Preparation method of bismuth zirconate microcrystalline ceramic glaze with photocatalysis function

A bismuth zirconate and photocatalysis technology, which is applied in the field of ceramic glazes, can solve the problems of poor bonding between photocatalytic films and substrates, uneven distribution of photocatalyst glazes, and affecting the aesthetics of ceramics, achieving good visible light response and improving light Good catalytic performance and surface decoration effect

Active Publication Date: 2017-05-10
SHAANXI UNIV OF SCI & TECH
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above methods, or there are shortcomings such as poor bonding between the photocatalytic film and the substrate, easy to fall off, or uneven distribution in the photocatalyst glaze, and the "rainbow effect" and other shortcomings, which directly affect the aesthetics of ceramics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of bismuth zirconate microcrystalline ceramic glaze with photocatalysis function
  • Preparation method of bismuth zirconate microcrystalline ceramic glaze with photocatalysis function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1) First, quartz, potassium feldspar, albite, borax, Bi 2 o 3 , Suzhou soil, lithium carbonate and other raw materials are prepared according to the following mass chemical composition ratios. SiO 2 :Al 2 o 3 :B 2 o 3 : Bi 2 o 3 : Li 2 O: Na 2 O:K 2 O=57:4:22:4:7:4:3.

[0032] 2) Dry mix and grind the above-mentioned powders, pass through a 60-mesh sieve to obtain the mixture, put it into a crucible, put it into an electric furnace and keep it at 1270°C for 20 minutes, take it out and pour it into water to quench to make a frit. Take out the frit from the water, put it into a ball mill after drying, and grind it finely. The mass ratio of control material (frit): ball: water is 1:1:0.8, pass through a 250-mesh sieve after grinding for 3 hours, and dry for later use. This powder is denoted as A material.

[0033] 3) Combine the above material A and Bi 2 o 3 , ZrO 2 And the mass ratio of Suzhou soil is A: Bi 2 o 3 : Suzhou soil = 82:7.4:7 ratio for batchi...

Embodiment 2

[0039] 1) First, quartz, potassium feldspar, albite, borax, Bi 2 o 3 , Suzhou soil, lithium carbonate and other raw materials are prepared according to the following mass chemical composition ratios. SiO 2 :Al 2 o 3 :B 2 o 3 : Bi 2 o 3 : Li 2 O: Na 2 O:K 2 O=58:5:23:3:6:3:2.

[0040] 2) Dry mix and grind the above-mentioned powders, pass through a 60-mesh sieve to obtain the mixture, put it into a crucible, put it into an electric furnace and keep it warm at 1280°C for 30 minutes, take it out and pour it into water to quench to make a frit. Take the frit out of the water, put it into a ball mill after drying, and grind it finely. The mass ratio of control material (frit): ball: water is 1:1:0.8, pass through a 250-mesh sieve after grinding for 4 hours, and dry for later use. This powder is denoted as A material.

[0041] 3) Combine the above material A and Bi 2 o 3 , ZrO 2 And the mass ratio of Suzhou soil is A: Bi 2 o 3 : Suzhou soil = 84: 7.2: 6 ratio for b...

Embodiment 3

[0045] 1) First, quartz, potassium feldspar, albite, borax, Bi 2 o 3 , Suzhou soil, lithium carbonate and other raw materials are prepared according to the following mass chemical composition ratios. SiO 2 :Al 2 o 3 :B 2 o 3 : Bi 2 o 3 : Li 2 O: Na 2 O:K 2 O=59:6:24:2:5:2:1.

[0046] 2) Dry mix and grind the above-mentioned powders, pass through a 40-mesh sieve to obtain the mixture, put it into a crucible, put it in an electric furnace at 1290° C. for 40 minutes, take it out and pour it into water to quench to obtain a frit. Take out the frit from the water, put it into a ball mill after drying, and grind it finely. The mass ratio of control material (frit): ball: water is 1:1:0.8, pass through a 250-mesh sieve after grinding for 3 hours, and dry for later use. This powder is denoted as A material.

[0047] 3) Combine the above material A and Bi 2 o 3 , ZrO 2 And the mass ratio of Suzhou soil is A: Bi 2 o 3 : Suzhou soil = 86:7:5 ratio for batching, and Bi ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of bismuth zirconate microcrystalline ceramic glaze with a photocatalysis function. The preparation method comprises the following steps: blending quartz, potassium feldspar, albite, borax, Bi2O3, Suzhou soil and lithium carbonate; preserving heat at 1,270-1,290 DEG C for 20-40min; taking out and pouring into water for quenching to obtain a frit; grinding the frit to obtain a material A; blending the material A with Bi2O3, ZrO2 and Suzhou soil to obtain a material B; adding the material B and a dispersing agent into water, stirring and uniformly mixing to obtain glaze slip; glazing the ceramic surface with the glaze slip; and firing to obtain a bismuth zirconate ceramic glaze with a photocatalysis function. The glaze prepared According to the invention has good gloss and stable chemical property. According to the invention, the ceramic glaze is prepared by adopting a firing technology, coating is not needed, and thus the prepared functional ceramic glaze is tightly combined with a ceramic base and does not fall off easily; and moreover, crystal flowers of special morphology can be quickly formed on the glaze surface, and the surface decoration effect is good.

Description

technical field [0001] The invention belongs to the technical field of ceramic glazes. Specifically relates to a preparation method of bismuth zirconate microcrystalline ceramic glaze with photocatalytic function. Background technique [0002] Photocatalytic technology began in 1972. Japanese scholars Fujishima and Honda discovered that hydrogen can be produced by photocatalytically decomposing water on semiconductor electrodes [Fujishima A., Honda K. Photocatalysis-decomposition of water at the surface of an irradiated semiconductor[J].Nature, 1972,238(5385):37-38.], this discovery has aroused great attention of scientific and technological workers to photocatalysis. With the increasingly prominent energy and environmental issues, photocatalytic technology has received extensive attention and achieved rapid development. Photocatalytic materials have potential applications in degradation of organic pollutants, air purification, antibacterial and self-cleaning. [0003] Si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C04B41/86B01J23/18
CPCC03C8/20C04B41/5023C04B41/86B01J23/18B01J35/39C04B41/4535
Inventor 曹丽云罗艺佳黄剑锋李嘉胤孔新刚刘一军
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com