Butyl rubber sealing tape used for automobile and preparing method thereof

A technology of butyl rubber and sealing tape, which is applied in the direction of adhesives, adhesive types, film/sheet adhesives, etc., and can solve problems such as poor air tightness, low temperature, and high temperature resistance

Inactive Publication Date: 2016-04-20
BAODING JINYUEMEI IND & TRADE CO LTD
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the butyl rubber sealing tape currently used in the automotive field generally has problems such as poor airtightness, high temperature resistance, low temperature resistance, and easy falling off.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Butyl rubber sealing tape used for automobile and preparing method thereof
  • Butyl rubber sealing tape used for automobile and preparing method thereof
  • Butyl rubber sealing tape used for automobile and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] Correspondingly, the present invention also provides a preparation method of butyl rubber sealing tape for automobiles, comprising the following steps: adding 15-20 parts by weight of butyl rubber into an internal mixer for mastication for 40-60 minutes, and then adding 6-10 Parts by weight of nano-scale calcium carbonate, 30-40 parts by weight of light calcium carbonate, after stirring, add 2-5 parts by weight of fumed silica, 10-20 parts by weight of low molecular weight polyisobutylene, 4-10 parts by weight of medium molecular weight polyisobutylene Isobutylene, 4-10 parts by weight of high molecular weight polyisobutylene, 6-10 parts by weight of pigments, and 8-15 parts by weight of petroleum resin are kneaded evenly, the temperature of the mill roll is controlled at 80°C, the material is discharged, and the rubber compound is obtained after spreading to room temperature; The sizing material is fed into an extrusion molding machine, extruded, cut and rolled to obtai...

Embodiment 1

[0053] A butyl rubber sealing tape for automobiles, consisting of the following parts by weight: 15 parts by weight of butyl rubber (high-grade product), 10 parts by weight of nano-scale calcium carbonate, 40 parts by weight of light calcium carbonate, gas phase method 2 parts by weight of silicon dioxide, 20 parts by weight of low molecular weight polyisobutene, 4 parts by weight of medium molecular weight polyisobutene, 10 parts by weight of high molecular weight polyisobutene, 6 parts by weight of carbon black, and 8 parts by weight of petroleum resin.

[0054] Preparation:

[0055] The main preparation process of the butyl rubber sealing tape of the present invention is as follows: the butyl rubber sealing tape is kneaded, kneaded, extruded, cut into strips, and packaged with release paper.

[0056] Specifically: first masticate butyl rubber for 45 minutes, then add nano-scale calcium carbonate and light calcium carbonate and stir evenly for 30 minutes, then add the rest o...

Embodiment 2

[0066] A butyl rubber sealing tape for automobiles, which is composed of the following parts by weight: 19 parts by weight of butyl rubber (high-grade product), 9 parts by weight of nano-scale calcium carbonate, and 36 parts by weight of light calcium carbonate. 3 parts by weight of silicon dioxide, 16 parts by weight of low-molecular-weight polyisobutene, 5 parts by weight of medium-molecular-weight polyisobutene, 8 parts by weight of high-molecular-weight polyisobutene, 7 parts by weight of ultramarine blue, and 14 parts by weight of petroleum resin.

[0067] Preparation:

[0068] The main preparation process of the butyl rubber sealing tape of the present invention is as follows: the butyl rubber sealing tape is kneaded, kneaded, extruded, cut into strips, and packaged with release paper.

[0069] Specifically: first masticate butyl rubber for 45 minutes, then add nano-scale calcium carbonate and light calcium carbonate and stir evenly for 30 minutes, then add the rest of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides butyl rubber sealing tape used for an automobile. The butyl rubber sealing tape is prepared from, by weight, 15-20 parts of butyl rubber, 6-10 parts of nanoscale calcium carbonate, 30-40 parts of light calcium carbonate, 2-5 parts of acticel, 10-20 parts of low-molecular-weight polyisobutene, 4-10 parts of middle-molecular-weight polyisobutene, 4-10 parts of high-molecular-weight polyisobutene, 6-10 parts of pigment and 8-15 parts of petroleum resin. One face of the provided butyl rubber sealing tape used for the automobile is bonded with an automobile steel plate, and the other face is bonded with a plastic moisture-proof film to have the waterproof effect. Experiment results show that performance indexes of the butyl rubber sealing tape used for the automobile reach or exceed those of existing similar products, the butyl rubber sealing tape used for the automobile has the advantages that airtightness is good, the sealing tape is resistant to high temperature and does not flow, and the bonding strength is not lowered at low temperature.

Description

technical field [0001] The invention relates to the technical field, in particular to a butyl rubber sealing tape for automobiles and a preparation method thereof. Background technique [0002] Butyl rubber has excellent air tightness and good adhesion, low temperature resistance, aging resistance and other characteristics, and is widely used in waterproof and airtight, shock-absorbing bonding and sealing, such as stationery bonding, building materials bonding and sealing Waterproof, shock-absorbing bonding and sealing of machinery and equipment, airtight bonding of material joints, etc., are a kind of bonding and sealing materials that are easy to use, widely used, safe, reliable, economical and practical. [0003] Butyl rubber sealing tape is widely used in the automotive field and construction industry because of its excellent air tightness, water tightness, good adhesion, aging resistance, low temperature resistance, water resistance, convenient construction and installa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/00C09J123/22C09J123/20C09J157/02C09J11/04
CPCC09J7/00C08K2201/011C08K2201/014C08L2201/08C08L2201/14C08L2205/025C08L2205/035C09J11/04C09J123/22C08L23/22C08L57/02C08K3/00C08K2003/265C08K3/36
Inventor 辛朝刚王田光王平格
Owner BAODING JINYUEMEI IND & TRADE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com