Regeneration technology for asphalt concrete pavement
A technology of asphalt concrete and craftsmanship, which is applied to the coagulation pavement, roads, roads and other directions of on-site paving, which can solve the problems of high regeneration cost, complicated restoration and regeneration process, and the inability of milling materials to meet the requirements of road paving, etc. problem, to achieve the effect of good recycling
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0050] Preparation of concrete admixtures
[0051] The chemical structural formula of monomer (I) is:
[0052]
[0053] where R 1 is methyl, R 2 is an ethyl group, n is 5, and this monomer can be prepared by esterifying polyethylene glycol and methacrylic acid according to a conventional esterification method, and then reacting the esterification product with ethoxychloride according to a conventional elimination reaction, or it can be Commercially purchased directly from Sigma-Aldrich;
[0054] The chemical structural formula of monomer (II) is:
[0055] This monomer is also commercially available from Sigma-Aldrich;
[0056] Adopt emulsion polymerization method, add 80g monomer (I) and 12g monomer (II) and 200mL deionized water in the 500mL round-bottomed flask that has mechanical stirring device, nitrogen is led under stirring, then add 0.1g ammonium persulfate as The initiator is heated up to the polymerization temperature, the polymerization temperature is 80°C,...
Embodiment 2
[0058] Use the W2000 milling machine to mill the asphalt concrete pavement of the high-grade highway in Fangzhuo section. The thickness of the first layer of milling is 5cm, and the thickness of the second layer of milling is 10cm; the first layer of milling material is screened , collect the granules of 10-31.5mm, crush the granules larger than 31.5mm and sieve again to obtain the granules of 10-31.5mm, which are recorded as granules A; mix the obtained granules of 10-31.5mm with emulsified asphalt, cement and The electric slag is mixed and regenerated at a weight ratio of 90:1:2:5 to obtain a regenerated material, which is recorded as the first regenerated material, and the particles smaller than 10mm are collected for later use, and the particles are recorded as particle B; wherein, the electric slag The specific surface area is 1800m 2 / kg, the content of free calcium oxide is 3% by weight; the second layer of milling material is crushed, and the particles of 10-20mm are c...
PUM
Property | Measurement | Unit |
---|---|---|
specific surface area | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap