Environment-friendly anti-static polyurethane anticorrosion paint and preparation method thereof

An anti-corrosion coating and anti-static technology, applied in polyurea/polyurethane coatings, anti-corrosion coatings, conductive coatings, etc., can solve problems affecting people's health, carcinogenicity, and toxic volatiles, and achieve excellent anti-corrosion performance, long service life, and low cost. Easy to get effect

Active Publication Date: 2015-12-30
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most anti-corrosion coatings currently on the market contain volatile organic solvents, some of which are toxic or even carcinogenic, seriously affecting people's health; in addition, with the popularization of electronic products, the electromagnetic wave signals in the surrounding environment are getting stronger and stronger, and radiation interference It is also becoming more and more serious, so higher requirements are put forward for the antistatic ability of equipment products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly anti-static polyurethane anticorrosion paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The preparation method of the environment-friendly antistatic polyurethane anticorrosion coating, the specific preparation steps include:

[0018] Step 1: Weigh raw materials according to certain parts by weight: according to parts by weight: 36 parts of water-based polyurethane emulsion, 28 parts of water-based acrylic resin, 4 parts of copper sulfide, 3 parts of montmorillonite, 2 parts of conductive mica powder, 2 parts of calcium carbonate 1 part, 2 parts of zinc oleate, 1 part of polyoxypropylene laurate, 1 part of sodium lauryl sulfate, 1 part of leveling agent, 0.2 part of defoamer, 12 parts of ethanol and an appropriate amount of deionized water;

[0019] Step 2: Dissolve sodium lauryl sulfate in deionized water, then add copper sulfide, montmorillonite, conductive mica powder, calcium carbonate and ethanol, stir and mix for 1 hour, then grind and disperse the slurry to 2500 Mesh fineness;

[0020] Step 3: Add water-based polyurethane emulsion, water-based acry...

Embodiment 2

[0023] The preparation method of the environment-friendly antistatic polyurethane anticorrosion coating, the specific preparation steps include:

[0024] Step 1: Weigh raw materials according to certain parts by weight: according to parts by weight: 60 parts of water-based polyurethane emulsion, 43 parts of water-based acrylic resin, 13 parts of copper sulfide, 12 parts of montmorillonite, 9 parts of conductive mica powder, 10 parts of calcium carbonate 5 parts of zinc oleate, 6 parts of polyoxypropylene laurate, 3 parts of sodium lauryl sulfate, 2 parts of leveling agent, 2 parts of defoamer, 25 parts of ethanol and appropriate amount of deionized water;

[0025] Step 2: Dissolve sodium lauryl sulfate in deionized water, then add copper sulfide, montmorillonite, conductive mica powder, calcium carbonate and ethanol, stir and mix for 4 hours, then grind and disperse the slurry to 2500 Mesh fineness;

[0026] Step 3: Add water-based polyurethane emulsion, water-based acrylic r...

Embodiment 3

[0029] The preparation method of the environment-friendly antistatic polyurethane anticorrosion coating, the specific preparation steps include:

[0030] Step 1: Weigh raw materials according to certain parts by weight: according to parts by weight: 48 parts of water-based polyurethane emulsion, 35 parts of water-based acrylic resin, 8 parts of copper sulfide, 7 parts of montmorillonite, 5 parts of conductive mica powder, 6 parts of calcium carbonate 4 parts of zinc oleate, 3 parts of polyoxypropylene laurate, 2 parts of sodium lauryl sulfate, 1.4 parts of leveling agent, 1 part of defoamer, 18 parts of ethanol and appropriate amount of deionized water;

[0031] Step 2: Dissolve the sodium lauryl sulfate in the raw material in deionized water, then add copper sulfide, montmorillonite, conductive mica powder, calcium carbonate and ethanol, stir and mix for 2.5 hours, then grind and disperse the slurry to 2500 mesh fineness;

[0032] Step 3: Add water-based polyurethane emulsio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses environment-friendly anti-static polyurethane anticorrosion paint and a preparation method thereof. The environment-friendly anti-static polyurethane anticorrosion paint comprises the following raw materials in parts by weight: 36-60 parts of aqueous polyurethane emulsion, 28-43 parts of aqueous acrylic resin, 4-13 parts of copper sulphide, 3-12 parts of montmorillonite, 2-9 parts of conductive mica powder, 2-10 parts of calcium carbonate, 2-5 parts of zinc oleate, 1-6 parts of PPG-n Laurate, 1-3 parts of sodium dodecyl sulfate, 1-2 parts of a levelling agent, 0.2-2 parts of an antifoaming agent, 12-25 parts of ethanol, and proper amount of deionized water. The prepared paint is large in surface resistance, shows good antistatic capability, and further, the conductive mica powder and copper sulphide raw materials are low in cost and easy to obtain and suitable for wide application. The prepared paint possesses good water proofness and acid resistance, displays excellent anticorrosion performance, and is long in practical service life and stable.

Description

technical field [0001] The invention belongs to the field of anticorrosion coatings, in particular to an environment-friendly antistatic polyurethane anticorrosion coating and a preparation method thereof. Background technique [0002] Among the many protective measures, painting is one of the most convenient, quick and effective protective measures. Coating is to apply paint on the surface of equipment products, which can play an insulating role to reduce the corrosion of equipment products by the external environment, prolong the service life of equipment, and reduce the cost of use. As people's requirements for the living environment are getting higher and higher, more and more attention is paid to environmental protection issues. However, most anti-corrosion coatings currently on the market contain volatile organic solvents, some of which are toxic or even carcinogenic, seriously affecting people's health; in addition, with the popularization of electronic products, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D133/00C09D5/24C09D5/08C09D7/12
Inventor 翁宇飞李力南
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com