Low temperature antique glaze with cleaner air effect and preparing method thereof

A technology of air purification and low temperature, which is applied in the field of low-temperature antique glaze and its preparation, and can solve the problem of less antique ceramics

Inactive Publication Date: 2017-01-25
佛山市高明区诚睿基科技有限公司
View PDF9 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Along with the rapid development of economy and people's raising to living standard, pottery has become the pottery that places such as people's family, office, shopping malls are used for decoration, but the ceramic glaze surface of existing technology, though smoothness is high, color is rich, but There are few antique ceramics, especially multi-functional antique glazes, which are basically not involved, so the technology needs to be improved, and there is an urgent need to develop functional antique glazes, such as antibacterial, anti-static, air purification and other functions, to further expand its application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low temperature antique glaze with cleaner air effect and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A low-temperature antique glaze with the effect of purifying air and a preparation method thereof, the preparation method comprising the following steps:

[0035] Step A, prepare negative ion low-temperature frit: mix and grind 10% quartz, 10% feldspar, 16% borax, 12% carbonate, 35% boric acid, 3% spodumene, 4% fluoride salt, and 1.5% kaolin Uniform; then add 0.5% antibacterial compound and 8% negative ion compound, and grind evenly to obtain a mixture; spread the mixture into a refractory sagger, and perform high-temperature melting at 1250~1320°C to obtain a molten slurry ; The slurry is water-quenched and cooled, and broken into particles to obtain negative ion low-temperature frit; wherein, the feldspar is obtained by mixing potassium feldspar and albite feldspar in a weight ratio of 4:1; the carbonate is obtained by Potassium carbonate, sodium carbonate, barium carbonate, lithium carbonate and calcium carbonate are mixed in a weight ratio of 3:1:3:2:1; the fluoride...

Embodiment 2

[0048] A low-temperature antique glaze with the effect of purifying air and a preparation method thereof, the preparation method comprising the following steps:

[0049] Step A, prepare negative ion low-temperature frit: mix and grind 15% quartz, 8% feldspar, 25% borax, 8% carbonate, 27% boric acid, 5% spodumene, 3% fluoride salt, and 3% kaolin uniform; then add 1% antibacterial compound and 5% negative ion compound, and grind evenly to obtain a mixture; spread the mixture into a refractory sagger, and perform high-temperature melting at 1250~1320°C to obtain a molten slurry ; The slurry is water-quenched and cooled, and broken into particles to obtain negative ion low-temperature frit; wherein, the feldspar is obtained by mixing potassium feldspar and albite feldspar in a weight ratio of 4:1; the carbonate is obtained by Potassium carbonate, sodium carbonate, barium carbonate, lithium carbonate and calcium carbonate are mixed in a weight ratio of 3:1:3:2:1; the fluoride salt ...

Embodiment 3

[0062] A low-temperature antique glaze with the effect of purifying air and a preparation method thereof, the preparation method comprising the following steps:

[0063] Step A, prepare negative ion low-temperature frit: mix and grind 18% quartz, 12% feldspar, 21% borax, 5% carbonate, 27% boric acid, 8% spodumene, 1% fluoride salt, and 5% kaolin Uniform; then add 2% antibacterial compound and 1% negative ion compound, and grind evenly to obtain a mixture; spread the mixture into a refractory sagger, and perform high-temperature melting at 1250~1320°C to obtain a molten slurry ; The slurry is water-quenched and cooled, and broken into particles to obtain negative ion low-temperature frit; wherein, the feldspar is obtained by mixing potassium feldspar and albite feldspar in a weight ratio of 4:1; the carbonate is obtained by Potassium carbonate, sodium carbonate, barium carbonate, lithium carbonate and calcium carbonate are mixed in a weight ratio of 3:1:3:2:1; the fluoride salt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low temperature antique glaze with cleaner air effect and preparing method thereof, the preparing method comprises the steps of: A, preparing low temperature frit; B, preparing glaze, mixing low temperature frit, colorant, potassium feldspar, quartz, calcite, talc, calcium phosphate, anion compounds and antibacterial composite to obtain the mixing powder, putting sodium tripolyphosphate and carboxymethyl cellulose into powder and mixing the powder evenly, fine grinding, and then adding water so as to obtain the glaze; C, applying the glaze evenly on the body, and then putting the body into the reducing atmosphere furnace, cooling the natural glaze to room temperature after heat preservation, and the low temperature antique glaze with cleaner air effect is obtained. Compared with the prior antique glaze, the antique glaze produced by the invention has the advantages of scientific ingredients,reasonable preparing method, pure color and stable performance; at the same time with a reasonable combination of negative ions and antibacterial composite materials, the synergistic action of the two making the antique glaze has characteristics of excellent anti-bacterial, anti-fouling and air purification, the scope of the application of the antique glaze is further broaden.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a low-temperature antique glaze with the effect of purifying air and a preparation method thereof. Background technique [0002] Bacteria and mold, as pathogenic bacteria, are very harmful to humans, animals and plants, affecting people's health and even life-threatening, and bringing significant economic losses. Therefore, the research on antibacterial materials and their products has attracted people's attention day by day, and the demand for antibacterial products will constitute a huge market. [0003] For environmental protection, negative air ions can eliminate indoor odors and various harmful gases. The irritating gases such as benzene, formaldehyde, ketone, ammonia volatilized from the decoration materials used in the interior decoration process, as well as the sour smell of leftovers in daily life, cigarettes and other harmful odors to the human body, use materials ric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/20C03C8/16C03C8/06C03C1/00C04B41/86
CPCC03C8/20C03C1/00C03C8/06C03C8/16C03C2204/02C04B41/5022C04B41/86C04B41/4539C04B41/0072
Inventor 黎淑娟
Owner 佛山市高明区诚睿基科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com