Organic steam corrosion-resistant gas separation film and preparation method thereof

A gas separation membrane, organic vapor technology, applied in separation methods, semi-permeable membrane separation, dispersed particle separation, etc., can solve the problems of damage, the base membrane is easily corroded, the membrane performance is degraded, etc. Separation selection performance, the effect of improving the bonding strength

Active Publication Date: 2016-05-04
JIANGSU JIUMO HIGH TECH CO LTD
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when separating certain strong polar organic solvent vapors in industry, the PVDF base membrane is easily corroded, and the pore structure of the base membrane support is destroyed, resulting in a decrease in membrane performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic steam corrosion-resistant gas separation film and preparation method thereof
  • Organic steam corrosion-resistant gas separation film and preparation method thereof
  • Organic steam corrosion-resistant gas separation film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Dissolve 3g of PEG400 and 1g of macromolecular PEG20000 mixed additives in N,N-dimethylformamide solvent at 40°C. After completely dissolving, add 15g of PVDF-HFP powder to the solution to prepare a casting solution with a total mass of 100g. Dissolve The temperature is maintained at 70°C. After obtaining a uniform and transparent casting solution, let it stand for 16 hours for defoaming, and evenly scrape it on the non-woven fabric with a scraper. The thickness of the scraper is 150 μm. , take it out immediately after staying for 2s, then immerse in deionized water for 30s, take out the membrane, and rinse the membrane surface with clean water for 30min repeatedly to obtain a PVDF-HFP porous base membrane. Dissolve the ternary copolymerization block silicone oil (if not specified, the ternary copolymerization block silicone oil is provided by Shandong Dayi Chemical Co., Ltd. in all examples) in the solvent toluene, mix well and add the crosslinking agent phenyl trimetho...

Embodiment 2～3

[0032] Examples 2-3 investigated the influence of coating film conditions on film performance and solvent resistance, and the rest of the conditions are the same as in Example 1. The conclusions are shown in Tables 2 to 4: the membrane with PVDF-HFP as the base membrane and ternary copolymerized silicone oil as the composite layer material maintains stable separation performance and has good solvent resistance during continuous operation.

[0033] Table 1 Embodiment 2~3 film-making conditions

[0034]

[0035]

Embodiment 4

[0037]Example 4 investigates the effect of using PVDF material as the base film on the performance and solvent resistance of the composite film during long-term operation, and the rest of the conditions are the same as in Example 1. The conclusions are shown in Tables 2 to 4: During the continuous operation of the membrane with PVDF as the base membrane and ternary copolymerized silicone oil as the composite layer material, the separation factor of the membrane and the permeation rate of n-hexane are both decreasing, which shows that PVDF is in the process of long-term operation. The substrate is easily eroded by n-hexane solvent, and the pores shrink and deform under the pressure of the membrane surface, resulting in a decrease in separation performance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an organic steam corrosion-resistant gas separation film and a preparation method thereof. A polyvinylidene fluoride-hexafluoropropene (PVDF-HFP) copolymer is used as a base film material, a micromolecule PEG-macromolecule PEG mixed additive is used, an alcohol-water dual coagulation bath is used, a film is formed on a polyester non-woven fabric through blade coating and a PVDF-HFP porous base film is prepared through a delayed phase inversion method. Ternary copolymer block silicone oil is dissolved in the organic solvent, the solution undergoes a crosslinking reaction under action of a catalyst and a crosslinking agent until a certain crosslinking degree, the surface of the PVDF-HFP porous base film is coated with the product by a blade and the coating is cured and molded at a high temperature so that a compounded layer is formed. The PVDF-HFP porous base film and the compounded layer have strong organic steam corrosion resistance and are bonded tightly. The organic steam corrosion-resistant gas separation film has excellent comprehensive properties and a very great industrial application prospect.

Description

technical field [0001] The invention relates to a gas separation membrane resistant to organic vapor corrosion and a preparation method thereof, belonging to the technical field of gas membrane separation. Background technique [0002] The tail gas emitted by petrochemical, pharmaceutical and other industries contains a large amount of organic vapors, such as ethylene, propylene, vinyl chloride, gasoline and other hydrocarbons. If it is discharged directly, from the perspective of economic interests, it is a serious waste of resources. From the perspective of safety, most of the organic vapors are flammable and explosive, and mixed with air to form explosive gas mixtures, causing great safety hazards to enterprises; In terms of environmental protection and social benefits, the emission of organic vapors reduces the quality of the atmospheric environment and poses serious hazards to human health. [0003] At present, there are two types of treatment methods for this type of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D71/34B01D69/12B01D67/00B01D53/22C08J5/18
CPCB01D53/22B01D69/125B01D71/34C08J5/18C08J2327/16C08J2383/04
Inventor 丁晓斌孙雪飞南江普王成
Owner JIANGSU JIUMO HIGH TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap