Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Rubber material for motorcycle engine gasket

A rubber material and engine technology, applied in the rubber field, can solve the problems of thermal stability, hardness, tear resistance and aging resistance that cannot meet demand, the performance of engine rubber gaskets declines, and the performance changes gradually. Stable structure and good aging resistance

Inactive Publication Date: 2016-04-20
崇夕山
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Motorcycle engine rubber gaskets are prone to aging due to the combined effects of various external factors, and their properties gradually change, especially unsaturated carbon chain rubber, which is easily attacked by heat, oxygen and ozone, resulting in changes in the molecular structure of the rubber, especially Motorcycle engine rubber gaskets are exposed to high temperature and rugged road conditions for a long time, especially in hot summer environments, the performance of motorcycle engine rubber gaskets drops significantly. At present, motorcycle engine rubber gaskets have thermal stability, hardness, and tear resistance. and aging resistance can not meet the demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of rubber material for motorcycle engine gasket, its raw material comprises by weight: 10 parts of tetrapropylene fluoro rubber, 40 parts of chloroprene rubber, 15 parts of methyl vinyl trifluoropropyl silicone rubber, 35 parts of modified graphite, 0.5 parts of nano-zinc oxide, 35 parts of acetylene carbon black, 5 parts of gypsum, 8 parts of lignin, 10 parts of nano-silica, 16 parts of nano-clay, 1 part of triallyl isocyanurate, diisopropyl peroxide 2 parts of benzene, 0.2 parts of N,N'-m-phenylene bismaleimide, 2 parts of vulcanization accelerator TMTD, 1 part of N-methylene carboxyl-2-benzothiazole sulfenamide, polydimethylsilane 2 parts of oxane, 1 part of disproportionated rosin, 2 parts of anti-aging agent RD.

Embodiment 2

[0017] A kind of rubber material for motorcycle engine gasket, its raw material comprises by weight: 30 parts of tetrapropylene fluorine rubber, 20 parts of chloroprene rubber, 35 parts of methyl vinyl trifluoropropyl silicone rubber, 20 parts of modified graphite, 1.5 parts of nano-zinc oxide, 20 parts of acetylene carbon black, 15 parts of gypsum, 2 parts of lignin, 18 parts of nano-silica, 8 parts of nano-clay, 2 parts of triallyl isocyanurate, diisopropyl peroxide 1 part of benzene, 0.8 parts of N,N'-m-phenylene bismaleimide, 1 part of vulcanization accelerator TMTD, 2 parts of N-methylene carboxyl-2-benzothiazole sulfenamide, polydimethylsiloxane 1 part of oxane, 2 parts of disproportionated rosin, 1 part of anti-aging agent RD.

Embodiment 3

[0019] A kind of rubber material for motorcycle engine gasket, its raw material comprises by weight: 20 parts of tetrapropylene fluorine rubber, 35 parts of chloroprene rubber, 20 parts of methyl vinyl trifluoropropyl silicone rubber, 30 parts of modified graphite, 0.8 parts of nano-zinc oxide, 25 parts of acetylene carbon black, 10 parts of gypsum, 5 parts of lignin, 15 parts of nano-silica, 14 parts of nano-clay, 1.2 parts of triallyl isocyanurate, diisopropyl peroxide 1.8 parts of benzene, 0.4 parts of N,N'-m-phenylene bismaleimide, 1.5 parts of vulcanization accelerator TMTD, 1.4 parts of N-methylene carboxyl-2-benzothiazole sulfenamide, polydimethyl 1.8 parts of base siloxane, 1.2 parts of disproportionated rosin, and 1.8 parts of anti-aging agent RD.

[0020] The modified graphite is prepared by the following process: 40 parts by weight of graphite powder, 30 parts of sodium nitrate, and 50 parts of sulfuric acid solution with a mass fraction of 88wt% are mixed, stirred ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber material for a motorcycle engine gasket, which is prepared from the following raw materials in parts by weight: 10-30 parts of tetrafluoroethylene-propylene rubber, 20-40 parts of neoprene, 15-35 parts of methyl vinyl trifluoropropyl silicone rubber, 20-35 parts of modified graphite, 0.5-1.5 parts of nano zinc oxide, 20-35 parts of acetylene black, 5-15 parts of gypsum, 2-8 parts of lignin, 10-18 parts of nano silicon dioxide, 8-16 parts of nano argil, 1-2 parts of triallyl isocyanurate, 1-2 parts of dicumyl peroxide, 0.2-0.8 part of N,N'-m-phenylenedimaleimide, 1-2 parts of vulkacit TMTD, 1-2 parts of N-methylene carboxyl-2-benzothiazole sulfonamide, 1-2 parts of polydimethylsiloxane, 1-2 parts of disproportionated rosin and 1-2 parts of antiager RD. The rubber material is high in hardness, thermally stable, good in heat resistance and excellent in tearing resistance performance.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a rubber material for a motorcycle engine gasket. Background technique [0002] Motorcycle engine rubber gaskets are prone to aging due to the combined effects of various external factors, and their properties gradually change, especially unsaturated carbon chain rubber, which is easily attacked by heat, oxygen and ozone, resulting in changes in the molecular structure of the rubber, especially Motorcycle engine rubber gaskets are exposed to high temperature and rugged road conditions for a long time, especially in hot summer environments, the performance of motorcycle engine rubber gaskets drops significantly. At present, motorcycle engine rubber gaskets have thermal stability, hardness, and tear resistance. And aging resistance can not meet the demand. Contents of the invention [0003] The invention provides a rubber material for a motorcycle engine gasket, which has high ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/02C08L83/08C08L27/12C08L83/04C08K13/06C08K9/04C08K3/04C08K3/36C08K3/22C08K5/14
CPCC08L11/02C08K2201/011C08K2201/014C08L83/08C08L2201/08C08L2205/035
Inventor 不公告发明人
Owner 崇夕山
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com