Permanent-magnet material resistant to high temperature and with high magnetic performance

A permanent magnet material, high magnetic technology, applied in the direction of magnetic materials, magnetic objects, electrical components, etc., can solve the problems of poor adhesion between magnetic powder and special resin, unsatisfactory high temperature resistance, and improved magnetic properties of magnets, to make up for Low operating temperature, reasonable control of grain size, and improved magnetic properties

Active Publication Date: 2017-07-14
JIANGSU PULONG MAGNETIC ELECTRICITY CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The advantages of NdFeB magnets are high cost performance and good mechanical properties; the disadvantages are that the Curie temperature point is low, the temperature characteristics are poor, and it is easy to be pulverized and corroded. It must be adjusted by adjusting its chemical composition and adopting surface treatment methods. To improve, in order to meet the requirements of practical application
[0004] In the existing technology, the Chinese invention patent CN101740193B, the title of the invention is: a high-performance high-resistivity rare earth permanent magnet and its preparation method. Started with technology, without adding insulating additives, studied the surface coupling process of magnetic powder, the mixing process of special resin and coupled magnetic powder, the orientation molding process of magnet temperature and pressure, etc., solved the problem of weak bonding between magnetic powder and special resin, special resin on the surface of magnetic powder There are a series of problems such as incomplete coating, easy agglomeration of special resin during processing, and limited improvement in magnetic properties of magnets after molding. From the results, it can be seen that the electrical insulation performance has indeed been significantly improved, but the high temperature resistance is not ideal. How? The development of high temperature resistant permanent magnet materials has become a development trend

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Magnetic powder surface coupling: Stir and mix 100 parts by weight of Nd2Fe14B magnetic powder and 0.2 parts by weight of graphene oxide powder to form a mixed magnetic powder; then mix 0.1 parts by weight of titanate coupling agent NDZ401 with 30 parts by weight of The xylene organic solvent is added in the magnetic powder of 100.2 parts by weight, and the above-mentioned solution is mixed uniformly by high-speed shear stirring at a speed of 2000 rpm for 0.5 h, and the magnetic powder and the coupling agent can be fully mixed by ultrasonic vibration for 0.5 h, and then The mixture is heated while stirring until the solvent is volatilized, and the modified mixed magnetic powder is dried and ground for use; (2) then the modified mixed magnetic powder is mixed with 0.1 parts by weight of ferrocene magnetic powder, dried , then add the mixed solution of 1 weight part of bisphenol A epoxy resin and acetone to the dried mixed magnetic powder, stir at a stirring speed of 2...

Embodiment 2

[0025] (1) Magnetic powder surface coupling: 100 parts by weight of Nd2Fe14B magnetic powder and 3 parts by weight of graphene oxide powder are stirred and mixed evenly to form a mixed magnetic powder, and 2 parts by weight of titanate coupling agent NDZ401 and 35 parts by weight of Alcohol was added to 103 parts by weight of the mixed magnetic powder, and the above solution was mixed uniformly by high-speed shear stirring at a speed of 500 rpm for 1 hour, and the mixed magnetic powder and the coupling agent could be fully mixed by ultrasonic vibration for 1 hour, and then the mixture was mixed Heating while stirring until the solvent volatilization is complete, drying and grinding the modified mixed magnetic powder for use; (2) then mixing the modified mixed magnetic powder with 0.3 parts by weight of ferrocene magnetic powder, drying, and then mixing The mixture of 6.5 parts by weight of phenol A epoxy resin and organic solvent acetone is added to the mixed magnetic powder af...

Embodiment 3

[0028] (1) Magnetic powder surface coupling: 100 parts by weight of Nd2Fe14B magnetic powder and 2 parts by weight of graphene oxide powder are stirred and mixed evenly to form a mixed magnetic powder, and 5 parts by weight of titanate coupling agent NDZ401 and 30 parts by weight of Xylene is added to the mixed magnetic powder of 102 parts by weight, and the above-mentioned solution is mixed uniformly by high-speed shear stirring at a speed of 800 rpm for 1.5h, and the mixed magnetic powder and the coupling agent can be fully mixed by ultrasonic oscillation for 1.5h, and then The mixture is heated while stirring until the solvent is volatilized, and the modified mixed magnetic powder is dried and ground for use; (2) then the modified mixed magnetic powder is mixed with 0.2 parts by weight of ferrocene magnetic powder, dried, Add the mixture of bisphenol A epoxy resin and organic solvent acetone to the surface-coupled mixed magnetic powder, stir for 1.5 hours at a stirring speed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
epoxy valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a permanent-magnet material resistant to high temperature and with high magnetic performance. The mass of the permanent-magnet material comprises 100 parts of Nd2Fe14B magnetic powder, 0.1-0.3 part of ferrocene magnetic powder, 0.1-5 parts of titanate coupling agent, 1-10 parts of bisphenol A epoxy resin and 0.2-3 parts of graphene oxide powder, and a cured material is formed after uniformly mixing the raw materials in a composite environment of a temperature field with a constant temperature being 20-200 DEG C and an orientation field with field magnetic intensity being 0.5-3T. With the permanent-magnet material provided by the invention, the defect of unfavorable temperature resistance of a bonded NdFeB material is improved, the application range of the bonded NdFeB material is expanded, the defect of low application temperature of the bonded NdFeB material can be made up, the magnetic performance of the magnet under high temperature is greatly improved, the weight loss of the magnet can be effectively reduced, and the corrosion resistance of the magnet is improved.

Description

technical field [0001] The invention relates to a rare earth permanent magnet material, which belongs to the technical field of materials, in particular to a permanent magnet material with high temperature resistance and high magnetic performance. Background technique [0002] The advantages of NdFeB magnets are high cost performance and good mechanical properties; the disadvantages are that the Curie temperature point is low, the temperature characteristics are poor, and it is easy to be pulverized and corroded. It must be adjusted by adjusting its chemical composition and adopting surface treatment methods. Improvement can meet the requirements of practical application. [0003] NdFeB magnets are divided into sintered type and bonded type according to different production methods. Compared with sintered permanent magnets, bonded magnets have many advantages such as high cost performance, convenient forming of special-shaped magnets, high processing precision, good toughne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/057
CPCH01F1/0576
Inventor 周连明
Owner JIANGSU PULONG MAGNETIC ELECTRICITY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products