Application of biodegradable rolling emulsion composite in aluminum alloy plate strip hot rolling technology

An aluminum alloy strip, biodegradable technology, applied in the direction of lubricating composition, petroleum industry, base material, etc., can solve the problems of large labor and energy consumption, and achieve convenient production and use, good extreme pressure performance and lubricating performance, The effect of high emulsification stability

Inactive Publication Date: 2016-01-13
CHINA PETROLEUM & CHEM CORP
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Taking the emulsion for hot rolling of aluminum alloy strips as an example, the current domestic annual consumption is 20,000-30,000 tons, and the annual discharge of e

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The composition of the composition is shown in the table below.

[0032] Serial number

Component name

Weight (kg)

1

Palm oil

2745

2

Trimethylolpropane Triisostearate

1400

3

Pentaerythritol oleate

1500

4

Oleic acid

1300

5

Triethanolamine

400

6

12-14 alcohol

600

7

Sodium Petroleum Sulfonate

200

8

Modified castor oil polyoxyethylene ether

800

9

Phosphate

300

10

Acid phosphate

300

[0033] 11

Octyl diphenylamine

50

12

Di-tert-butyl p-cresol

100

13

Organosiloxane

5

14

Benzisothiazolinone

200

15

Methylene Dimorpholine

100

[0034] The preparation method of the composition is as follows:

[0035] The first step: add 1300 kg of oleic acid and 400 kg of triethanolamine into a reactor with a rotation speed of 80 to 120 revolutions per minute, and heat to 50° C. while stirring, and hold for 60 minutes.

[0036] The second step: 1400kg trimethylolpropane triisostearate, 1500kg pentaerythritol oleate, 2745kg palm oil, 600kg 12-14 alcohol, 300kg acid ...

Embodiment 2

[0040] The composition of the composition is shown in the table below.

[0041] Serial number

[0042] 3

[0043] The preparation method of the composition is as follows:

[0044] The first step: add 1200kg of oleic acid and 400kg of triethanolamine into a reactor with a rotation speed of 80-120 rpm, and heat to 50°C while stirring, and hold for 60 minutes.

[0045] The second step: 3345kg palm oil, 2650kg trimethylolpropane oleate, 400kg 12-14 alcohol, 300kg acid phosphate, 200kg petroleum sodium sulfonate, 100kg octyl diphenylamine, 100kg di-tert-butyl p-cresol in sequence Add it to the blending kettle and keep stirring at constant temperature for 30 minutes until the additives are completely dissolved.

[0046] The third step: add 500kg modified castor oil polyoxyethylene ether, 300kg nonylphenol polyoxyethylene ether, 5kg organosiloxane, 150kg iodopropynyl butyl carbamate and 150kg methylene dimorpholine, continue Stir until it is uniform and transparent, cool to room tempe...

Embodiment 3

[0051] The composition of the composition is shown in the table below.

[0052] Serial number

Component name

Weight (kg)

1

Palm oil

3345

2

Neopentyl glycol oleate

2350

3

Tall oleic acid

1200

4

Triethanolamine

500

5

12-14 alcohol

400

6

Sodium Petroleum Sulfonate

100

7

Modified castor oil polyoxyethylene ether

400

8

Polyoxyethylene nonylphenol ether

600

9

Acid phosphate

300

10

Phosphite

200

11

Octyl diphenylamine

100

12

Di-tert-butyl p-cresol

100

13

Organosiloxane

5

14

Iodopropynyl butyl carbamate

200

15

Methylene Dimorpholine

200

[0053] The preparation method of the composition is as follows:

[0054] The first step: add 1200kg tall oleic acid and 500kg triethanolamine into a reactor with a rotation speed of 80-120 rpm, and heat it to 50°C while stirring, and keep it for 60 minutes.

[0055] The second step: 3345kg palm oil, 2350kg trimethylolpropane oleate, 600kg 12-14 alcohol, 300kg acid phosphate, 100kg petroleum sodium sulfonate, 100kg octyl ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Kinematic viscosityaaaaaaaaaa
Saponification valueaaaaaaaaaa
Acid valueaaaaaaaaaa
Login to view more

Abstract

The invention relates to the application of a biodegradable rolling emulsion composite in an aluminum alloy plate strip hot rolling technology. The biodegradable rolling emulsion composite is prepared from, by weight, 60-80 parts of vegetable oil and synthetic ester, 2-10 parts of at least one of oleic acid, triethanolamine and tall oil acid, 0-15 parts of at least one of petroleum sodium sulfonate, modified castor oil polyoxyethylene ether and alkylphenol polyoxyethylene ether, 0-5 parts of 12-14 alcohol, 0-10 parts of at least one of phosphite ester and phosphate ester, 1-5 parts of at least one of acid phosphate ester and isostearic acid, 0.5-2 parts of butylated hydroxytoluene, 0.05-1 part of octyl diphenylamine, 0.05-0.2 part of organosiloxane and 0.5-3 parts of at least one of methylene dimorpholine, iodo-n-butylproparglycarbamate and benzisothiazolones.

Description

Technical field [0001] The invention relates to the application of a biodegradable rolling emulsified oil composition in a hot rolling process of aluminum alloy plate and strip. Background technique [0002] In recent years, thanks to the development of my country's economy, the domestic metal processing industry has developed rapidly, and the consumption of metal processing fluid has been increasing year by year. At present, the non-renewable pure mineral oil type metal processing oil is gradually decreasing, and water-based metal processing fluid has become the mainstream product in the market, which also brings a series of environmental problems. The emulsified metal working fluid contains a large amount of mineral oil and has poor biodegradability. It is a material with a greater impact on the environment. These waste fluids have low recycling value and are difficult to handle. The mineral oil in it has poor degradability in the environment and is directly discharged to human...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/04C10M111/02C10N40/24C10N30/06
Inventor 王靖宇张旭杨志东李晓阳杨兰张斌
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap