Waterborne transparent fireproof paint for historic buildings and preparation method of waterborne transparent fireproof paint

A technology for fire-retardant coatings and ancient buildings, applied in anti-corrosion coatings, powder coatings, coatings, etc., can solve the problems that flame-retardant coatings are difficult to have both flame retardancy and decorative properties, and fire-retardant coatings are difficult to apply at the same time, so as to achieve enhanced protection, The effect of speed reduction and stability improvement

Active Publication Date: 2017-05-10
应急管理部四川消防研究所 +1
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a water-based transparent ancient building fireproof coating and its preparation method, which solves the problem that the existing fireproof coating is difficult to be applied to ancient buildings with different materials and different degrees of corrosion and weathering at the same time, as well as the flame retardancy and decorative properties of the fire-retardant coating. Hard to have both

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne transparent fireproof paint for historic buildings and preparation method of waterborne transparent fireproof paint
  • Waterborne transparent fireproof paint for historic buildings and preparation method of waterborne transparent fireproof paint
  • Waterborne transparent fireproof paint for historic buildings and preparation method of waterborne transparent fireproof paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The present embodiment provides a kind of water-based transparent fireproof coating for ancient buildings, comprising 28.7% of amino resin, 2.6% of polyvinyl alcohol, 4.3% of ethylene-ethylene acetic acid copolymer, 9.3% of polysiloxane, 12.3% of phosphorus nitrogen phosphonate, Phosphonate 7.8%, Guanidine Phosphate 6.3%, Pentaerythritol 12.8%, Zirconium Borate 0.6%, Phytic Acid 4.7%, Triethanolamine 1.2%, Thickener XS-1670.43%, Ultraviolet Absorber UV1130 0.37%, Ultraviolet Absorber UV292 0.47%, wetting and dispersing agent SP-76 20.36%, coalescent PPH 0.47%, water-based coating coalescent XS-12 0.48%, defoamer A203E 0.4%, wood stabilizer MJB-TF5.7% and the balance of water.

Embodiment 2

[0032] This embodiment provides a method for preparing the water-based transparent ancient building fireproof coating described in Embodiment 1, which specifically includes the following steps.

[0033] (1) take each component by the formula of embodiment 1;

[0034](2) Water, account for 0.2% defoamer A203E of coating gross weight, dispersant, phosphorus nitrogen phosphonate, phosphonate, polysiloxane, guanidine phosphate, pentaerythritol, zirconium borate, phytic acid, triethanolamine Add it to the stirring device, stir at 1500-2000r / min for 20-30min, then place it in a three-roller mill for 2-3h;

[0035] (3) Reduce the speed of the disperser to 500-800r / min, continue to add film-forming aids PPH, amino resin, polyvinyl alcohol, ethylene-ethylene acetic acid copolymer and 0.2% of the total weight of the coating defoamer A203E, Thickening and leveling agent XS-167, water-based paint film-forming aid XS-12, ultraviolet absorber UV1130 and ultraviolet absorber UV292, wood sta...

Embodiment 3

[0047] The present embodiment provides a kind of water-based transparent fireproof coating for ancient buildings, comprising 26.7% of amino resin, 2.6% of polyvinyl alcohol, 4.3% of ethylene-ethylene acetic acid copolymer, 7.3% of polysiloxane, 14.3% of phosphorus nitrogen phosphonate, Phosphonate 8.8%, Guanidine Phosphate 6.3%, Pentaerythritol 12.8%, Zirconium Borate 0.6%, Phytic Acid 4.7%, Triethanolamine 1.2%, Thickener XS-1670.43%, Ultraviolet Absorber UV1130 0.37%, Ultraviolet Absorber UV292 0.47%, wetting and dispersing agent SP-76 20.36%, coalescent PPH 0.47%, water-based coating coalescent XS-12 0.48%, defoamer A203E 0.4%, wood stabilizer MJB-TF5.7% and the balance of water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses waterborne transparent fireproof paint for historic buildings and a preparation method of the waterborne transparent fireproof paint. The paint is prepared from, by weight, 25-30 parts of amino resin, 1-3 parts of waterborne polyvinyl alcohol powder, 3-5 parts of ethylene-vinyl acetate copolymer, 5-10 parts of polysiloxane, 18.5-34.5 parts of fire retardant, 10-15 parts of pentaerythritol, 1-5 parts of phytic acid, 0.5-1.5 parts of triethanolamine, 2.1-3.5 parts of additives, 5-10 parts of a wood stabilizer and 10-29 parts of water. The method includes steps of raw material weighing, primary mixing and secondary mixing. By condensation polymerization of active polysiloxane emulsion and active phosphonate, fireproof performance of the paint is improved, coating transparency is realized, original appearances of materials can be kept, and the paint is less prone to cracking and excellent in weather resistance; since a main component of the paint is dry powder, storage life of the paint is effectively prolonged; due to addition of the waterborne wood stabilizer and the phytic acid in the fireproof paint, rotten and deformed wood materials are protected effectively.

Description

technical field [0001] The invention belongs to the technical field of building fireproof coatings, and in particular relates to a water-based transparent ancient building fireproof coating and a preparation method thereof. Background technique [0002] The Chinese nation has a splendid civilization of five thousand years, and its history and culture have been passed down for a long time. Ancient buildings and ancient dwellings are artistic treasures with a long history, marking the civilization level of a country, witnesses of human history, and the common precious wealth of all mankind. However, due to some characteristics of its mostly wooden structure, its flame retardancy is poor. Fires often occur in ancient buildings and ancient dwellings all over our country. Once these national treasures are caught in fire, they will never be restored. [0003] Due to the lack of effective "active" protection means, most of them adopt "passive" spraying, fire hydrants and other met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/20C09D129/04C09D123/08C09D183/06C09D5/03C09D5/08C09D7/12
CPCC08L2201/02C08L2201/10C08L2205/035C09D5/033C09D5/08C09D161/20C08L29/04C08L23/0853C08L83/06C08K13/02C08K5/5333C08K5/5353C08K5/31C08K2003/387C08K5/053C08K5/521
Inventor 王新钢
Owner 应急管理部四川消防研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com