Multi-principle-element alloy and method thereof for processing surface of aluminum alloy

A multi-principal element alloy and aluminum alloy surface technology, applied in metal material coating process, coating, fusion spraying, etc., can solve problems such as joint interface cracks and cracks, and achieve uniform fusion, porosity reduction, and improved bonding Effect of Strength and Intrinsic Quality of Coatings

Active Publication Date: 2016-03-30
ZHOUSHAN HECHENG MACHINERY
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of ceramic powder to improve the wear resistance of aluminum alloys cannot essentially so

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1

[0018] 1. A multi-principal alloy, calculated in mole parts, including the following components: 14 parts Co, 16 parts Cr, 1 part Al, 20 parts Si, 20 parts Fe, 5 parts Ti, 19 parts Mn, 2 parts B , 3 parts of La.

[0019] 2. The above-mentioned multi-principle alloy is used for surface treatment of aluminum alloy, including the following steps:

[0020] 1) Clean the ZL102 aluminum alloy substrate with acetone; in order to improve the bonding strength between the multi-principal alloy coating and the aluminum alloy substrate, after cleaning, perform sandblasting and roughening treatment.

[0021] 2) Use plasma spraying equipment to spray the multi-principal alloy powder with a good proportion on the surface of the aluminum alloy substrate after step 1); wherein the particle size of the multi-principal alloy powder is -200~+350 mesh; Argon gas protection is carried out during the process, and the thickness is 0.3mm.

[0022] 3) Use TJ-HL-T5000 CO with a maximum power o...

Example Embodiment

[0024] Example 2

[0025] 1. A multi-principal alloy, based on mole parts, including the following components: 14 parts Co, 16 parts Cr, 1 part Al, 20 parts Si, 20 parts Fe, 5 parts Ti, 19 parts Mn, 2 parts B , 3 parts of La.

[0026] 2. The above-mentioned multi-principle alloy is used for surface treatment of aluminum alloy, including the following steps:

[0027] 1) Clean the 6061 wrought aluminum alloy aluminum alloy substrate with absolute ethanol; after the cleaning is completed, perform sandblasting and coarsening treatment.

[0028] 2) Use plasma spraying equipment to spray the multi-principal alloy powder with a good proportion on the surface of the aluminum alloy substrate after step 1); wherein the particle size of the multi-principal alloy powder is -200~+350 mesh; Argon gas protection is carried out during the process, and the thickness is 0.3mm.

[0029] 3) Use TJ-HL-T5000 CO with a maximum power of 5kW 2 The laser remelts the plasma sprayed surface treated in step 2). A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses multi-principle-element alloy and a method thereof for processing the surface of aluminum alloy. The alloy is prepared from, by molfraction, 14-22 parts of Co, 14-22 parts of Cr, 1-3 parts of Al, 14-22 parts of Si, 14-22 parts of Fe, 1-10 parts of Ti, 14-22 parts of Mn, 1-3 parts of B and 1-3 parts of La. The method includes the steps that an aluminum alloy substrate is firstly cleaned and subjected to sand blasting, multi-principle-element alloy powder is sprayed on the surface of the aluminum alloy substrate through a plasma spraying device, finally the plasma sprayed surface is remelted through a CO2 laser device, and then the multi-principle-element alloy is prepared. The characteristics of the high- entropy effect, the slow diffusion effect, nano phase strengthening, super-high lattice distortion and the 'cocktail effect' of the multi-principle-element alloy are utilized for a multi-principle-element alloy coating, high tenacity of the alloy can be easily kept, and the prepared coating has the beneficial effects of being high in strength, resistant to abrasion and the like.

Description

technical field [0001] The invention belongs to the technical field of material surface treatment and strengthening, and in particular relates to a multi-principal alloy and a method for surface treatment of aluminum alloys. Background technique [0002] Aluminum and aluminum alloys are one of the most widely used materials in non-ferrous metals. Aluminum alloys have many excellent properties such as low density, easy processing, low thermal expansion coefficient, high thermal conductivity, high specific stiffness and specific strength; therefore, in daily production and life And aviation, automobiles, high-speed rail, engine pistons, optical instruments, missile mosaic structures and other fields have been widely used. However, with the further development of industrial production, higher requirements are placed on the surface properties of aluminum alloys, and wear resistance is particularly important. [0003] At present, the method of preparing wear-resistant coatings...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C30/00C23C4/06C23C4/134C23C4/18
CPCC22C19/07C22C22/00C22C27/06C22C30/00C22C38/005C22C38/02C22C38/04C22C38/06C22C38/10C22C38/14C22C38/18C22C38/32C23C4/06C23C4/18
Inventor 黄灿涂坚刘承鑫柴林江黄福祥周志明
Owner ZHOUSHAN HECHENG MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap