Wear-resistant oxide-based metal ceramic knife and manufacturing method thereof

A technology of ceramic cutting tools and base metals, which is applied to other manufacturing equipment/tools, turbines, engine components, etc., can solve the problems of low market share and achieve wide application, good wear resistance, compactness and improved bending strength Effect

Inactive Publication Date: 2016-08-24
陈林美
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Wear-resistant oxide-based cermet knives are rarely seen in the domestic market, and a small amount of sales and good reputation are basically imported products, and the market share of domestic products is even less

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A wear-resistant oxide-based cermet cutter, made of the following raw materials in parts by weight: 45 parts of magnesium oxide, 40 parts of zirconia, 3 parts of magnesium powder, 40 parts of copper powder, 10 parts of asbestos powder, black bismuth gold ore 3 parts of barite powder, 4 parts of barite powder, 6 parts of germanium dioxide, 2 parts of ditin trioxide, 6 parts of cadmium selenide, and 11 parts of paraffin wax.

[0015] The steps of the preparation method are as follows: first put all raw materials into a high-speed mixer, mix and stir them, then place the uniformly mixed mixture in a mold and press it into a preform, the pressing pressure is 40-50MPa, and then the preform High temperature sintering, the sintering temperature is 900-1200°C, the sintering time is 3-6h, and the temperature can be lowered to room temperature.

Embodiment 2

[0017] A wear-resistant oxide-based cermet cutter, made of the following raw materials in parts by weight: 55 parts of magnesium oxide, 50 parts of zirconia, 10 parts of magnesium powder, 50 parts of copper powder, 14 parts of asbestos powder, black bismuth gold ore 8 parts of barite powder, 9 parts of barite powder, 8 parts of germanium dioxide, 5 parts of ditin trioxide, 7 parts of cadmium selenide, and 15 parts of paraffin wax.

[0018] The steps of the preparation method are as follows: first put all raw materials into a high-speed mixer, mix and stir them, then place the uniformly mixed mixture in a mold and press it into a preform, the pressing pressure is 40-50MPa, and then the preform High temperature sintering, the sintering temperature is 900-1200°C, the sintering time is 3-6h, and the temperature can be lowered to room temperature.

Embodiment 3

[0020] A wear-resistant oxide-based cermet cutter, made of the following raw materials in parts by weight: 50 parts of magnesium oxide, 45 parts of zirconium dioxide, 6 parts of magnesium powder, 45 parts of copper powder, 12 parts of asbestos powder, black bismuth gold ore 6 parts of powder, 7 parts of barite powder, 7 parts of germanium dioxide, 3 parts of ditin trioxide, 6 parts of cadmium selenide, and 13 parts of paraffin wax.

[0021] The steps of the preparation method are as follows: first put all raw materials into a high-speed mixer, mix and stir them, then place the uniformly mixed mixture in a mold and press it into a preform, the pressing pressure is 40-50MPa, and then the preform High temperature sintering, the sintering temperature is 900-1200°C, the sintering time is 3-6h, and the temperature can be lowered to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant oxide-based metal ceramic knife and a manufacturing method thereof. The wear-resistant oxide-based metal ceramic knife is manufactured by, by weight, 45-55 parts of magnesium oxide, 40-50 parts of zirconium dioxide, 3-10 parts of magnesium powder, 40-50 parts of copper powder, 10-14 parts of asbestos powder, 3-8 parts of maldonite powder, 4-9 parts of barite powder, 6-8 parts of germanium dioxide, 2-5 parts of tin trioxide, 6-7 parts of cadmium selenide and 11-15 parts of paraffin. Compared with conventional metal ceramic knives, the wear-resistant oxide-based metal ceramic knife manufactured by the method has higher wear resistance and heat resistance and excellent cutting performance; through optimization of components and content, compactness and bending resistance of metal ceramic tissue are improved remarkably, and the wear-resistant oxide-based metal ceramic knife can be widely used for high-speed cutting of low-medium-carbon steel and low-alloy steel.

Description

technical field [0001] The invention specifically relates to a wear-resistant oxide-based cermet cutter and a preparation method thereof. Background technique [0002] Cermet English word cermet or ceramet is composed of ceramic (ceramic) and metal (metal). Cermet refers to the composite material of metal and ceramic prepared by powder metallurgy method. Cermet has the advantages of both metal and ceramic. It has low density, high hardness, wear resistance and good thermal conductivity. Brittle. Cermet not only has the toughness, high thermal conductivity and good thermal stability of metal, but also has the characteristics of high temperature resistance, corrosion resistance and wear resistance of ceramics. Cermets have broad application prospects in aerospace, national defense, precision manufacturing and other fields. Oxide-based cermets are based on alumina, zirconia, magnesia, beryllium oxide, etc., compounded with metal tungsten, chromium or cobalt, and have the cha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C29/12C22C1/05B22F3/16B22F5/00
CPCC22C29/12B22F3/16B22F5/00B22F2005/001C22C1/051C22C29/005
Inventor 陈林美
Owner 陈林美