A formaldehyde and chitin technology applied in the chemical industry to achieve high removal efficiency, formaldehyde elimination and low cost
Inactive Publication Date: 2017-02-22
林映霞
View PDF0 Cites 7 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Formaldehyde is easily absorbed through the respiratory tract, but rarely absorbed through the skin
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] A formaldehyde repelling material, comprising the following components and parts by weight: tea extract 3, chitin 2, calcium chloride 7, ferric oxide 2, starch adhesive 9, potassium permanganate 1, sodium hydroxide 0.5, chlorine Sodium chloride 2, attapulgite 22, bentonite 6, diatomaceous earth 8, activated carbon 10, titanium dioxide 8, mugwort leaf extract 8, grapefruit peel extract 5, orange peel extract 9, purslane extract 2, saponins Extract 6, Hydroxymethylcellulose 11, Alkaline Earth Metal Chloride 6, Water 45.
[0012] The particle size of calcium chloride and ferric oxide is 250nm. Attapulgite and diatomaceous earth are 80 mesh.
Embodiment 2
[0014] A formaldehyde repelling material, comprising the following components and parts by weight: tea extract 5, chitin 4, calcium chloride 9, ferric oxide 3.5, starch adhesive 11, potassium permanganate 2, sodium hydroxide 0.8, chlorine Sodium chloride 4, attapulgite 25, bentonite 8, diatomaceous earth 12, activated carbon 13, titanium dioxide 11, mugwort leaf extract 9, grapefruit peel extract 6, orange peel extract 10, purslane extract 3, saponins Extract 8, Hydroxymethylcellulose 14, Alkaline Earth Metal Chloride 9, Water 50. The particle size of calcium chloride and ferric oxide is 320nm. Attapulgite and diatomaceous earth are 100 mesh.
Embodiment 3
[0016] A formaldehyde repelling material, comprising the following components and parts by weight: tea extract 4, chitin 3, calcium chloride 8, ferric oxide 3, starch adhesive 10, potassium permanganate 1.5, sodium hydroxide 0.7, chlorine Sodium chloride 3.5, attapulgite 24, bentonite 7, diatomaceous earth 11, activated carbon 12, titanium dioxide 9, mugwort leaf extract 8.5, grapefruit peel extract 5.5, orange peel extract 9.5, purslane extract 2.5, saponins Extract 7, Hydroxymethylcellulose 13, Alkaline Earth Metal Chloride 8, Water 47. The particle size of calcium chloride and ferric oxide is 280nm. Attapulgite and diatomaceous earth are 90 mesh.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to the field of chemical materials, and particularly relates to a formaldehyde removing material. The formaldehyde removing material is prepared from the following components in parts by weight: 3 to 5 parts of tea leaf extract, 2 to 4 parts of chitin, 7 to 9 parts of calcium chloride, 2 to 3.5 parts of iron sesquioxide, 9 to 11 parts of starch adhesive, 1 to 2 parts of potassium hypermanganate, 0.5 to 0.8 part of sodium hydroxide, 2 to 4 parts of sodium chloride, 22 to 25 parts of attapulgite clay, 6 to 8 parts of bentonite, 8 to 12 parts of diatomite, 10 to 13 parts of activated carbon, 8 to 11 parts of titanium pigment, 8 to 9 parts of folium artemisiae argyi extract, 5 to 6 parts of shaddock peel extract, 9 to 10 parts of orange peel extract, 2 to 3 parts of herba portulacae extract, 6 to 8 parts of fructus gleditsiae extract, 11 to 14 parts of hydroxymethyl cellulose, 6 to 9 parts of alkaline earth metal chloride and 45 to 50 parts of water. The formaldehyde removing material is low in cost, is healthy and environment-friendly, can be also used for effectively eliminating formaldehyde in daily life, removing dampness, sterilizing and getting rid of a peculiar smell, can be used for purifying air, further will not form secondary pollution, is high in formaldehyde removal rate, long in acting time, further, is nontoxic, and has no any side effects on a human body.
Description
technical field [0001] The invention relates to the field of chemical industry, in particular to a formaldehyde repelling material. Background technique [0002] Formaldehyde is an important organic raw material, mainly used in the plastic industry such as phenolic resin, urea-formaldehyde plastic - electric jade, synthetic fiber such as synthetic vinylon - polyvinyl formal, leather industry, medicine, dyes, etc. At present, pure cotton textiles are mostly used as formaldehyde printing and dyeing auxiliaries, because pure cotton textiles are easy to wrinkle, and the use of formaldehyde-containing auxiliaries can improve the stiffness of cotton cloth. Textiles containing formaldehyde will gradually release free formaldehyde during people's wearing and use, which will cause respiratory inflammation and skin inflammation through human respiratory tract and skin contact, and will also irritate the eyes. Formaldehyde can cause allergies and can also induce cancer. Manufacturers...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more