Epoxy-resin-based di-ester strong-viscidity storage battery sealant and manufacturing method

A technology of epoxy resin and battery, which is applied in the direction of epoxy resin glue, adhesive, adhesive type, etc., can solve the problems of damaging the battery shell and high bonding strength, and achieve the effect of increasing curing speed and bonding efficiency

Inactive Publication Date: 2016-10-12
哈尔滨永淇化工有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003]With the increasing market demand for batteries year by year, more and more attention has been paid to the disposal of used batteries and the maintenance of batteries, and the key to battery maintenance is to open the sealing cover Can not damage the battery shell, if some existing sealants have high bonding strength, the battery shell will be damaged because the sealant is difficult to peel off when the sealing cover is opened, and the high bonding strength that is easy to peel off is relatively low, how to ensure Good bonding strength and no damage to the battery casing when the sealing cover is opened is a difficult problem to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy-resin-based di-ester strong-viscidity storage battery sealant and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of epoxy resin-based double fat strong viscous battery sealant, it is characterized in that: comprise A component and B component; Described A component is made of ketimine, PC-polycarbonate, methyl ethyl ketone peroxide, chloroprene Rubber composition; B component is composed of epoxy resin, ethylene glycol diester methacrylate, acrylate rubber, tetramethylthiourea, dibutyl phthalate, defoamer, paraffin; wherein the A group Parts, including: 15-25 parts of ketimine, 15-25 parts of PC-polycarbonate, 2-6 parts of methyl ethyl ketone peroxide, 10-25 parts of neoprene rubber; the B component , including: 60-80 parts of epoxy resin, 10-20 parts of ethylene glycol diester methacrylate, 5-15 parts of acrylate rubber, 3-15 parts of tetramethylthiourea, 10-25 parts of Dibutyl phthalate, 10-15 parts of defoamer, 0.1-5 parts of paraffin.

[0018] The A component includes: 20 parts of ketimine, 20 parts of PC-polycarbonate, 4 parts of methyl ethyl ketone peroxide, and 15 p...

Embodiment 2

[0026] A kind of epoxy resin-based double fat strong viscous battery sealant, it is characterized in that: comprise A component and B component; Described A component is made of ketimine, PC-polycarbonate, methyl ethyl ketone peroxide, chloroprene Rubber composition; B component is composed of epoxy resin, ethylene glycol diester methacrylate, acrylate rubber, tetramethylthiourea, dibutyl phthalate, defoamer, paraffin; wherein the A group Parts, including: 15-25 parts of ketimine, 15-25 parts of PC-polycarbonate, 2-6 parts of methyl ethyl ketone peroxide, 10-25 parts of neoprene rubber; the B component , including: 60-80 parts of epoxy resin, 10-20 parts of ethylene glycol diester methacrylate, 5-15 parts of acrylate rubber, 3-15 parts of tetramethylthiourea, 10-25 parts of Dibutyl phthalate, 10-15 parts of defoamer, 0.1-5 parts of paraffin.

[0027] The A component is mixed at a temperature of 36-66°C and an air pressure of 10pa, and the component B is mixed at a temperature...

Embodiment 3

[0032] The preferred version of the present invention is: The A component includes: 20 parts of ketimine, 20 parts of PC-polycarbonate, 4 parts of methyl ethyl ketone peroxide, and 15 parts of neoprene rubber; the B Components include: 70 parts epoxy resin, 15 parts ethylene glycol diester methacrylate, 10 parts acrylate rubber, 8 parts tetramethylthiourea, 15 parts dibutyl phthalate , 12 parts of defoamer, 3 parts of paraffin.

[0033]Component A is at a temperature of 40°C, and component B is at a temperature of 45°C and an air pressure of 10pa. Mix the raw materials in component A and component B according to the ratio, and then stand still for distribution. When using, directly mix component A Component B and component B are mixed evenly according to the weight ratio, and then the potting operation can be carried out.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an epoxy-resin-based di-ester strong-viscidity storage battery sealant. The sealant is prepared from a component A and a component B, wherein the component A is prepared from ketimine, PC-polycarbonate, methyl ethyl ketone peroxide and chloroprene rubber; the component B is prepared from epoxy resin, hydroxypropyl methacrylate, acrylic rubber, tetramethylthiourea, dibutyl phthalate, a defoaming agent and paraffin. Heat generated mutually when the sealant is in use is utilized, the curing speed and the bonding efficiency of an assembly adhesive are improved, the heat resistance, the acid resistance and the adhesive property of the sealant are better than those of other kinds of storage battery sealants, during manufacturing and sealant preparation, the proportion does not need to be strictly controlled, heating and curing are not needed, the storage battery production process is simplified, and the production cost of storage batteries is lowered.

Description

technical field [0001] The invention relates to the technical field of chemical engineering, in particular to an epoxy resin-based double-fat strong-adhesive battery sealant and a production method that can seal batteries. Background technique [0002] With the rapid development of China's battery industry, the performance of the battery sealant, which is directly related to the quality of the battery, has attracted more and more attention from experts in the industry and various industries at home and abroad. The main components of sealing adhesives widely used in the battery industry are Amine or modified amine-cured epoxy system or polyurethane system adhesives, epoxy system adhesives require a long curing time at room temperature, sometimes even heat curing, and are relatively brittle, so this system is used as lead The sealing materials for poles and tank covers of acid batteries are still unsatisfactory; polyurethane adhesives can meet the requirements of lead-acid bat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C09J169/00C09J111/00C09J11/06C09J11/08
CPCC09J163/00C08L2201/08C08L2205/035C09J11/06C09J11/08
Inventor 刘振亭
Owner 哈尔滨永淇化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap