Anti-ultraviolet blue light protection film

A protective film and anti-ultraviolet technology, which is applied in the direction of electronic equipment, applications, adhesive additives, etc., can solve problems that no one has studied, and achieve the effect of simple preparation process and good light transmittance

Inactive Publication Date: 2017-06-20
杭州科翼科技有限公司
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the structure of this kind of protective film that can absorb blue light and shield ultraviolet rays to exert anti-blue light and anti-ultraviolet functions is a scratch-resistant coating or a separate optical film layer, and the anti-blue light and anti-ultraviolet functions are given to this layer of the adhesive layer. Protective film-like film has not been studied

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] An anti-ultraviolet and blue light protective film, the protective film is a composite film composed of a polyurethane layer and a polyester layer, and a composite adhesive layer is used between the polyurethane layer and the polyester layer, and the composite adhesive layer is composed of An adhesive coating of an ultraviolet blue light absorber, wherein the adhesive is a PVB adhesive, and the ultraviolet blue light agent is a compounding agent of modified melanin powder, 2-hydroxyl-4-methoxybenzophenone and titanium dioxide, and the modified melanin The ratio of powder, 2-hydroxy-4-methoxybenzophenone and titanium dioxide is 1:0.5:0.1; the adhesive is used according to actual needs,

[0026] The specific proportion of the adhesive is as follows: 18 parts of PVB, 25 parts of ethyl acetate, 0.1 part of ultraviolet blue light agent, 10 parts of bisphenol F epoxy resin, 5 parts of styrene, 3 parts of dimethyl itaconate, polydimethyl 2 parts of siloxane, 5 parts of polyvin...

Embodiment 2

[0035] An anti-ultraviolet and blue light protective film, the protective film is a composite film composed of a polyurethane layer and a polyester layer, and a composite adhesive layer is used between the polyurethane layer and the polyester layer, and the composite adhesive layer is composed of An adhesive coating of an ultraviolet blue light absorber, wherein the adhesive is a PVB adhesive, and the ultraviolet blue light agent is a compounding agent of modified melanin powder, 2-hydroxyl-4-methoxybenzophenone and titanium dioxide, and the modified melanin The ratio of powder, 2-hydroxy-4-methoxybenzophenone and titanium dioxide is 5:0.5:0.1; the adhesive is used according to actual needs,

[0036] The specific proportion of the adhesive is as follows: 18 parts of PVB, 25 parts of ethyl acetate, 0.5 parts of ultraviolet blue light agent, 10 parts of bisphenol F epoxy resin, 5 parts of styrene, 3 parts of dimethyl itaconate, polydimethyl 2 parts of siloxane, 5 parts of polyvi...

Embodiment 3

[0045] An anti-ultraviolet and blue light protective film, the protective film is a composite film composed of a polyurethane layer and a polyester layer, and a composite adhesive layer is used between the polyurethane layer and the polyester layer, and the composite adhesive layer is composed of Adhesive coating of ultraviolet and blue light absorbing agent, wherein, the adhesive is PVB adhesive, and the ultraviolet and blue light agent is the compounding agent of unmodified melanin powder, 2-hydroxy-4-methoxybenzophenone and titanium dioxide, unmodified The ratio of melanin powder, 2-hydroxy-4-methoxybenzophenone and titanium dioxide is 1:0.5:0.1; the adhesive is used according to actual needs,

[0046] The specific proportion of the adhesive is as follows: 18 parts of PVB, 25 parts of ethyl acetate, 0.05 parts of ultraviolet blue light agent, 10 parts of bisphenol F epoxy resin, 5 parts of styrene, 3 parts of dimethyl itaconate, polydimethyl 2 parts of siloxane, 5 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
barrier rateaaaaaaaaaa
barrier rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of polymer films and particularly relates to an anti-ultraviolet blue light protection film. The protection film is a composite film compounded by a polyurethane layer and a polyester layer, wherein the polyurethane layer and the polyester layer are compounded by a compound adhesive layer; the compound adhesive layer is an adhesive coating containing an ultraviolet blue light absorbent; the adhesive is a PVB adhesive; the ultraviolet blue light absorbent is a compound agent prepared from modified or unmodified melanin powder, 2-hydroxy-4-methoxybenzophenone and titanium dioxide. The preparation method of the film is simple; the film has high light transmittance, is capable of effectively absorbing ultraviolet light and blue light, and can be applied to multiple fields such as electronic industrial products and automobile adhesion films and the like according to different thicknesses of the film.

Description

technical field [0001] The invention relates to the technical field of polymer films, in particular to an anti-ultraviolet blue light protective film. Background technique [0002] Blue light is a high-energy visible light with a wavelength of 380-500nm, which can penetrate the lens to reach the retina, causing the retinal pigment epithelial cells to die, resulting in a lack of nutrients for light-sensitive cells, causing irreversible vision damage, and blue light is tiny in the air. Particles have a high probability of scattering and are prone to glare. In addition, blue light can also stimulate the brain, inhibit the secretion of melatonin and increase the production of adrenal cortex hormones, thereby destroying the balance of hormone secretion and directly affecting sleep quality. Among them, short-wave blue light with a wavelength of 400-480 nanometers is the most harmful to the retina. The short-wave blue light in this range can stimulate the retina to excite free rad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/08B32B27/40B32B27/36B32B7/12C09J4/02C09J4/06C09J11/04C09J11/06C09J11/08C08L75/04C08L83/04C08L23/08C08K13/06C08K9/04C08K3/34
CPCB32B7/12B32B27/08B32B27/36B32B27/40B32B2307/71B32B2457/20B32B2605/003C08K2201/011C08L75/04C09J4/06C09J11/04C09J11/06C09J11/08C08L83/04C08L23/0853C08K13/06C08K9/04C08K3/346
Inventor 龚毅超
Owner 杭州科翼科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com