Preparation method of collagen fiber/silver chloride hybrid material

A collagen fiber and hybrid material technology, applied in fiber processing, animal fibers, flame retardant fibers, etc., can solve the problems of easy erosion by mold, bacteria, application limitation of collagen fibers, poor thermal stability, etc., and achieve good antibacterial properties. , high application value, good thermal stability

Active Publication Date: 2016-03-09
HUNAN UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, collagen fiber has defects such as strong water absorption, easy to be eroded by microorganisms and chemicals, poor thermal stability, and flammability; collagen fiber is mainly composed of collagen, which has the general properties of protein and is easily eroded by mold and bacteria; therefore, The application of collagen fibers in industry is relatively limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Collagen fiber 0.2g, 20ml silver nitrate solution (concentration is 2.5%) join in the reaction vessel that stirrer is arranged, leave standstill 12 hours after stirring for 4 hours; Slowly add dropwise 10ml sodium chloride solution ( Concentration is 3.5%), the dropping speed of sodium sulfate solution is about 0.5 drop / second; Fiber / Silver Chloride Hybrid Materials.

[0017] The hybrid material is observed under a scanning electron microscope, and it can be found that silver chloride particles are attached to the surface of collagen fibers. The water absorption rate of the collagen fiber material before modification is 436%, and the water absorption rate after modification is 141%, and the water absorption rate is greatly reduced. The hybrid material has good antibacterial activity against Aspergillus flavus, Aspergillus niger, Escherichia coli and the like.

Embodiment 2

[0019] Collagen fiber 0.3g, 20ml silver nitrate solution (concentration is 3%) join in the reaction vessel that stirrer is arranged, leave standstill 12 hours after stirring for 4 hours; Slowly add 10ml sodium chloride solution ( Concentration is 3.5%), the dropping speed of sodium sulfate solution is about 0.5 drop / second; Fiber / Silver Chloride Hybrid Materials.

[0020] The hybrid material is observed under a scanning electron microscope, and it can be found that silver chloride particles are attached to the surface of collagen fibers. The water absorption rate of the collagen fiber material before modification is 436%, and the water absorption rate after modification is 135%, so the water absorption rate is greatly reduced. The hybrid material has good antibacterial activity against Aspergillus flavus, Aspergillus niger, Escherichia coli and the like.

Embodiment 3

[0022] Collagen fiber 0.4g, 20ml silver nitrate solution (concentration is 3.5%) join in the reaction vessel that stirrer is arranged, leave standstill 12 hours after stirring for 4 hours; Slowly add dropwise 10ml sodium chloride solution ( Concentration is 3.5%), the dropping speed of sodium sulfate solution is about 0.5 drop / second; Fiber / Silver Chloride Hybrid Materials.

[0023] The hybrid material is observed under a scanning electron microscope, and it can be found that silver chloride particles are attached to the surface of collagen fibers. The water absorption rate of the collagen fiber material before modification is 436%, and the water absorption rate after modification is 129%, and the water absorption rate is greatly reduced. At the same time, the hybrid material has good antibacterial activity against Aspergillus flavus, Aspergillus niger, Escherichia coli and so on. Example 4:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a preparation method of a collagen fiber / silver chloride hybrid material. The method is mainly as follows: weighing 2-5 parts by weight of collagen fiber, adding into 200 parts by weight of a silver nitrate solution with the concentration of 2.5% to 4%, stirring for 4 hours, then standing for 12 hours; while stirring, slowly adding dropwise 100 parts by weight of a sodium chloride solution with the concentration of 3.5%, wherein the dropping rate of the sodium chloride solution is controlled in 0.5 drop / sec; after the dropwise addition is complete, standing for 5 minutes, then filtering by suction, and washing with water; and finally, drying in vacuum for 5 to 8 hours at a temperature of 60-80 DEG C to obtain the collagen fiber / silver chloride hybrid material. Through the method, the defects of being high in water absorption, hygroscopic, low in thermal stability, perishable, low in mechanical strength and the like of the collagen fiber can be improved, the antibacterial properties of the material can be greatly enhanced, the scope of application in industry can be broadened; the technology is simple, the reaction is carried out at room temperature in ordinary pressure, device requirements are not critical, and the method is suitable for mass production.

Description

technical field [0001] The invention belongs to the technical field of organic-inorganic hybrid materials, and in particular relates to a preparation method of a collagen fiber / silver chloride hybrid material. Background technique [0002] Collagen fiber is the largest biomass resource in the world, and collagen fiber accounts for more than 90% of the large amount of waste leather produced by the tanning industry. Recycling waste leather, treating it in a suitable way and applying it in various industries can not only effectively control the environment, but also create huge economic benefits. Collagen fibers are white short fibrous solids with good biodegradability, biocompatibility, low antigenicity, low cytotoxicity, etc., and can be used in food, medicine, cosmetics and other fields; the surface of collagen fibers is rich in -OH, -COOH, -CONH 2 , -NH 2 And other active groups, so it also has a strong application potential in the fields of separation engineering, texti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/13D06M101/14
CPCD06M11/13D06M2101/14D06M2200/30
Inventor 周虎周杰余斌周智华李文奎陈昭明
Owner HUNAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products