A technology of heat-resistant paint and high hardness, applied in the field of paint, can solve the problems of low paint hardness, oil resistance, antibacterial and heat resistance, etc., achieve good oil resistance and antibacterial performance, eliminate local unevenness, improve hardness and oil resistance, antibacterial and heat resistance The effect of thermal performance

Active Publication Date: 2016-06-29
宁波长发涂料有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The paint in the prior art has low hardness, and its oil-resistant, anti-bacterial, and heat-resistant properties cannot meet the needs in actual production. Therefore, it is necessary to develop a paint with high hardness, oil-resistant, anti-bacterial, and heat-resistant properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of high-hardness oil-resistant antibacterial heat-resistant paint proposed by the present invention, its raw material comprises by weight: 100 parts of fluorinated modified nitrile rubber, 60 parts of nano inorganic antibacterial powder, 10 parts of styrene-acrylic emulsion, 5 parts of alkyd resin , 6 parts of ethyl acetate, 3 parts of epoxy resin, 4 parts of polyvinyl chloride resin, 6 parts of aluminum hydroxide, 3 parts of bentonite, 3 parts of barite powder, 2.5 parts of nitrocellulose, 2 parts of zinc oxide, 3 parts of mica powder , 4 parts of zeolite powder, 4 parts of chlorinated paraffin, 3.5 parts of calcium ferrite, 4 parts of hexamethylcellulose, 6 parts of citric acid, 3 parts of propanol, 4 parts of xylene, and 2.5 parts of curing agent.

[0016] Nano inorganic antibacterial powder is prepared according to the following process: mix 5 parts of urea, 3 parts of polyvinylpyrrolidone and 10 parts of deionized water in parts by weight, then add 5 parts of...

Embodiment 2

[0018] A kind of high-hardness oil-resistant antibacterial heat-resistant paint proposed by the present invention, its raw material comprises by weight: 80 parts of fluorinated modified nitrile rubber, 80 parts of nano inorganic antibacterial powder, 5 parts of styrene-acrylic emulsion, 8 parts of alkyd resin , 3 parts of ethyl acetate, 5 parts of epoxy resin, 2 parts of polyvinyl chloride resin, 9 parts of aluminum hydroxide, 1 part of bentonite, 4 parts of barite powder, 1 part of nitrocellulose, 3 parts of zinc oxide, 1 part of mica powder , 6 parts of zeolite powder, 1 part of chlorinated paraffin, 5 parts of calcium ferrite, 3 parts of hexamethylcellulose, 8 parts of citric acid, 1 part of propanol, 6 parts of xylene, and 1 part of curing agent.

[0019] The nano-inorganic antibacterial powder is prepared according to the following process: mix 2 parts of urea, 5 parts of polyvinylpyrrolidone and 5 parts of deionized water in parts by weight, then add 8 parts of sodium chl...

Embodiment 3

[0021] A kind of high-hardness oil-resistant antibacterial heat-resistant paint proposed by the present invention, its raw material comprises by weight: 120 parts of fluorinated modified nitrile rubber, 40 parts of nano inorganic antibacterial powder, 15 parts of styrene-acrylic emulsion, 2 parts of alkyd resin , 9 parts of ethyl acetate, 1 part of epoxy resin, 6 parts of polyvinyl chloride resin, 3 parts of aluminum hydroxide, 5 parts of bentonite, 2 parts of barite powder, 4 parts of nitrocellulose, 1 part of zinc oxide, 5 parts of mica powder , 2 parts of zeolite powder, 7 parts of chlorinated paraffin, 2 parts of calcium ferrite, 5 parts of hexamethylcellulose, 4 parts of citric acid, 5 parts of propanol, 2 parts of xylene, and 4 parts of curing agent.

[0022] The nano-inorganic antibacterial powder is prepared according to the following process: mix 8 parts of urea, 1 part of polyvinylpyrrolidone and 15 parts of deionized water in parts by weight, then add 2 parts of sodi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high-hardness, oil-resistant, antibacterial and heat-resisting paint. Raw materials of the paint comprise fluorination modified nitrile rubber, nano inorganic antibacterial powder, a styrene-acrylic emulsion, alkyd resin, ethyl acetate, epoxy resin, polyvinyl chloride resin, aluminum hydroxide, bentonite, barite powder, nitrocotton, zinc oxide, mica powder, zeolite powder, chlorinated paraffin, calcium ferrite, hexamethyl cellulose, citric acid, propanol, xylene and a curing agent. The paint has high hardness, good oil resistance and antibacterial property and excellent heat resistance.

Description

technical field [0001] The invention relates to the field of paints, in particular to a high-hardness oil-resistant, antibacterial, and heat-resistant paint. Background technique [0002] Paint is a chemical mixture coating that can firmly cover the surface of objects for protection, decoration, marking and other special purposes. It belongs to organic chemical polymer materials, and the formed coating film belongs to the type of polymer compounds. In real life, the surface of many items needs to be treated with paint, which not only improves the beauty of the item, but also effectively prolongs the life of the item. [0003] The paints in the prior art have low hardness and oil-resistant, anti-bacterial, heat-resistant properties cannot meet the needs in actual production, so it is necessary to develop a paint with high hardness, oil-resistant, anti-bacterial, heat-resistant properties. Contents of the invention [0004] In order to solve the technical problems in the b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D115/02C09D125/14C09D167/08C09D163/00C09D127/06C09D101/18C09D191/06C09D101/28C09D5/14C09D7/12
CPCC08K2201/011C08L2201/08C08L2205/02C08L2205/035C09D5/14C09D5/18C09D7/61C09D7/62C09D7/63C09D115/02C08L25/14C08L67/08C08L63/00C08L27/06C08L1/18C08L91/06C08L1/28C08K13/06C08K9/10C08K3/16C08K2003/2227C08K3/346C08K2003/3045C08K2003/2296C08K3/34C08K3/24C08K5/092
Inventor 许盟凯
Owner 宁波长发涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap