A kind of environment-friendly cold-setting black ink and its production process

A technology of black ink and production process, applied in ink, household utensils, applications, etc., can solve the problems of limited use range of cold-set ink, affect the quality of printed matter, and high price, so as to enhance the adaptability of ink stacking and shorten the bead milling time , the effect of increasing solid content

Active Publication Date: 2018-05-15
茂名阪田油墨有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional cold-setting black ink mainly uses rosin-modified phenolic resin as the binder. Since the rosin-modified phenolic resin contains phenol, methanol and other chemical substances, the ink emits phenolic gas molecules during use, which is not conducive to human health. In addition, traditional cold-setting Low-grade printing paper is used for solid ink printing. These low-grade printing papers have higher requirements for ink quality, especially for ink viscosity and adaptability of ink accumulation. However, high-quality inks are also expensive due to their Relatively high, which therefore limits the use of coldset inks
In addition, when the printing quantity is large, the traditional cold-setting ink is easy to drop the plate during the printing process, which affects the quality of the printed matter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] An environmentally friendly coldset black ink which includes the following raw materials by weight:

[0064] Carbon black 25kg, rosin modified phenolic resin 15kg, petroleum resin 10kg, vegetable oil 15kg, mineral oil 7kg, alkyd resin 7kg, calcium carbonate 10kg, kaolin 10kg, anti-drying agent 1kg.

[0065] The production process of the above-mentioned environment-friendly cold-setting black ink comprises the following steps:

[0066] Step 1, wetting: add 30°C water to 25kg carbon black to wet the carbon black, then stir for 30 minutes to obtain wet carbon black;

[0067]Step 2, the preparation of varnish: 15kg rosin modified phenolic resin, 10kg petroleum resin, 7kg alkyd resin, 7kg mineral oil and 15kg vegetable oil are dropped into stirring tank and stirred evenly, make varnish;

[0068] Step 3, replacement: put the wet carbon black obtained in step 1 into the varnish water obtained in step 2 and add 10kg calcium carbonate and 10kg kaolin, then stir evenly to make t...

Embodiment 2

[0076] An environmentally friendly coldset black ink which includes the following raw materials by weight:

[0077] Carbon black 30kg, rosin modified phenolic resin 15kg, petroleum resin 11kg, vegetable oil 15kg, mineral oil 8kg, alkyd resin 5kg, calcium carbonate 7kg, kaolin 8kg, anti-drying agent 1kg.

[0078] The production process of the above-mentioned environment-friendly cold-setting black ink comprises the following steps:

[0079] Step 1, wetting: add 45°C water to 30kg carbon black to wet the carbon black, then stir for 45 minutes to obtain wet carbon black;

[0080] Step 2, the preparation of varnish: 15kg rosin modified phenolic resin, 11kg petroleum resin, 5kg alkyd resin, 8kg mineral oil and 15kg vegetable oil are put into a stirring tank and stirred evenly to obtain varnish;

[0081] Step 3, replacement: put the wet carbon black obtained in step 1 into the varnish water obtained in step 2 and add 7kg calcium carbonate and 8kg kaolin, then stir evenly to make th...

Embodiment 3

[0089] An environmentally friendly coldset black ink which includes the following raw materials by weight:

[0090] Carbon black 30kg, rosin modified phenolic resin 10kg, petroleum resin 15kg, vegetable oil 15kg, mineral oil 7kg, alkyd resin 3kg, calcium carbonate 10kg, kaolin 8kg, anti-drying agent 2kg.

[0091] The production process of the above-mentioned environment-friendly cold-setting black ink comprises the following steps:

[0092] Step 1, wetting: add 50°C water to 30kg carbon black to wet the carbon black, then stir for 45 minutes to obtain wet carbon black;

[0093] Step 2, preparation of varnish: 10kg rosin modified phenolic resin, 15kg petroleum resin, 3kg alkyd resin, 7kg mineral oil and 15kg vegetable oil are dropped into a stirring tank and stirred evenly to obtain varnish;

[0094] Step 3, replacement: put the wet carbon black obtained in step 1 into the varnish water obtained in step 2 and add 10kg calcium carbonate and 8kg kaolin, then stir evenly to make ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of cold-set black ink, in particular relates to environment-friendly cold-set black ink and a production process thereof. The environment-friendly cold-set black ink is prepared from the following components in percentage by weight: 20 percent to 35 percent of carbon black, 5 percent to 25 percent of rosin modified phenolic resin, 1 percent to 15 percent of petroleum resin, 15 percent to 45 percent of vegetable oil, 5 percent to 25 percent of mineral oil, 1 percent to 10 percent of alkyd resin, 1 percent to 25 percent of calcium carbonate, 1 percent to 25 percent of kaolin, and 1 percent to 5 percent of antidesiccant. The proportion of the petroleum resin, the calcium carbonate, and the kaolin in printing ink is improved, the production cost is reduced, due to the calcium carbonate and the kaolin, the solid-containing content of raw materials is improved, and the control of the petroleum resin to viscosity is improved, so that the ink has good ink piling adaptability. A kneader is used for dispersing the solid-containing content in the raw materials, the fineness of the solid-containing content is strictly controlled, and the adaptability of image weakening of the ink is enhanced.

Description

technical field [0001] The invention relates to the technical field of cold-setting ink, in particular to an environment-friendly cold-setting black ink and a production process thereof. Background technique [0002] Offset printing ink is currently the most widely used printing method in the printing industry. Among them, the cold-setting ink has a fast printing speed and can be dried quickly at room temperature without the need for a dryer. etc. favor. The traditional cold-setting black ink mainly uses rosin-modified phenolic resin as the binder. Since the rosin-modified phenolic resin contains phenol, methanol and other chemical substances, the ink emits phenolic gas molecules during use, which is not conducive to human health. In addition, traditional cold-setting Low-grade printing paper is used for solid ink printing. These low-grade printing papers have higher requirements for ink quality, especially for ink viscosity and adaptability of ink accumulation. However, hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/103C09D11/106C09D11/06C09D11/105C09D11/03
CPCC09D11/03C09D11/06C09D11/103C09D11/105C09D11/106
Inventor 永沼孝介吴国蓬
Owner 茂名阪田油墨有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products