Preparation method of yttrium zirconate microcrystal ceramic glaze having photocatalytic function

A technology of microcrystalline ceramics and yttrium zirconate, which is applied in the field of preparation of yttrium zirconate microcrystalline ceramic glazes with photocatalytic function, which can solve the problems of poor bonding between photocatalytic film and substrate, uneven distribution of photocatalyst, and affecting the aesthetics of ceramics, etc. Problems, to achieve good visible light response, good surface decoration effect, and improve the effect of absorption utilization

Active Publication Date: 2017-05-17
SHAANXI UNIV OF SCI & TECH
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above methods, or there are shortcomings such as poor bonding between the photocatalytic film and the substrate, easy to fall off, or uneven distribution of the photocatalyst in the glaze, and the "rainbow effect" and other shortcomings, which directly affect the aesthetics of ceramics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of yttrium zirconate microcrystal ceramic glaze having photocatalytic function
  • Preparation method of yttrium zirconate microcrystal ceramic glaze having photocatalytic function
  • Preparation method of yttrium zirconate microcrystal ceramic glaze having photocatalytic function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1) First, quartz, potassium feldspar, albite, borax, Y 2 o 3 , Suzhou soil, and lithium carbonate are prepared according to the following mass chemical composition ratios. SiO 2 :Al 2 o 3 :B 2 o 3 : Y 2 o 3 : Li 2 O: Na 2 O:K 2 O=57:4:22:4:7:4:3.

[0033] 2) Dry mix and grind the above-mentioned powders, pass through a 60-mesh sieve to obtain the mixture, put it into a crucible, put it into an electric furnace and keep it at 1270°C for 20 minutes, take it out and pour it into water to quench to make a frit. Take out the frit from the water, put it into a ball mill after drying, and grind it finely. The mass ratio of control material (frit): ball: water is 1:1:0.8, pass through a 250-mesh sieve after grinding for 3 hours, and dry for later use. This powder is denoted as A material.

[0034]3) Combine the above material A and Y 2 o 3 , ZrO 2 And Suzhou soil is A material according to the mass ratio: Y 2 o 3 : Suzhou soil = 82:5:7 ratio for batching, and ...

Embodiment 2

[0041] 1) First, quartz, potassium feldspar, albite, borax, Y 2 o 3 , Suzhou soil, and lithium carbonate are prepared according to the following mass chemical composition ratios. SiO 2 :Al 2 o 3 :B 2 o 3 : Y 2 o 3 : Li 2 O: Na 2 O:K 2 O=58:5:23:3:6:3:2.

[0042] 2) Dry mix and grind the above-mentioned powders, pass through a 60-mesh sieve to obtain the mixture, put it into a crucible, put it into an electric furnace and keep it warm at 1280°C for 30 minutes, take it out and pour it into water to quench to make a frit. Take the frit out of the water, put it into a ball mill after drying, and grind it finely. The mass ratio of control material (frit): ball: water is 1:1:0.8, pass through a 250-mesh sieve after grinding for 4 hours, and dry for later use. This powder is denoted as A material.

[0043] 3) Combine the above material A and Y 2 o 3 , ZrO 2 And Suzhou soil is A material according to the mass ratio: Y 2 o 3 : Suzhou soil = 84:4.8:6 ratio for batching...

Embodiment 3

[0047] 1) First, quartz, potassium feldspar, albite, borax, Y 2 o 3 , Suzhou soil, lithium carbonate and other raw materials are prepared according to the following mass chemical composition ratios. SiO 2 :Al 2 o 3 :B 2 o 3 : Y 2 o 3 : Li 2 O: Na 2 O:K 2 O=59:6:24:2:5:2:1.

[0048] 2) Dry mix and grind the above-mentioned powders, pass through a 40-mesh sieve to obtain the mixture, put it into a crucible, put it in an electric furnace at 1290° C. for 40 minutes, take it out and pour it into water to quench to obtain a frit. Take out the frit from the water, put it into a ball mill after drying, and grind it finely. The mass ratio of control material (frit): ball: water is 1:1:0.8, pass through a 250-mesh sieve after grinding for 3 hours, and dry for later use. This powder is denoted as A material.

[0049] 3) Combine the above material A and Y 2 o 3 , ZrO 2 And Suzhou soil is A material according to the mass ratio: Y 2 o 3 : Suzhou soil = 86:4.6:5 ratio for b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a yttrium zirconate microcrystal ceramic glaze having a photocatalytic function. The preparation method comprises the following steps: preparing quartz, potash feldspar, albite, borax, Y2O3, Suzhou clay and lithium carbonate, keeping the above raw materialsat 1270-1290 DEG C for 20-40 minutes, taking out, pouring into water, quenching to prepare a fusion cake, and grinding the fusion cake to obtain a material A; preparing the material A, Y2O3, ZrO2 and Suzhou clay to obtain a material B; adding the material B and dispersing agent into water, and uniformly stirring and mixing to prepare a glaze slip; and applying the glaze slip to the surface of ceramics, and firing to obtain the yttrium zirconate microcrystal ceramic glaze having a photocatalytic function. According to the invention, the ceramic glaze is prepared through a firing process and does not need coating, so that the prepared functional ceramic glaze material can be tightly combined with a ceramic matrix; and the photocatalyst Y2Zr2O7 generated in the sintering process of Y2O3 and ZrO2 is uniformly distributed in the glaze material, thereby avoiding the condition that the aesthetic property of the glaze material is influenced due to a rainbow effect.

Description

technical field [0001] The invention belongs to the technical field of ceramic glazes, and in particular relates to a preparation method of yttrium zirconate microcrystalline ceramic glaze with photocatalytic function, which is applied in the fields of architectural sanitary ceramics and daily-use ceramics. Background technique [0002] With the development of modern society, in the process of rapid urbanization, social contradictions and environmental problems have gradually become prominent, especially in recent years, air quality has been criticized by the whole people [Guo Shihong, Gao Ming, et al. Coordination of air quality and urbanization quality Relationship Research [J]. Ecological Economy, 2015, 31(3):25-30.]. We know that in the home environment that is closely related to people's lives, the main air pollutants include volatile organic compounds, air colonies, CO 2 [Zhuang Xiaomin. Analysis of indoor air pollution and research on the release of typical pollutant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C03C8/02C04B41/86C03C10/02
CPCC03C8/02C03C8/20C03C10/00C04B41/5023C04B41/86C04B41/4539C04B41/4543
Inventor 曹丽云罗艺佳黄剑锋李嘉胤孔新刚刘一军
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap