BPDA type BDATHQ branched polyamide resin film and preparation method thereof

A technology of polyimide resin and polyamic acid resin, which is applied in the field of polyimide film and its preparation, can solve the problem of difficult preparation of high molecular weight polyimide resin, unpublished literature or patent reports, Problems such as the decline in comprehensive performance of film products, to achieve excellent dimensional stability, simple operation, and significant comprehensive performance superiority

Inactive Publication Date: 2017-01-04
DONGHUA UNIV +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Its disadvantages are: (1) the raw material 2,2-bis(3,4-dicarboxyphenyl) hexafluoropropane dianhydride monomer is extremely expensive, resulting in very high cost of film products, which seriously hinders its further application; ( 2) Due to the low reactivity of 2,2-bis(3,4-dicarboxyphenyl) hexafluoropropane dianhydride monomer and aromatic dibasic primary amine, it is difficult to prepare high molecular weight polyimide resin, Therefore, the overall performance of its film products is greatly reduced, especially its mechanical properties.
At present, there are no published literature or patent reports about the BPDA type BDATHQ branched polyimide resin film and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • BPDA type BDATHQ branched polyamide resin film and preparation method thereof
  • BPDA type BDATHQ branched polyamide resin film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Add 180.0 g (0.9 mol) of 4,4'-diaminodiphenyl ether (DADPE), 10.8 (0.1 mol) of p-phenylenediamine (PPDA) and 1470 g of N,N-dimethylacetamide (DMAc) to the polymerization In the bottle, stir at room temperature. After completely dissolving, cool in an ice-water bath to below 5°C, add 297.1 grams (1.01 moles) of 3,3',4,4'-biphenyltetracarboxylic dianhydride (BPDA), stir, and 5 After reacting at °C for 1 hour, 1957.9 g of a homogeneous, transparent and viscous BPDA-type polyamic acid resin solution was obtained, which was designated as BPDA-PAA-1. Using Brookfield CAP2000+ vertebral plate viscometer, its viscosity at 50°C is measured as 630mPa.s. .

Embodiment 2

[0037] 262.8 grams (0.9 moles) of 1,4-bis(4-aminophenoxy)benzene (144BAPB), 10.8 grams (0.1 moles) of m-phenylenediamine (MPDA), 2000 grams of N,N-dimethylacetamide ( DMAc) and 920 grams of N-methyl-2-pyrrolidone (NMP) were added to the polymerization bottle, stirred at room temperature, after they were completely dissolved, cooled in an ice-water bath to below 5°C, and 308.9 grams (1.05 moles) of 3,3',4 , 4'-biphenyltetracarboxylic dianhydride (BPDA), stirred, and reacted at 8°C for 4 hours to obtain 3502.5 grams of homogeneous, transparent, viscous BPDA-type polyamic acid resin solution, recorded as BPDA-PAA- 2. Using Brookfield CAP2000+ vertebral plate viscometer, the viscosity at 50°C was measured as 572mPa.s.

Embodiment 3

[0039] 51.8 g (0.1 mole) of 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane (BAPFP), 180.0 g (0.9 mole) of 4,4'-diaminodiphenyl ether (DADPE ) and 3,290 grams of N-methyl-2-pyrrolidone (NMP) were added to the polymerization bottle, stirred at room temperature, and after they were completely dissolved, they were cooled in an ice-water bath to below 5°C, and 317.7 grams (1.08 moles) of 3,3',4, 4'-biphenyltetracarboxylic dianhydride (BPDA), stirred, reacted at 10°C for 6 hours, and obtained 3839.5 grams of homogeneous, transparent, viscous BPDA-type polyamic acid resin solution, recorded as BPDA-PAA-3 . Using Brookfield CAP2000+ vertebral plate viscometer, its viscosity at 50°C is measured as 425mPa.s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a BPDA type BDATHQ branched polyamide resin film and a preparation method thereof. In raw materials of the film, the mass ratio of BDATHQ and BPDA type linear polyamic acid resins is 1:(100-800). The preparation method comprises the following steps: mixing aromatic dual primary amine with strongly polar aprotic organic solvent, stirring at room temperature, cooling to 5 DEG C or below, adding BPDA, stirring, and reacting at 5-10 DEG C for 1-6 hours to obtain a BPDA type polyamic acid resin solution; and mixing the resin solution with BDATHQ at room temperature, stirring, forming a film, heating, performing dewatering thermal imidization, cooling, and stripping to obtain the final product. The method provided by the invention is mild in reaction conditions, simple to operate, low in cost and friendly to environment, thereby being beneficial to industrial large-scale production; and the film can be used in the high-tech fields of flexible solar cells, space telescopes, large generator main insulation, magnet wire wrapping electrical insulation materials, flexible copper-clad plates and the like.

Description

technical field [0001] The invention belongs to the field of polyimide film and its preparation, in particular to a BPDA type BDATHQ branched polyimide resin film and its preparation method. Background technique [0002] Polyimide film is a kind of polymer material with excellent comprehensive properties. It has particularly excellent heat resistance, low temperature resistance, flame retardancy, electrical properties and mechanical properties. It is widely used in electronic microelectronics, printing High-tech fields such as circuit boards, wires and cables, motor main insulation, shipping, aerospace, lasers, and optoelectronics. [0003] However, traditional polyimide films, such as the KAPTON film produced by the American DUPONT company and the domestic H film, have a molecular structure of pyromellitic dianhydride, that is, the main monomer raw material is pyromellitic acid di anhydride and 4,4'-diaminodiphenyl ether. [0004] NASA (NASA) plans to launch the Next Gene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L79/08C08G73/10C08J5/18
CPCC08L79/08C08G73/1071C08J5/18C08J2379/08
Inventor 虞鑫海周志伟
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com