A kind of color gold glaze ceramic tile and preparation method thereof

A ceramic tile and colored gold technology, applied in the field of colored gold glazed tiles and its preparation, can solve the problems of unstable bonding of metal ceramic tiles, wear and tear of metal layers, etc., achieve strong colorful metal effects, reduce production costs and energy consumption, The effect of high compressive strength

Inactive Publication Date: 2019-08-30
虞雨先
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method adopts the method of covering the metal layer or bonding the metal layer to produce the effect of colored gold glaze, but the cermet tiles prepared by this method are not firmly bonded, and the metal layer is easily worn and peeled off.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A colored gold glazed ceramic tile made of the following raw materials by weight: 30 parts of zinc oxide, 20 parts of aluminum oxide, 10 parts of silicon oxide, 20 parts of potassium feldspar, 10 parts of clay, 0.5 parts of iron oxide, and 0.5 parts of titanium oxide parts, 5 parts of mercury sulfide.

[0019] The preparation method of the above-mentioned color gold glazed ceramic tile is carried out according to the following steps:

[0020] (1) According to parts by weight, 30 parts of zinc oxide, 20 parts of aluminum oxide, 10 parts of silicon oxide, 20 parts of potassium feldspar, 10 parts of clay, 0.5 part of iron oxide, 0.5 part of titanium oxide, 5 parts of mercury sulfide, add water 100 parts, input to the ball mill for grinding and pulping;

[0021] (2) Use an automatic hydraulic brick press to press the slurry into a green body; the pressure applied by the automatic hydraulic brick press is 45MPa;

[0022] (3) The green body is dried in a drying kiln at a dr...

Embodiment 2

[0027] A colored gold glazed ceramic tile, made of the following raw materials by weight: 10 parts of silicon oxide, 20 parts of aluminum oxide, 20 parts of calcium oxide, 10 parts of potassium feldspar, 5 parts of white clay, 0.1 part of iron oxide, and 0.1 part of titanium oxide 2 parts, chlorite powder 2 parts.

[0028] The preparation method of the above-mentioned color gold glazed ceramic tile is carried out according to the following steps:

[0029] (1) According to parts by weight, 10 parts of silicon oxide, 20 parts of aluminum oxide, 20 parts of calcium oxide, 10 parts of potassium feldspar, 5 parts of clay, 0.1 part of iron oxide, 0.1 part of titanium oxide, 2 parts of chlorite powder, add 80 parts of water, input to the ball mill for grinding and pulping;

[0030] (2) Use an automatic hydraulic brick press to press the slurry into a green body; the pressure applied by the automatic hydraulic brick press is 42MPa;

[0031] (3) Dry the green body through a drying ki...

Embodiment 3

[0036] A colored gold-glazed ceramic tile made of the following raw materials by weight: 10 parts of zinc oxide, 20 parts of silicon oxide, 10 parts of aluminum oxide, 20 parts of calcium oxide, 10 parts of copper oxide, 30 parts of potassium feldspar, and 15 parts of clay 1 part, 1 part of iron oxide, 1 part of titanium oxide, 10 parts of bamboo leaf stone powder.

[0037] The preparation method of the above-mentioned color gold glazed ceramic tile is carried out according to the following steps:

[0038] (1) According to parts by weight, 10 parts of zinc oxide, 20 parts of silicon oxide, 10 parts of aluminum oxide, 20 parts of calcium oxide, 10 parts of copper oxide, 30 parts of potassium feldspar, 15 parts of clay, 1 part of iron oxide, titanium oxide 1 part, 10 parts of bamboo leaf stone powder, add 150 parts of water, input to ball mill for grinding and pulping;

[0039] (2) Use an automatic hydraulic brick press to press the slurry into a green body; the pressure applie...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a colorful-metal glazed ceramic tile and a production method thereof and belongs to the technical field of production of building materials. The colorful-metal glazed ceramic tile is produced from the following materials, by weight: 50-80 parts of frit, 10-30 parts of potassium feldspar, 5-15 parts of white clay, 0.1-1 part of ferric oxide, 0.1-1 part of titanium oxide, and 2-10 parts of an additive. The mosaic gold glazed ceramic tile has great colorful metal effect and is fired at a time, production steps are simple, production cost and energy consumption are reduced, the produced ceramic tile has lasting colorful metal effect and never fades, the tile never changes color on rainy days when in contact with acids and bases, and the tile never cracks at high temperature, is high in tensile strength and compressive strength and is suitable for large-scale industrial production.

Description

technical field [0001] The invention belongs to the technical field of building material preparation, and in particular relates to a colored gold-glazed ceramic tile and a preparation method thereof. Background technique [0002] With the improvement of people's aesthetic concepts, the requirements for ceramic tiles are not only anti-fall, rainproof, and fireproof, but also require a certain aesthetic feeling. Color gold glazed tiles have a beautiful appearance and are loved by people. Conventional production processes require The effect of colored gold glaze can only be achieved after one, two, and three firing processes, which requires high energy consumption, high cost, and the production process is quite complicated. [0003] Patent 201220233208.4 discloses a metal-ceramic brick. The surface of the ceramic layer of the metal-ceramic brick is partially or completely covered with a metal layer. The metal layer is formed by sintering nanoscale or ultrafine metal particles, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/453C04B35/622C04B35/10C04B35/01C04B35/19C04B41/86C04B35/63
Inventor 虞雨先
Owner 虞雨先