Molding sand for high-density models and preparation method of molding sand

A high-density, molding sand technology, applied in the direction of casting molding equipment, molds, cores, etc., can solve the problems of poor comprehensive performance and affect the surface quality of castings, achieve high wet compressive strength and hot tensile strength, and ensure comprehensive performance and quality stability, the effect of improving surface quality

Inactive Publication Date: 2016-10-05
安徽创奇乐智能游乐设备有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the continuous development of casting technology, the performance requirements of molding sand are getting higher and higher. At present, there are shortcomings of poor comprehensive performance in the market for high-density molding, which seriously affects the surface quality of castings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A high-density molding sand made from the following raw materials (kg): cement slag 34, yellow loam 72, xonotlite 28, columnar zeolite 20, quartz sand 49, olivine 22, activated sludge dry powder 12 , coke powder 7, yellow phosphorus slag 12, colloidal graphite powder 18, molybdenum disilicide 7, calcium lignosulfonate 9, polyethylene glycol 10, improver 490;

[0014] The preparation method of the modifier is as follows: a. Take the following raw materials by weight (kg): polyvinylpyrrolidone 15, polyvinyl alcohol 11, sodium tripolyphosphate 5, cornstarch 16, guar gum 13, acrylic acid 32, acrylic acid Amide 28, soybean oil 7, Span 801.5, ammonium persulfate 0.15, sodium bisulfite 0.08; b. Mix cornstarch and guar gum evenly, add water equivalent to 3 times the amount of the mixture, and heat in a water bath to 85°C. Stir for 25 minutes, cool down to 50°C, add soybean oil and Span 80, stir for 10 minutes, and set aside; c. Mix polyvinylpyrrolidone, polyvinyl alcohol, and s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wet compressive strengthaaaaaaaaaa
strengthaaaaaaaaaa
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention discloses molding sand for high-density models and a preparation method of the molding sand. The molding sand is prepared from raw materials in parts by weight as follows: 27-39 parts of cement slurry, 64-76 parts of yellow loam, 22-34 parts of xonotlite, 15-25 parts of epistilbite, 41-53 parts of quartz sand, 16-24 parts of olivine, 8-16 parts of activated sludge dry powder, 5-10 parts of coke powder, 10-15 parts of yellow phosphorus ore, 14-22 parts of colloidal graphite powder, 5-10 parts of molybdenum disilicide, 7-11 parts of calcium lignosulphonate, 8-12 parts of polyethylene glycol and 450-550 parts of a modifier. The molding sand has the relatively high wet compressing strength and thermal tensile strength and further had the excellent gas permeability, liquidity and thermal resistance, the preparation technology of the molding sand is simple, the manufacturing cost is low, and the molding sand is suitable for large-scale popularization and application to the high-density models.

Description

technical field [0001] The invention relates to high-density molding sand and a preparation method thereof, belonging to the technical field of molding sand. Background technique [0002] Sand casting is the most common casting method, and molding sand is the most important molding material in the current molding process. Molding sand is generally made by mixing molding materials such as raw sand for casting, molding sand binder and auxiliary additives in a certain proportion. Castings produced with sand molds account for more than 80% of the total casting production. The quality of molding sand directly affects the appearance quality of castings and casting defects such as sand holes, pores, and sand inclusions. With the continuous development of casting technology, the requirements for the performance of molding sand are getting higher and higher. At present, there is a shortcoming of poor comprehensive performance for high-density molding in the market, which seriously ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C1/00B22C1/02
CPCB22C1/00B22C1/02
Inventor 张庆
Owner 安徽创奇乐智能游乐设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products