Light weight porous melamine resin type border-crossing capturing material and preparation method thereof

A technology of transboundary capture material and melamine resin, which is applied in the field of lightweight porous melamine resin transboundary capture material and its preparation, can solve the problems that it is difficult to meet the requirements of EMAS materials, and overcome the flammability and antifreeze performance of sprayed organic matter Good, good frost resistance effect

Active Publication Date: 2016-03-09
朱晓燕
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to flammability, it is difficult to meet the requirements of EMAS materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light weight porous melamine resin type border-crossing capturing material and preparation method thereof
  • Light weight porous melamine resin type border-crossing capturing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A preparation process for a lightweight porous melamine resin transboundary capture material, comprising the following steps:

[0056] 1) Preparation of suspension: Dissolve 100 parts by weight of melamine formaldehyde resin in 33.3 parts by weight of water, add 300 parts by weight of a mixture of petrolatum and montmorillonite, 15 parts by weight of alkylphenol polyoxyethylene ether, 60 parts by weight of n-pentyl Alkanes and normal hexane mix blowing agent, 22 parts by weight of sulfuric acid by 1:1, stir and mix uniformly to form stable slurry, the particle diameter of described stone fat and montmorillonite is 1mm, and described melamine formaldehyde resin is melamine, The precondensate of formaldehyde, the molar ratio of melamine and formaldehyde is 1:1 when it is synthesized;

[0057] 2) Put the slurry prepared in step 1) in a 2450MHz tunnel-type microwave heating furnace at a temperature of 80°C, foam and solidify for 1.8 hours, and the slurry undergoes a curing ...

Embodiment 2

[0063] A preparation process for a lightweight porous melamine resin transboundary capture material, comprising the following steps:

[0064] 1) Preparation of suspension: Dissolve 100 parts by weight of melamine formaldehyde resin in 33.3 parts by weight of water, add 400 parts by weight of a mixture of vermiculite and illite, 20 parts by weight of fatty acid polyethylene glycol ether, 70 parts by weight of petroleum ether, 25 parts by weight part formic acid, stirring and mixing uniformly to form stable slurry, the particle diameter of described vermiculite and illite is 0.5mm, and described melamine-formaldehyde resin is the precondensate of melamine, formaldehyde, and the mol ratio of melamine and formaldehyde is 2 during its synthesis :1;

[0065] 2) Put the slurry prepared in step 1) in a 2000MHz tunnel-type microwave heating furnace at a temperature of 75°C, foam and solidify for 2 hours, and the slurry undergoes a curing reaction to form a lightweight porous material, ...

Embodiment 3

[0071] A preparation process for a lightweight porous melamine resin transboundary capture material, comprising the following steps:

[0072] 1) Preparation of suspension: Dissolve 100 parts by weight of melamine formaldehyde resin in 33.3 parts by weight of water, add 500 parts by weight of a mixture of allophane and aphthite, 25 parts by weight of alkyltrimethylammonium salt, 80 parts by weight of n-hexyl Alkane, 28 parts by weight of acetic acid, stirred and mixed uniformly to form a stable slurry, the particle diameter of the allophane and apophyllite is 0.1mm, and the melamine-formaldehyde resin is a precondensate of melamine and formaldehyde, and melamine is synthesized The molar ratio with formaldehyde is 3:1;

[0073] 2) Put the slurry prepared in step 1) in a 915MHz tunnel-type microwave heating furnace at a temperature of 75°C, foam and solidify for 2 hours, and the slurry undergoes a curing reaction to form a lightweight porous material, which is then dried naturall...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a light weight porous melamine resin type border-crossing capturing material and a preparation method thereof. The preparation method comprises the following steps: (1) evenly mixing crystal water mineral powder, melamine-formaldehyde resin, a surfactant, and a curing agent according to a certain ratio to form stable slurry; (2) heating the slurry prepared in the step (1) to a temperature of 70 to 85 DEG C, rapidly adding a foaming agent, and carrying out curing reactions to form a light weight porous material; (3) drying the light weight porous material obtained in the step (2); (4) cutting the light weight porous material obtained in the step (3) according to the size requirements through hot cutting. The prepared capturing material has a good anti-freezing performance and overcomes the shortage of easily flammable property of common spraying organic substances.

Description

technical field [0001] The invention relates to the field of novel materials, in particular to a lightweight porous melamine resin transboundary capture material and a preparation process thereof. Background technique [0002] Aircraft stalling off the runway during takeoff and landing often leads to serious aviation accidents. In order to avoid such aviation accidents, active and passive capture methods can effectively prevent aircraft from rushing out of the runway safety zone and reduce accidents. Among them, the active capture adopts the aircraft parachute and hook lock system. This method is suitable for military aircraft with relatively small volume, more frequent takeoffs and faster speed. For large-scale civil aircraft, it is commonly used in the world to install the characteristic material arresting system (EMAS) at the end of the runway. [0003] The main functional unit of a performance material arresting system is the arresting bed. At present, the unit materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/28C08L71/02C08K3/34C08K5/19C08K3/22C08J9/14C08J9/10
CPCC08J9/10C08J9/14C08K3/22C08K3/34C08K5/19C08L61/28C08L71/02C08J9/103C08J2203/04C08J2361/28C08K2003/2224C08K2201/014C08L2201/02C08L2203/14C08K3/346
Inventor 朱晓燕
Owner 朱晓燕
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap