Forming method for microwave oven cavity or oven cavity

A molding method and microwave technology, applied in microwave heating, oven coatings, heating methods, etc., can solve the problems of human health hazards, huge energy consumption, cavity deformation and use, etc., and achieve good use safety, easy operation, and high temperature resistance. strong effect

Active Publication Date: 2017-05-31
深芏(中山)科技实业有限公司
View PDF13 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional molding method of microwave oven or oven cavity is mostly spraying enamel coating or Teflon coating on the surface of the alloy cavity. However, the enamel coating must be baked at a high temperature above 800°C, and the cavity is easily caused by thermal expansion and contraction. Body deformation and use of hu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] A method for forming a cavity of a microwave oven or an oven, comprising the following steps:

[0019] (1) Prepare sheet: select and prepare sheet according to the thickness of molding cavity, described sheet is common iron plate, aluminized plate or cold-rolled plate;

[0020] (2) Firstly carry out sand blasting treatment to the surface, the pressure of the sand blasting treatment is 0.7MPa, the sand material particle size is 60-120 mesh, and then clean and package into sheets or coils;

[0021] (3) Cut the sheet or coil, bend it, and weld it after shallow stretching;

[0022] (4) After degreasing, cleaning and drying, ceramic coating is sprayed, heated and solidified, and the curing temperature is 280°C. The ceramic coating is composed of the following raw materials in parts by weight:

[0023] Silicon carbide 3, tetraethyl orthosilicate 100, boron nitride 30, inorganic toner 12, polyacrylamide 0.5, silane coupling agent Kh560 0.7, isopropyl tris(dioctyl pyrophosphat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a forming method for a microwave oven cavity or an oven cavity. The forming method comprises the following steps of preparing sheet materials; performing surface treatment on the sheet materials; performing welding and shaping, and powder ceramic coating spraying. According to the forming method, the rough sand finish surfaces of the sheet materials are prepared firstly; then a welding and forming way is adopted, and next, the ceramic coating is sprayed, so that it is ensured that the cavity is not deformed, and the ceramic coating which is low in energy consumption, high in strength, resistant to high temperature, non-viscous and easy to clean can be obtained; the sheet materials are subjected to sand blasting treatment firstly and then the powder ceramic coating is sprayed, so that the conditions of high energy consumption, high-temperature solidification and deformation, or toxic fluorine-containing gas decomposition at a high temperature of the conventional enamel coating or Teflon coating can be avoided; and in addition, the cavity forming method disclosed by the invention achieves the beneficial effects of simple process, easy operation, high use safety, and strong high-temperature resistance.

Description

technical field [0001] The invention belongs to the field of cavity processing, and specifically designs a method for forming a cavity of a microwave oven or an oven. Background technique [0002] The traditional molding method of microwave oven or oven cavity is mostly spraying enamel coating or Teflon coating on the surface of the alloy cavity. However, the enamel coating must be baked at a high temperature above 800°C, and the cavity is easily caused by thermal expansion and contraction. Body deformation and use of huge energy consumption, while the heat-resistant temperature of Teflon coating is about 250 ℃, it can decompose toxic fluorine-containing gas under high temperature environment, which will cause great harm to human health, so in order to improve the above defects , it is necessary to continuously improve the molding method of the cavity. Contents of the invention [0003] The object of the present invention is to provide a method for forming a cavity of a m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H05B6/64F24C15/00
CPCF24C15/00F24C15/005H05B6/64H05B2206/04
Inventor 杨文举
Owner 深芏(中山)科技实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap