A kind of negative ion coating of ultraviolet curing and preparation method thereof

A technology of negative ion coating and ultraviolet light, which is applied in the direction of epoxy resin coating, polyurea/polyurethane coating, coating, etc., to achieve the effect of fast curing speed

Active Publication Date: 2017-09-12
瑞通高分子科技(浙江)有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many patents for negative ion coatings in China, but there is no invention patent for ultraviolet negative ion coatings. It is of great practical significance to develop negative ion coatings with ultraviolet light and environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of negative ion coating of ultraviolet curing and preparation method thereof
  • A kind of negative ion coating of ultraviolet curing and preparation method thereof
  • A kind of negative ion coating of ultraviolet curing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] The preparation of nano-anion slurry is: nano-anion powder: hydroxyethyl methacrylate = 1:4, first add hydroxyethyl methacrylate in the reaction kettle, and slowly add nano-anion powder and dispersant under stirring state, control Warm at 50-60°C for 3 hours. Wherein the dispersant is a special nanometer dispersant which belongs to the macromolecule anion type, and its consumption is 5-8% of the negative ion powder. Then refine to a fineness of less than 10um.

[0042] The negative ion powder is: nano-scale iron magnesium tourmaline powder, terbium oxide, twelve calcium fourteen aluminum oxide, coral fossils; opal; serpentine; a mixture of at least two kinds of medical stone. Preference is given to a mixture of ferrite powder, terbium oxide, and opal.

[0043] The UV oligomer is one or a mixture of several oligomers in bisphenol A epoxy acrylate, urethane acrylate, amino acrylate and polyester acrylate. Among them, bisphenol A epoxy acrylate and urethane acrylate are...

Embodiment 2

[0050] Pump the above components 1, 2, and 4 into the reactor, heat, add 50% of the catalyst at 65°C, control the temperature at 100-105°C until the acid value is less than 1.0mgKOH / g, then add the rest of the catalyst After 20 minutes of reaction, the temperature can be lowered to 80°C and the material can be discharged. The PE related indicators: viscosity 80-200mpa.s / 60℃; AV<1.0mgKOH / g. The preparation MF of embodiment 2 nano negative ion slurry

[0051] Prepare the nano-anion slurry according to the formula data in the following table 2

[0052]

[0053]

[0054] Pump hydroxyethyl methacrylate into the reaction kettle, add nano-dispersant and stir evenly, slowly add nano-anion powder, and control the temperature at 50-60°C for 3 hours. Then refine to a fineness of less than 10um for later use.

Embodiment 3

[0055] Embodiment 3 prepares ultraviolet light curing anion coating

[0056] The paint is prepared according to the 3 groups of data formulas in Table 3.

[0057]

[0058] Make the above components into coatings and control related indicators; fineness: 200mj / cm 2 (curing degree RAU95%).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a UV-curable anion coating and a preparation method thereof. The invention provides a UV-curable composition, which comprises: an oligomer; a diluent monomer; a halogenated acrylate; an initiator, and a nano-anion slurry materials, coating additives. Wherein the amount of halogenated acrylate is 10-15%, and the halogenated acrylate is the reaction product of the following substances: epichlorohydrin; methacrylic acid; catalyst; wherein, the catalyst is a quaternary ammonium salt but not limited to: benzyl triethyl Ammonium chloride, tetrabutylammonium bromide, consumption is 0.2-0.3% of the total amount of this step. The amount of nano-anion slurry is 15-25%. The nano-anion powder and hydroxyethyl methacrylate are stirred in a special dispersant and the temperature is controlled at 50-60°C for 3 hours. When the coating amount reaches 40g / m2, the amount of negative ions generated by the UV curable negative ion coating composition is greater than 2000 / cm3.

Description

technical field [0001] The invention belongs to the field of UV (ultraviolet light curing) coating preparation, and the invention particularly relates to a preparation method of an ultraviolet light curing negative ion coating. Background technique [0002] Negative ions can not only promote the synthesis and storage of vitamins in the human body, but also strengthen and activate the physiological activities of the human body, so it is also called "air vitamin". , such as after a thunderstorm, the negative ions in the air increase, and people feel comfortable. In the air-conditioned room, because the negative ions in the air almost disappear after a series of air-conditioning purification treatments and long ventilation ducts, people will feel chest tightness, dizziness, fatigue, and decline in work efficiency and health when they stay in it for a long time. syndrome". In the medical field, negative ions are recognized as an effective means of killing germs and purifying t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information