the effect of seamless waterproofing cannot be achieved at all, and the worldwide problem of building waterproofing cannot be solved.
[0003] Most of the exterior walls of existing concrete buildings in our country still use exterior wall bricks. The weight of exterior wall bricks is generally more than eight kilograms per square meter, beca

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] In the present embodiment, an environment-friendly multi-effect nano-water-based paint includes the following components by weight: 40 parts of polymer synthetic resin emulsion, 3 parts of nano-scale silicon dioxide, 0.5 part of nano-titanium dioxide, and 1 part of water-based paint thickener , 0.5 parts of polyether surfactant, 0.4 part of preservative, 1 part of antifreeze, 1 part of curing agent, 0.4 part of dispersant, 25 parts of filler, 10 parts of water;

[0021] Its preparation method is as follows:

[0022] S1. First, put water, dispersant, and preservative liquid materials into the dispersion tank, stir evenly, put filler, nano-scale silicon dioxide, and nano-titanium dioxide in the stirring state, and accelerate the dispersion for 30 minutes to obtain a mixture;

[0023] S2, transfer the mixture in S1 to the paint mixing tank, drop into the polymer synthetic resin emulsion in the paint mixing tank, add water-based paint thickener, polyether surfactant, antifr...

Embodiment 2

[0026] In the present embodiment, an environment-friendly multi-effect nano-water-based paint includes the following components by weight: 45 parts of polymer synthetic resin emulsion, 4 parts of nano-scale silicon dioxide, 0.8 part of nano-titanium dioxide, and 1.2 parts of water-based paint thickener , 0.8 parts of polyether surfactant, 0.6 parts of preservative, 1.5 parts of antifreeze, 1.2 parts of curing agent, 0.6 parts of dispersant, 30 parts of filler, 15 parts of water;

[0027] Its preparation method is as follows:

[0028] S1. First, put water, dispersant, and preservative liquid materials into the dispersion tank, stir evenly, put filler, nano-scale silicon dioxide, and nano-titanium dioxide in the stirring state, and accelerate the dispersion for 30 minutes to obtain a mixture;

[0029] S2, transfer the mixture in S1 to the paint mixing tank, drop into the polymer synthetic resin emulsion in the paint mixing tank, add water-based paint thickener, polyether surfact...

Embodiment 3

[0032] In the present embodiment, an environment-friendly multi-effect nano-water-based paint includes the following components by weight: 50 parts of polymer synthetic resin emulsion, 4.5 parts of nano-scale silicon dioxide, 1.2 parts of nano-titanium dioxide, and 1.5 parts of water-based paint thickener , 1.2 parts of polyether surfactant, 0.7 part of preservative, 2 parts of antifreeze, 1.5 parts of curing agent, 0.8 part of dispersant, 35 parts of filler, 20 parts of water;

[0033] Its preparation method is as follows:

[0034] S1. First, put water, dispersant, and preservative liquid materials into the dispersion tank, stir evenly, put filler, nano-scale silicon dioxide, and nano-titanium dioxide in the stirring state, and accelerate the dispersion for 30 minutes to obtain a mixture;

[0035] S2, transfer the mixture in S1 to the paint mixing tank, drop into the polymer synthetic resin emulsion in the paint mixing tank, add water-based paint thickener, polyether surfacta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses environmentally-friendly multi-effect nanometer water-based paint. The water-based paint is prepared from, by weight, 40-60 parts of macromolecular synthesis resin emulsion, 3-6 parts of nanometer scale silicon dioxide, 0.5-2 parts of nanometer titanium dioxide, 1-2 parts of water-based paint thickening agents, 0.5-2 parts of polyether type surface active agents, 0.4-1 part of preservative, 1-3 parts of anti-freezing agents, 1-2 parts of solidifying agents, 0.4-1.2 parts of dispersing agents, 25-45 parts of filling and 10-30 parts of water. The environmentally-friendly multi-effect nanometer water-based paint is waterproof, high in hardness, resistant to washing, high in adhesive force, smoothness and cleanness and resistant to oil stains, ageing and bacteria, meanwhile the content of VOC and formaldehyde is low, and the water-based paint is safe, environmentally friendly, excellent in performance and wide in application range.

Description

technical field [0001] The invention relates to the technical field of water-based paint, in particular to an environment-friendly multi-effect nano water-based paint. Background technique [0002] Waterproof materials used in the construction industry are generally divided into three categories: coiled materials, solvents, and asphalt ointment. However, there are problems such as high-temperature flow, low-temperature embrittlement, low tensile strength, low elongation, and poor adhesion. At the same time, the colors of the three materials are all black, so these products have strong heat absorption, easy cracking, aging and pollute the environment, etc. Moreover, the effect of seamless waterproofing cannot be achieved at all, and the worldwide problem of building waterproofing cannot be solved. [0003] Most of the exterior walls of existing concrete buildings in my country still use exterior wall bricks. The weight of exterior wall bricks is generally more than eight ki...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D125/14C09D133/04C09D131/04C09D5/14C09D7/12
Inventor 高忠青
Owner ZIBO KUAKE MEDICINE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap