PVC modified material used for antiskid carpets, and preparation method thereof

Abstract

The invention relates to the technical field of PVC materials, and concretely to a PVC modified material used for antiskid carpets, and a preparation method thereof. The PVC modified material used for anti-skid carpets comprises, by weight, 80-120 parts of PVC resin, 40-60 parts of a plasticizer, 10-15 parts of heavy calcium carbonate, 5-15 parts of light calcium carbonate, 3-7 parts of a high composite stabilizer, 1-3 parts of chlorinated polyethylene, 1-3 parts of a wear resistant modifier, 0.3-0.7 parts of an antiskid agent, 0.6-1.0 part of an ultraviolet resisting agent, 0.3-0.7 parts of an antioxidant and 0.3-0.7 parts of a lubricant. The PVC modified material used for antiskid carpets has the advantages of good wear resistance, good antiskid and anti-aging effect, environmental protection, excellent resistance to temperature and weather, high strength, excellent impact resistance, good flame retardation effect, excellent processability and excellent comprehensive performances.

Description

technical field [0001] The invention relates to the technical field of PVC materials, in particular to a PVC modified material for anti-slip carpets and a preparation method thereof. Background technique [0002] Polyvinyl chloride (PVC) is one of the earliest industrialized and widely used general-purpose thermoplastics. It has the advantages of light weight, high strength, insulation, flame retardancy, corrosion resistance, excellent comprehensive performance, low price and wide source of raw materials; but also There are the following disadvantages: 1. The toughness is poor, and it is easy to be brittle when impacted, so it cannot be used as a structural material. In addition, the brittleness of polyvinyl chloride is greatly affected by temperature. The lower limit of general PVC products is -15°C. The lower limit of use of PVC is -30°C; 2. Poor thermal stability, it begins to decompose HCl at 100°C, and decomposes more rapidly when it is higher than 150°C, and the meltin...

AI Technical Summary

Problems solved by technology

[0002] Polyvinyl chloride (PVC) is one of the earliest industrialized and widely used general-purpose thermoplastics. It has light weight, high strength, insulation, flame retardancy, corrosion resistance, It has the advantages of excellent comprehensive performance, low price and wide source of raw materials; but it also has the following disadvantages: 1. Poor toughness, easy to be brittle when impacted, so it cannot be used as a structural material. In addition, the brittleness of polyvinyl chloride is greatly affected by temperature. Large, the lower limit of general PVC products is -15°C, and the lower limit of soft PVC is -30°C; 2. Poor thermal stability, it begins to decompose HCl at 100°C, and decomposes more rapidly when it is higher than 150°C. The melting temperature of PVC is about 210°C; 3. The viscosity of PVC is extremely high and its fluidity is extremely poor, which limits its use to a certain extent.

[0003] However, the existing PVC materials for carpets have defects such as anti-slip, wear-resistant and anti-aging properties, which limit their use to a certain extent.