Polymer composite material mixed with radix puerariae fiber powder and preparation method thereof

The technology of pueraria fiber and composite material is applied in the field of preparation of polymer composite materials, which can solve the problems of wasting natural resources and polluting the environment, and achieves the effect of satisfying high performance, wide sources, and improving heat resistance and friction and wear performance.

Inactive Publication Date: 2017-05-24
江苏省盐城市射阳县射阳港对虾养殖二公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, Pueraria slag is discarded or simply processed and utilized not only pollutes the environment, but also wastes natural resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer composite material mixed with radix puerariae fiber powder and preparation method thereof
  • Polymer composite material mixed with radix puerariae fiber powder and preparation method thereof
  • Polymer composite material mixed with radix puerariae fiber powder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1: the preparation method of the polymer composite material that is mixed with kudzu root fiber powder, comprises the steps,

[0034](1) Preparation of kudzu root fiber powder: add water to the kudzu root dregs and stir until it is completely submerged, then use ultrasonic cleaning for 10 minutes, filter, add water to wash again, repeat the above process three times, and then put the washed kudzu root dregs at 40°C Dry for 6 hours; wrap the treated pueraria slag with filter paper, and extract it in petroleum ether solution. The temperature of the water bath during extraction is 75°C; repeat the extraction several times under the above extraction conditions until the liquid in the extractor changes from yellow-green to yellow-green. Nearly colorless, take out the kudzu root slag, and dry it for 6 hours at a temperature of 40°C to obtain the kudzu root fiber powder;

[0035] (2) Mixing: Mix the following components:

[0036] The material time is 20 minutes, ...

Embodiment 2

[0040] Embodiment 2: the preparation method of the polymer composite material that is mixed with kudzu root fiber powder, comprises the steps,

[0041] (1) Preparation of kudzu root fiber powder: add water to kudzu root dregs and stir until it is completely submerged, then use ultrasonic cleaning for 15 minutes, filter, add water to wash again, repeat the above process three times, and then put the washed kudzu root dregs at 50°C Dry for 8 hours; wrap the treated pueraria slag with filter paper, and extract it in petroleum ether solution. The temperature of the water bath during extraction is 80°C; repeat the extraction several times under the above extraction conditions until the liquid in the extractor changes from yellow-green to yellow-green. Nearly colorless, take out the kudzu root slag, and dry it at a temperature of 50°C for 8 hours to obtain the kudzu root fiber powder;

[0042] (2) Mixing: Mix the following components:

[0043]

[0044] The material time is 40 ...

Embodiment 3

[0048] Embodiment 3: the preparation method of the polymer composite material that is mixed with kudzu root fiber powder, comprises the steps,

[0049] (1) Preparation of kudzu root fiber powder: add water to kudzu root dregs and stir until it is completely submerged, then use ultrasonic cleaning for 20 minutes, filter, add water to wash again, repeat the above process three times, and then put the washed kudzu root dregs at 60°C Dry for 10 hours; wrap the treated kudzu root residue with filter paper, and extract in petroleum ether solution. The temperature of the water bath during extraction is 85°C; repeat the extraction several times under the above extraction conditions until the liquid in the extractor changes from yellow-green to yellow-green. Nearly colorless, take out the kudzu root slag, and dry it for 10 hours at a temperature of 60°C to obtain the kudzu root fiber powder;

[0050] (2) Mixing: Mix the following components:

[0051]

[0052]

[0053] The materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polymer composite material mixed with radix puerariae fiber powder. The polymer composite material is prepared from the following components in parts by weight: 6 to 12 parts of modified phenolic resin, 5 to 10 parts of nitrile rubber powder, 15 to 21 parts of radix puerariae fiber powder, 10 to 20 parts of graphite, 1 to 3 parts of antimony sulfide, 1 to 3 parts of zinc oxide, 5 to 15 parts of coke, 10 to 20 parts of calcium carbonate, 5 to 15 parts of mullite powder, 5 to 15 parts of clay, 4 to 6 parts of chromite and 1 to 3 parts of alumina. According to the polymer composite material, the radix puerariae fiber powder and the mullite powder with high specific heat are combined to enhance the polymer composite material, so that the mechanical strength of a product is increased, the heat resistance and friction and wear properties of the product can be obviously improved, and the high-performance requirement of the composite material is satisfied; additionally, an extraction process of the radix puerariae fiber powder is simple, sources are wide, the environmental requirement is satisfied, and the polymer composite material prepared from the radix puerariae fiber powder has the advantage of low cost and is suitable for industrialized mass production and use.

Description

technical field [0001] The invention belongs to the field of polymer composite material preparation, and in particular relates to the preparation of a polymer composite material produced by using kudzu root waste residue. Background technique [0002] With the rapid development of the automobile industry, higher requirements are put forward for the development of clutch face polymer composite materials, not only requiring it to have a suitable friction coefficient and wear rate, but also to be environmentally friendly, comfortable and low-cost. Faced with these more stringent requirements, people have found some solutions to improve friction and wear performance, and the use of high-performance fiber-reinforced polymer composites is one of them. [0003] However, many of these methods are at the expense of cost or are not environmentally friendly, and are difficult to produce on a large scale, such as aramid fibers and carbon fibers, especially carbon fibers, which have good...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L99/00C08L61/14C08L9/02C08K3/04C08K3/30C08K3/22C08K3/26C08K3/34B29C51/08B29C51/42B29C71/02
CPCB29C51/08B29C51/42B29C71/02C08K2201/014C08L99/00C08L2201/08C08L2205/03C08L61/14C08L9/02C08K3/04C08K2003/3009C08K2003/2296C08K2003/265C08K3/34C08K3/346C08K2003/2227
Inventor 王占红宋娟王杰蒋穹杨子润张勇马原野罗森
Owner 江苏省盐城市射阳县射阳港对虾养殖二公司