High-gloss anti-scratch waterborne glazing oil and preparation method thereof
A water-based varnish, high-gloss technology, applied in coatings, paper coatings, textiles and papermaking, etc., can solve the problems of high hardness, easy to be scratched, poor toughness, etc., to achieve high gloss, good adhesion, The effect of improving flexibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1
[0020] The high-gloss and scratch-resistant water-based varnish of this embodiment, in parts by weight, includes 50 parts of styrene-acrylic emulsion, 10 parts of acrylic modified polyurethane emulsion, 10 parts of alkali-soluble acrylic resin, 0.1 part of defoamer, and 10 parts of wax emulsion , 4 parts wetting agent, 0.5 part slip agent, 8 parts dodecyl alcohol ester and 7.5 parts water.
[0021] Among them, the acrylic modified polyurethane emulsion is prepared by the following method: add 200g polyethylene glycol (PEG2000) to a 500mL four-necked flask with a stirrer, a condenser and a thermometer, heat it up to 120°C to make it melt, and put it in a vacuum of 10mmHg. Dehydration under vacuum for 2 hours, then cooled to 80 °C, stopped vacuuming, passed nitrogen, and added 90 g of isophorone diisocyanate dropwise. After constant temperature reaction for 3 hours, 10 g of dimethylolpropionic acid and 0.1 g of dibutyltin dilaurate were added to continue. Re...
Example Embodiment
[0023] Example 2
[0024] The high-gloss and scratch-resistant water-based varnish of this embodiment, in parts by weight, includes 30 parts of styrene-acrylic emulsion, 30 parts of acrylic modified polyurethane emulsion, 10 parts of alkali-soluble acrylic resin, 0.1 part of defoamer, and 10 parts of wax emulsion , 4 parts wetting agent, 0.5 part slip agent, 6 parts dodecyl alcohol ester and 7.5 parts water.
[0025] Wherein, the acrylic modified polyurethane emulsion is prepared by the following method: add 250g polyethylene glycol (PEG2000) to a 500mL four-necked flask with a stirrer, a condenser and a thermometer, heat it up to 120°C to make it melt, and put it in a vacuum of 10mmHg. Dehydration under vacuum for 3 hours, then cooling to 80°C, stop vacuuming, pass nitrogen, add 110g isophorone diisocyanate dropwise, after constant temperature reaction for 3 hours, add 15g dimethylolpropionic acid and 1.3g dibutyltin dilaurate to continue Reaction; measure the NCO value ev...
Example Embodiment
[0027] Example 3
[0028] The high-gloss and scratch-resistant water-based varnish of this embodiment, in parts by weight, includes 20 parts of styrene-acrylic emulsion, 40 parts of acrylic modified polyurethane emulsion, 10 parts of alkali-soluble acrylic resin, 0.1 part of defoamer, and 10 parts of wax emulsion , 4 parts wetting agent, 0.5 part slip agent, 4 parts dodecyl alcohol ester and 7.5 parts water.
[0029] Wherein, the acrylic modified polyurethane emulsion is prepared by the following method: add 230g polyethylene glycol (PEG2000) to a 500mL four-necked flask with a stirrer, a condenser and a thermometer, heat it up to 120°C to make it melt, and put it in a vacuum of 10mmHg. Dehydration under vacuum for 2.5h, then cooling to 80℃, stop vacuuming, pass nitrogen, add 100g isophorone diisocyanate dropwise, after constant temperature reaction for 3h, add 12g dimethylolpropionic acid and 0.8g dibutyltin dilaurate Continue the reaction; measure the NCO value every 30mi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap