Insulation electric pole

A technology for utility poles and materials, which is applied in the field of electric power materials, can solve the problems of low tensile strength and compressive strength of utility poles, high cost of molding process, irregular pores, etc., and achieve excellent uniformity of pore size, light weight, and crack resistance good strength effect

Active Publication Date: 2016-02-17
南通旭德科技有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Electric poles made of ordinary concrete have the properties of light weight, low maintenance requirements, and good insulation, but the molding process is not only costly, but also has defects such as material shortage, irregular pores, warping deformation, and foaming during the production process. defect
The tensile strength and compressive strength of the formed utility poles are low, and they are prone to breakage in bad weather

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An insulated utility pole, which is prepared according to the following method:

[0020] 1) Put corn stalks and peanut shells into a pulverizer at a weight ratio of 1:1 for crushing, and pass through a 50-mesh sieve to obtain material A;

[0021] 2) Mix polyurethane foam and egg shell according to the weight ratio of 1:1, crush it into 50-mesh powder, then add the same weight of water and soak for 30 minutes to obtain material B;

[0022] 3) Grind and pulverize the discarded fish bones, then add 20g / L sodium hydroxide aqueous solution accounting for twice the weight of the discarded fish bones and soak for 120 hours, then heat to 60°C, extract for 6 hours, and finally add dodecylbenzene Sodium sulfonate, stir evenly to obtain material C; the weight ratio of waste fish bone and sodium dodecylbenzene sulfonate is 3:1;

[0023] 4) Add 100 parts of 42.5 ordinary Portland cement, 60 parts of crushed stone, 35 parts of blast furnace slag, 30 parts of carbide slag, 20 parts o...

Embodiment 2

[0027] An insulated utility pole, which is prepared according to the following method:

[0028] 1) Put corn stalks and peanut shells into a pulverizer at a weight ratio of 1:1 for crushing, and pass through a 50-mesh sieve to obtain material A;

[0029] 2) Mix polyurethane foam and egg shell according to the weight ratio of 1:1, crush it into 50-mesh powder, then add the same weight of water and soak for 30 minutes to obtain material B;

[0030] 3) Grind and pulverize the discarded fish bones, then add 20g / L sodium hydroxide aqueous solution accounting for twice the weight of the discarded fish bones and soak for 120 hours, then heat to 60°C, extract for 6 hours, and finally add dodecylbenzene Sodium sulfonate, stir evenly to obtain material C; the weight ratio of waste fish bone and sodium dodecylbenzene sulfonate is 3:1;

[0031] 4) Add 120 parts of 42.5 ordinary Portland cement, 80 parts of crushed stone, 45 parts of blast furnace slag, 40 parts of carbide slag, 30 parts o...

Embodiment 3

[0035] Taking Example 2 as an example, the performance of the product prepared by the present invention is as follows:

[0036] The thickness of the concrete layer is 60mm;

[0037] Concrete compressive strength: 157MPa;

[0038] Concrete flexural strength: 18.6MPa;

[0039] Concrete impermeability performance: P12 level without water seepage height;

[0040] Concrete carbonation resistance: 28 days carbonation detection depth is 0.3mm;

[0041] Concrete freeze-thaw resistance: 400 freeze-thaw cycles without quality loss;

[0042] Electric pole crack test: r 0 cr ≥1.3, the design of ordinary partially prestressed poles r 0 cr ≥0.8;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of electric materials, and discloses an insulation electric pole. The insulation electric pole is made through the following steps: 1, preparing a material A; 2, preparing a material B; 3, preparing a material C; 4, preparing concrete; and 5, molding, and demolding. The electric pole has good freeze thaw resistance, good compressive strength and good rupture strength.

Description

technical field [0001] The invention belongs to the technical field of electric power materials, and in particular relates to an insulated utility pole. Background technique [0002] The utility poles used in traditional overhead transmission lines generally have defects such as heavy weight, perishability, and poor durability. They have a short lifespan, require frequent maintenance during operation, and are prone to various safety hazards. For example, steel poles and iron towers also have problems such as corrosion and rust, construction, transportation and maintenance difficulties. For ultra-high voltage and ultra-high voltage power transmission, because the self-weight of steel poles and iron towers exceeds the strength limit, the height of the tower cannot be raised. In the annual transmission line tripping accidents, lightning strike accidents and pollution flashover accidents account for almost half each. Extensive use of composite insulators still cannot completely...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B14/02C04B18/14C04B18/04C04B22/14C04B18/24C04B16/08
CPCY02W30/91
Inventor 刘杰王东阳王士勇张恒李效忠
Owner 南通旭德科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com