Composite fluorocarbon resin coating with excellent adhesion

A technology of compounding fluorocarbon resin and fluorocarbon resin, used in epoxy resin coatings, anti-corrosion coatings, polyester coatings, etc., can solve the problems of insufficient adhesion performance, strong chemical corrosion performance, etc. The effect of good focus and film compactness, excellent heat resistance and adhesion, and excellent corrosion resistance

Inactive Publication Date: 2016-03-16
合肥市易远新材料有限公司
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Fluorocarbon coating is a coating made of fluorocarbon resin as a film-forming substance. Due to the existence of F-C bonds in the macromolecular chain of fluororesin, the fluororesin coating formulated with fluororesin as the base material has many excellent properties, such as super-resistant Weather aging, super anti-fouling ability, etc.; but the adhesion performance of traditional fluorocarbon resins can not meet the demand, and the strong chemical corrosion performance needs to be improved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of composite fluorocarbon resin coating with excellent adhesion, its raw materials include by weight: 15 parts of modified FEVE fluorocarbon resin, 60 parts of epoxy modified alkyd resin, 20 parts of epoxy resin, 3 parts of dicyandiamide , 1 part of sodium dodecylbenzenesulfonate, 8 parts of carboxymethyl cellulose, 1 part of ethylene glycol ethyl ether acetate, 15 parts of superfine calcium carbonate, 2 parts of magnesium silicate, 15 parts of kaolin, 2 parts of talcum powder , 6 parts of graphene, 2 parts of amyl acetate, 10 parts of propylene glycol, 1 part of wetting agent, 3 parts of preservative, 2 parts of ethyl acetate, 7 parts of butylated amino resin, 2 parts of methyl etherified amino resin, water 80 servings.

Embodiment 2

[0018] A kind of composite fluorocarbon resin coating with excellent adhesion, its raw materials include by weight: 35 parts of modified FEVE fluorocarbon resin, 20 parts of epoxy modified alkyd resin, 35 parts of epoxy resin, 1 part of dicyandiamide , 2 parts of sodium dodecylbenzenesulfonate, 3 parts of carboxymethyl cellulose, 5 parts of ethylene glycol ethyl ether acetate, 5 parts of superfine calcium carbonate, 10 parts of magnesium silicate, 5 parts of kaolin, 8 parts of talcum powder , 2 parts of graphene, 8 parts of amyl acetate, 4 parts of propylene glycol, 3 parts of wetting agent, 1 part of preservative, 10 parts of ethyl acetate, 2 parts of butylated amino resin, 6 parts of methyl etherified amino resin, water 40 servings.

Embodiment 3

[0020] A kind of composite fluorocarbon resin coating with excellent adhesion, its raw materials include by weight: 20 parts of modified FEVE fluorocarbon resin, 50 parts of epoxy modified alkyd resin, 26 parts of epoxy resin, 2.3 parts of dicyandiamide , 1.6 parts of sodium dodecylbenzenesulfonate, 6.5 parts of carboxymethyl cellulose, 2 parts of ethylene glycol ethyl ether acetate, 13 parts of superfine calcium carbonate, 4 parts of magnesium silicate, 12 parts of kaolin, 4 parts of talcum powder , 4.5 parts of graphene, 4 parts of amyl acetate, 8 parts of propylene glycol, 1.5 parts of wetting agent, 2.6 parts of preservative, 3 parts of ethyl acetate, 5 parts of butylated amino resin, 3 parts of methyl etherified amino resin, water 65 servings.

[0021] The ion exchange capacity of kaolin is 5mg / 100g.

[0022] The modified FEVE fluorocarbon resin is prepared by the following process: 200-00 parts by weight of dichloromethane, 80 parts of FEVE fluorocarbon resin, 30 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses composite fluorocarbon resin coating with excellent adhesion. The coating is prepared from the following raw materials in parts by weight: 15-35 parts of modified FEVE fluorocarbon resin, 20-60 parts of epoxy modified alkyd resin, 20-35 parts of epoxy resin, 1-3 parts of dicyandiamide, 1-2 parts of sodium dodecyl benzene sulfonate, 3-8 parts of carboxymethylcellulose, 1-5 parts of ethylene glycol monoethyl ether acetate, 5-15 parts of super fine calcium carbonate, 2-10 parts of magnesium silicate, 5-15 parts of kaolin, 2-8 parts of talc powder, 2-6 parts of graphene, 2-8 parts of amyl acetate, 4-10 parts of propylene glycol, 1-3 parts of a wetting agent, 1-3 parts of preservative, 2-10 parts of ethyl acetate, 2-7 parts of butylated amino resin, 2-6 parts of methylated amino resin and 40-80 parts of water. The composite fluorocarbon resin coating has good adhesion and excellent corrosion resistance.

Description

technical field [0001] The invention relates to the technical field of fluorocarbon resin coatings, in particular to a composite fluorocarbon resin coating with excellent adhesion. Background technique [0002] With the increasingly stringent requirements of the society for energy conservation and environmental protection, coating products show a development trend of high performance, zero volatile organic compounds, and zero pollution. Fluorocarbon coating is a coating made of fluorocarbon resin as a film-forming substance. Due to the existence of F-C bonds in the macromolecular chain of fluororesin, the fluororesin coating formulated with fluororesin as the base material has many excellent properties, such as super-resistant Weather aging resistance, super anti-fouling ability, etc.; but the adhesion performance of traditional fluorocarbon resins cannot meet the demand, and the strong chemical corrosion performance needs to be improved urgently. Contents of the invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D167/08C09D163/00C09D127/12C09D5/08C09D7/12
Inventor 李政源
Owner 合肥市易远新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com