Cable material with high expansion force

A high-expansion, cable technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve problems such as shortening service life, affecting cable performance, copper conductor oxidation, etc., to prolong service life, prolong aging resistance, save energy cost effect

Inactive Publication Date: 2016-04-06
王威淞
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Oxidation of copper conductors may occur during the production of cables, and the existing solution is to block the contact between copper and air, or use a passivation film to isolate the contact between copper and the outside world. Damage to the copper body itself seriously affects the performance of the cable and shortens its service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A cable material with high expansion force is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0015] 100 parts of polyvinyl chloride resin, 40 parts of PVC resin, 15 parts of PBT resin, 15 parts of dibutyl phthalate, 10 parts of benzoyl peroxide, 7 parts of dipentaerythritol hexaacrylate, 2 parts of silane coupling agent, 0.6 parts of antimicrobial agent composed of asarin and dihydrocapsaicin in a weight ratio of 2:3, 10 parts of corn stalk ash, 3 parts of graphite, magnesium oxide, zinc oxide and stearic acid in a weight ratio of 3:2:2 3 parts of anti-aging agent, 16 parts of filling material composed of heavy calcium carbonate and carbon toner according to the weight ratio of 3:5, and 4 parts of silica gel.

Embodiment 2

[0017] A cable material with high expansion force is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0018] 100 parts of polyvinyl chloride resin, 45 parts of PVC resin, 18 parts of PBT resin, 16 parts of dibutyl phthalate, 11 parts of benzoyl peroxide, 8 parts of dipentaerythritol hexaacrylate, 3 parts of silane coupling agent, 0.7 parts of antibacterial agent composed of asarin and dihydrocapsaicin in a weight ratio of 2:3, 13 parts of corn stalk ash, 4 parts of graphite, magnesium oxide, zinc oxide and stearic acid in a weight ratio of 3:2:2 4 parts of anti-aging agent, 17 parts of filling material composed of heavy calcium carbonate and carbon toner according to the weight ratio of 3:5, and 5 parts of silica gel.

Embodiment 3

[0020] A cable material with high expansion force is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0021] 100 parts of polyvinyl chloride resin, 50 parts of PVC resin, 20 parts of PBT resin, 18 parts of dibutyl phthalate, 12 parts of benzoyl peroxide, 10 parts of dipentaerythritol hexaacrylate, 4 parts of silane coupling agent, 0.8 parts of antibacterial agent composed of asarin and dihydrocapsaicin in a weight ratio of 2:3, 15 parts of corn stalk ash, 5 parts of graphite, magnesium oxide, zinc oxide and stearic acid in a weight ratio of 3:2:2 5 parts of anti-aging agent, 18 parts of filling material composed of heavy calcium carbonate and carbon toner according to the weight ratio of 3:5, and 6 parts of silica gel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cable material with high expansion force, and is characterized in that the cable material comprises the following raw materials in parts by weight: 100 parts of polyvinyl chloride resin, 40-50 parts of PVC resin, 15-20 parts of PBT resin, 15-18 parts of dibutyl phthalate, 10-12 parts of benzoyl peroxide, 7-10 parts of dipentaerythritol hexaacrylate, 2-4 parts of a silane coupling agent, 0.6-0.8 part of an antibacterial agent, 10-15 parts of straw ash, 3-5 parts of graphite, 3-5 parts of an anti-aging agent, 16-18 parts of a filling material, and 4-6 parts of silicone rubber. The cable material extends the aging resistance of the cable material, the filling material has the advantages of stable chemical structure, good gelation ability and high expansion ability, prolongs the service life of a cable, and saves the resources; a copper body is protected from avoiding oxidation, the copper body cannot be damaged, the service life is extended, the cost is saved, and the efficacy is improved; the addition of the straw ash, the requirements of the standards on environmental protection are met; and the extrusion process performance is excellent.

Description

technical field [0001] The invention belongs to the technical field of cable materials, in particular to a cable material with high expansion force. Background technique [0002] The application of high-voltage power cables in my country is very common and extensive. Most of the high-voltage power cables are laid underground and the environment is mostly humid. Moisture can easily penetrate into the interior of the cable structure. Therefore, under normal high-voltage energization, the theory of electrical stress believes that the internal stress of the cable during production and operation is the main reason for promoting the growth of water branches. When the cable is subjected to voltage and water, in the high-voltage power frequency electric field, the polar water molecules migrate strongly and convert the electric field energy into kinetic energy and heat energy, and the water molecules with huge energy move violently inside the insulation. The insulation level of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L67/02C08K13/02C08K3/22C08K5/09C08K3/26C08K3/04H01B3/44
CPCC08L27/06C08L2203/202C08L2205/025C08L2205/03H01B3/443
Inventor 王威淞
Owner 王威淞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products