Multifunctional paste-shaped plaster and preparation method thereof

A multi-functional, paste-like technology, applied in the construction field, can solve the problems affecting the aesthetic quality of the building, and the clay is prone to efflorescence, etc.

Inactive Publication Date: 2016-01-27
苏州大乘环保新材有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, composite Portland cement is added to its composition, and the silicate is a weak acid and strong alkali salt, which undergoes a hydration reaction with water to form free calcium, silicic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Step 1: Weigh 35 parts of 80-120 mesh quartz sand, 30 parts of 325 mesh heavy calcium carbonate powder, 0.5 part of hydroxyethyl methyl cellulose ether with a viscosity of 75000, and 1.5 parts of wood fiber and add them to a dry powder mixing mixer and stir Uniform spare;

[0037] Step 2: Then weigh 31.93 parts of silicon-acrylic emulsifier and add it to the cylinder mixing tank, start the mixer, the stirring speed is 50--100r / min, add 0.25 parts of mineral oil type defoamer, dodecyl alcohol while stirring 0.7 parts of ester, 0.12 parts of isothiazolinone derivative fungicide and organic nitrogen-containing compound preservative, let them mix well, then add the powder mixed in (1), mix well and stir evenly to get a multi-functional paste Shaped clay products.

Embodiment 2

[0039] Step 1 Weigh 43 parts of 70-100 mesh quartz sand, 35 parts of 325 mesh quartz powder, 0.2 part of hydroxypropyl methylcellulose ether with a viscosity of 150000, and 1 part of wood fiber, and add them to a dry powder mixing mixer and stir evenly for later use;

[0040] Step 2: Then weigh 20 parts of pure acrylic emulsifier and add it to the cylinder mixing tank, start the mixer, and the stirring speed is 50--100r / min, while stirring, add 0.2 parts of silicone defoamer, lauryl alcohol ester 0.5 part, 0.1 part of isothiazolinone derivative fungicide and organic nitrogen-containing compound preservative, let them fully mix evenly, then add the powder mixed in step 1, fully mix and stir to get a multifunctional paste cement finished product.

Embodiment 3

[0042] Step 1 Weigh 31.2 parts of 100-140 mesh quartz sand, 25 parts of 325 mesh heavy calcium carbonate powder, 0.35 part of hydroxypropyl methylcellulose ether with a viscosity of 100000, and 2 parts of wood fiber, and add them to a dry powder mixing mixer and stir evenly spare;

[0043] Step 2: Then weigh 400g of silicon-acrylic emulsifier and add it to the tank mixing tank, start the mixer, and the stirring speed is 50--100r / min, while stirring, add 0.3 parts of silicone defoamer, 1 lauryl alcohol ester 0.15 parts of isothiazolinone derivative fungicide and organic nitrogen-containing compound preservative, let them mix well, then add the powder mixed in (1), mix well and stir evenly to get multifunctional paste cement finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses multifunctional paste-shaped plaster and a preparation method thereof. The multifunctional paste-shaped plaster is prepared from 30-45 parts of quartz sand, 25-35 parts of packing, 0.2-0.5 part of water retention thickening agent, 20-40 parts of emulsifying agent, 0.5-1 part of coalescing agent, 0.1-0.15 part of preservative, 0.2-0.3 part of defoaming agent and 1-2 parts of anti-cracking fibers. The preparation method includes the steps that the quartz sand, the packing, the water retention thickening agent and the wood fibers are weighed first, and then are evenly stirred after being mixed, so that a mixed material is obtained; afterwards, a certain quantity of silicone-acrylic emulsifying agent is weighed and added into a stirring machine to be stirred, the defoaming agent, the coalescing agent and the preservative are added while stirring is carried out, and the mixture is fully and evenly mixed; then the mixed material which is well mixed before is added to be fully mixed and evenly stirred. The plaster does not contain cement, and thus the efflorescence condition can be avoided when solidified plaster meets rainwater.

Description

technical field [0001] The invention relates to the field of construction, and more specifically relates to a multifunctional paste-like cement and a preparation method thereof. Background technique [0002] Clay is a muddy plastic solid with strong adhesive properties. This type of plastic solid is generally composed of solid or liquid adhesives with adhesive properties and powder fillers with certain functions. Appropriate pigments and Accessories. [0003] The Chinese patent application number is 201210453312.9, which discloses a polymer cement, which is a single-component, dry powder, water-based, processed through scientific proportioning, and integrates waterproof, bonding, plugging and leveling functions. An integrated non-toxic and tasteless water-based self-leveling cement-based rigid-flexible waterproof paste plugging and leveling material, which belongs to cement-based polymer water-based dry powder waterproof mortar. However, composite Portland cement is added ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/32C04B24/04C04B24/42C04B24/08C04B24/12C04B24/38C04B103/69C04B103/50C04B103/44
Inventor 单秀军张裕强
Owner 苏州大乘环保新材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap