Preparation method of cathode material lithium nickel cobalt manganese oxide of lithium battery

A technology of nickel-cobalt lithium manganese oxide and positive electrode materials, applied in battery electrodes, circuits, electrical components, etc., can solve the problems of high labor intensity in operation, many compounds added, difficult control of the reaction process, etc., and achieve excellent safety performance and discharge performance and excellent cycle performance

Inactive Publication Date: 2017-02-15
JIANGXI JIANGTE LITHIUM LON BATTERY MATERIAL
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many compounds added in the above method, the reaction process steps are too long, and the reaction process cannot be automatically controlled.
Manual operation is labor-intensive, and the reaction process is not easy to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of cathode material lithium nickel cobalt manganese oxide of lithium battery
  • Preparation method of cathode material lithium nickel cobalt manganese oxide of lithium battery
  • Preparation method of cathode material lithium nickel cobalt manganese oxide of lithium battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The preparation method of a kind of nickel cobalt manganate lithium of present embodiment 1 refers to LiNi 0.6 co 0.2 mn 0.2 o 2 The preparation method uses soluble nickel, cobalt, and manganese salts as raw materials, and its specific process steps are as follows: 1) co-precipitation reaction to prepare nickel-cobalt lithium manganese oxide precursor, using soluble nickel, cobalt sulfate, and manganese chloride as raw materials, Add water to make a mixed aqueous solution of nickel, cobalt, and manganese salts, add aqueous sodium hydroxide solution as a precipitating agent, use ammonia water as a complexing agent, carry out co-precipitation reaction under heating and the presence of alkali, filter to obtain filtrate and filter residue, and filter residue cleaning In order to obtain the precursor of nickel-cobalt-manganese; control the mass molar ratio of nickel salt, cobalt salt, and manganese chloride in the mixed aqueous solution to 2-3:1-1.5:1-1.2; control the reac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention aims to provide a preparation method of a cathode material lithium nickel cobalt manganese oxide of a lithium battery. Soluble nickel, cobalt and manganese salt are taken as raw materials, and the method is characterized by comprising specific process steps as follows: 1) preparation of a nickel-cobalt-manganese precursor through coprecipitation: soluble nickel, cobalt sulfate and manganese chloride are taken as the raw materials, water is added, a nickel, cobalt and manganese salt mixed aqueous solution is prepared, a sodium hydroxide aqueous solution is added as a precipitant, ammonia water is taken as a complexing agent, coprecipitation is performed under conditions of heating and alkali presence, a filtrate and filer residues are obtained through filtering, the filter residues are cleaned, and the nickel-cobalt-manganese precursor is prepared; 2) preparation of a lithium nickel cobalt manganese oxide product through mixing: the prepared nickel-cobalt-manganese precursor is dried, ground and stirred and mixed sufficiently with lithium salt, the mixture is loaded in a bowl, calcined, sintered, broken screened, dried and packaged, and the cathode material lithium nickel cobalt manganese oxide is obtained; the calcining and sintering time and the sintering temperature are controlled. Full-automatic controlled production is adopted in the production process, the production operation is convenient, reaction conditions are mild, and the prepared ternary cathode material lithium nickel cobalt manganese oxide has excellent performance.

Description

[0001] Technical field: [0002] The invention relates to the preparation of a positive electrode material of a lithium battery, in particular to a preparation method of nickel cobalt lithium manganese oxide, a positive electrode material of a lithium battery. [0003] Background technique: [0004] As a new type of green secondary battery, lithium-ion batteries are widely used in wireless communication, transportation, aerospace and other aspects. Lithium-ion batteries are mainly composed of positive electrode materials, lithium-intercalated transition metal oxides, negative electrode materials such as highly graphitized Carbon, separators such as polyolefin microporous membranes and electrolyte materials. The lithium-ion cathode material is a crucial factor restricting the performance of lithium-ion batteries in all aspects. [0005] Lithium-ion battery cathode material is one of the key materials in lithium-ion batteries, and its performance will directly affect the perform...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/131H01M4/505H01M4/525
CPCH01M4/131H01M4/505H01M4/525Y02E60/10
Inventor 胡伟钟盛文李晓艳李喜福刘美景
Owner JIANGXI JIANGTE LITHIUM LON BATTERY MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products