Concrete reinforced curing agent
An enhanced curing agent technology, applied in the field of reinforced concrete curing agent, can solve the problems of poor durability, low water retention rate, large application amount, etc., and achieve improved strength and crack resistance, high water retention and weather resistance, and reduced volume shrinkage effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] A concrete reinforced curing agent is composed of the following raw materials in parts by mass: 90 parts of silicon-acrylic emulsion, 6 parts of sodium silicate, 5 parts of aluminum sulfate, 2 parts of early strength agent, 3 parts of water-repellent agent, 1 part of leveling agent, konjac 2 parts of fine powder, 5 parts of deionized water; Among them, the silicone acrylic emulsion is composed of active silicone resin, styrene, isooctyl acrylate, Acrylamide, silane coupling agent, sodium persulfate, methyl methacrylate, dodecyl alcohol ester and deionized water, early strength agent is triethanolamine, water repellent is sodium methyl siliconate, leveling agent It is fluorocarbon modified polyacrylate.
[0020] The preparation method of a concrete reinforced curing agent is: dissolving konjac fine powder in deionized water, then adding silicon acrylic emulsion, early strength agent, water repellent, leveling agent and mixing, then adding sodium silicate, sulfuric acid ...
Embodiment 2
[0022] A concrete reinforced curing agent is composed of the following raw materials in parts by mass: 90 parts of silicon-acrylic emulsion, 6 parts of sodium silicate, 7 parts of aluminum sulfate, 3 parts of early strength agent, 4 parts of water-repellent agent, 0.5 part of leveling agent, konjac 3 parts of fine powder, 7 parts of deionized water; Among them, the silicone acrylic emulsion is composed of active silicone resin, styrene, isooctyl acrylate, Acrylamide, silane coupling agent, sodium persulfate, methyl methacrylate, dodecyl alcohol ester and deionized water, early strength agent is triethanolamine, water repellent is sodium methyl siliconate, leveling agent It is fluorocarbon modified polyacrylate.
[0023] Its preparation method is with embodiment 1.
Embodiment 3
[0025] A concrete reinforced curing agent is composed of the following raw materials in parts by mass: 85 parts of silicon-acrylic emulsion, 9 parts of sodium silicate, 3 parts of aluminum sulfate, 4 parts of early strength agent, 2 parts of water-repellent agent, 1.8 parts of leveling agent, konjac 2 parts of fine powder, 8 parts of deionized water; Among them, the silicone acrylic emulsion is composed of active silicone resin, styrene, isooctyl acrylate, Acrylamide, silane coupling agent, sodium persulfate, methyl methacrylate, dodecyl alcohol ester and deionized water, early strength agent is triethanolamine, water repellent is sodium methyl siliconate, leveling agent It is fluorocarbon modified polyacrylate.
[0026] Its preparation method is with embodiment 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com