Unglazed high-density bright crystal ceramic and preparation method thereof

A high-density, crystal-clear technology, applied in the field of ceramic manufacturing, can solve problems such as affecting the beauty of ceramic art and reducing product value, and achieve the effects of enhancing beauty and collection value, saving production processes, and positive social and economic benefits.

Active Publication Date: 2016-10-12
德化县中晟工艺有限责任公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Even wares with the same body glaze composition, because of their different positions in the kiln, sometimes have different glaze colors after firing, which is the so-called phenomenon of "different wares in the same kiln". Moreover, there are bubbles in glazed ceramics, and the bubbles are the result of glaze firing. A relatively common phenomenon in ceramics. Over time, glaze color bubbles tend to become dead bubbles, which affects the aesthetics of ceramic art itself and reduces product value.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Unglazed high-density bright crystal ceramic and preparation method thereof
  • Unglazed high-density bright crystal ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0024] The raw materials of the unglazed high-density crystal porcelain blank are composed of 38 parts by weight of kaolin, 23 parts of high silica, 17 parts of potassium feldspar, 6 parts of albite feldspar, 12 parts of quartz, and 4 parts of Dehua local china clay;

[0025] The chemical composition of kaolin is: aluminum oxide 35.96%, silicon dioxide 48.15%, iron oxide 0.02%, titanium oxide 0.01%, calcium oxide 0.45%, magnesium oxide 0.57%, potassium oxide 2.17%, sodium oxide 0.2%, balance 12.47 %;

[0026] The chemical composition of potassium feldspar is: 10.18% alumina, 80.45% silica, 0.03% iron oxide, 0.03% titanium oxide, 0.21% calcium oxide, 0.05% magnesium oxide, 8.29% potassium oxide, 0.21% sodium oxide, and Amount 0.55%;

[0027] The chemical composition of albite is: 19.47% alumina, 69.28% silica, 0.09% iron oxide, 0.05% titanium oxide, 0.7% calcium oxide, 0.52% magnesium oxide, 0.5% potassium oxide, 8.47% sodium oxide, and Amount 0.92%.

specific Embodiment 2

[0028] The raw materials of the unglazed high-density crystal porcelain blank are composed of 42 parts by weight of kaolin, 24 parts of high silica, 15 parts of potassium feldspar, 7 parts of albite feldspar, 11 parts of quartz, and 1 part of Dehua local china clay;

[0029] The kaolin, potassium feldspar, and albite are selected from the same raw materials as those in Embodiment 1.

specific Embodiment 3

[0030] The raw materials of glazed high-density crystal porcelain blank are composed of 40 parts by weight of kaolin, 28 parts of high silica, 12 parts of potassium feldspar, 5 parts of albite feldspar, 13 parts of quartz, and 2 parts of Dehua local china clay;

[0031] The kaolin, potassium feldspar, and albite are selected from the same raw materials as those in Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of ceramic production and particularly relates to unglazed high-density bright crystal ceramic and a preparation method thereof. In the unglazed high-density bright crystal ceramic, the blank is prepared from kaolin, high-silicon soil, potassium feldspar, albite, quartz and Dehua local china clay. By improving the blank and firing technology, the prepared bright crystal ceramic has high density and good thermal shock resistance and is safe to use; without glazing, the water absorption is lower than or equal to 0.2, the lead release is lower than 0.1, the cadmium release is lower than 0.1, the whiteness is high, and bubbles are avoided; in the production of the bright crystal ceramic, complicated production processes are saved, the production cost is greatly reduced since the glazing is not needed, the waste of natural resources is effectively avoided, and the product yield is high; the bright crystal ceramic is natural and moist and has the ceramic appeal incomparable for the glazed ceramic; along with the time change, the ceramic product is naturally tarnished, and the beauty and collection value of the ceramic art work are enhanced; and the bright crystal ceramic is particularly suitable for producing high-grade tea set, Buddha and sculptures and brings positive social and economic benefits.

Description

technical field [0001] The invention relates to the technical field of ceramic manufacturing, in particular to an unglazed high-density crystal porcelain and a preparation method thereof. Background technique [0002] In ceramic production, because the glaze is sensitive to the temperature and atmosphere in the kiln, the fired products will have certain differences in glaze color and enamel quality. Even wares with the same body glaze composition, because of their different positions in the kiln, sometimes show different glaze colors after firing, which is the so-called phenomenon of "different wares in the same kiln". Moreover, there are bubbles in glazed ceramics, and the bubbles are the result of glaze firing. It is a relatively common phenomenon in ceramics. Over time, glaze color bubbles tend to become dead bubbles, which affects the beauty of ceramic art itself and reduces the value of products. Contents of the invention [0003] In order to solve the deficiencies o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C04B33/24
CPCC04B33/13C04B33/24
Inventor 林福椿苏小云
Owner 德化县中晟工艺有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com