Synthesis method of water-absorbent resin with novel structure

A technology of water-absorbent resin and a new structure, which is applied in the field of synthesis of water-absorbent resin with a new structure, can solve the problems of low gel strength, pressure absorption rate of water-absorbent resin, poor liquid-through performance, and low molecular cross-linking degree, etc., to achieve high The effect of gel strength, good water retention capacity, and high absorption rate

Active Publication Date: 2017-07-28
SHANDONG NUOER BIOLOGICAL TECH
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Water-absorbent resin is a polymer with a three-dimensional network structure. If the grid is large and the molecular freedom is large, the water absorption ratio will be higher. The pressure absorption rate and liquid perme

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] A method for synthesizing a water-absorbent resin with a new structure. The method consists of raw materials in parts by weight: 200-300 parts by weight of acrylic acid, 1-5 parts of a crosslinking agent, 700-800 parts of deionized water, 0.5-2 parts of a redox initiator, and octane Alcohol 50-80, ethanol 10-80, butanediol diglycidyl ether 5-15, aluminum sulfate 20-40, silicon dioxide 2-5 and sodium hydroxide solution; the preparation method steps are as follows:

[0018] (1) After adding acrylic acid, deionized water and cross-linking agent into the reactor for mixing, pass nitrogen gas to remove oxygen, then add initiator to polymerize at a temperature of 20-25°C and raise the temperature naturally;

[0019] (2) The reaction is over if the temperature does not rise, and then kept at a temperature of 80-90°C for 90-150 minutes, and granulated to obtain resin colloidal particles;

[0020] (3) Resin colloid particles are added to sodium hydroxide solution, dried, crushed...

Embodiment 1

[0030] Select the following raw materials in parts by weight: Acrylic acid 220, tetraallyloxyethane 1, deionized water 780, potassium persulfate 0.3, ascorbic acid 0.8, octane glycol 52, ethanol 40, butanediol diglycidyl ether 8, sulfuric acid Aluminum 24, silicon dioxide 2 and 48% sodium hydroxide solution 85.8; the specific preparation process is as follows:

[0031] (1) Add acrylic acid, deionized water, tetraallyloxyethane and blow high-purity nitrogen into the reactor; add potassium persulfate and ascorbic acid to initiate polymerization at 20-25°C and raise the temperature naturally;

[0032] (2) The reaction is considered as the end of the reaction when the temperature no longer rises. The temperature peak is about 85-90°C, and the temperature is kept at 82°C for 90 minutes. The reacted colloid is granulated to obtain resin colloid particles;

[0033] (3) The resin colloidal particles are neutralized by adding sodium hydroxide solution, drying the colloidal particles ne...

Embodiment 2

[0049] Select the following raw materials in parts by weight: Acrylic acid 250, trimethylolpropane triacrylate 1.2, deionized water 750, potassium persulfate 0.34, ascorbic acid 0.9, octane glycol 59, ethanol 40, butanediol diglycidyl ether 9, Aluminum sulfate 27.3, silicon dioxide 2.3 and 48% sodium hydroxide solution 97.5; the specific preparation process is as follows:

[0050] (1) Add acrylic acid, deionized water, trimethylolpropane triacrylate into the reactor and blow high-purity nitrogen gas; add potassium persulfate and ascorbic acid to initiate polymerization at 20-25°C and raise the temperature naturally;

[0051] (2) The reaction is considered as the end of the reaction when the temperature no longer rises. The temperature peak is about 85-90°C, and the temperature is kept at 82°C for 90 minutes. The reacted colloid is granulated to obtain resin colloid particles;

[0052] (3) The resin colloidal particles are neutralized by adding sodium hydroxide solution, drying...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a synthesis method of water-absorbent resin with a novel structure. The synthesis method is characterized by comprising, by weight, 200-300 parts of acrylic acid, 1-5 parts of cross-linking agents, 700-800 parts of deionized water, 0.5-2 parts of oxidation reduction initiating agents, 50-80 parts of octylene glycol, 10-80 parts of ethyl alcohol, 5-15 parts of butanediol diglycidyl ether, 20-40 parts of aluminum sulfate, 2-5 parts of silicon dioxide and sodium hydroxide solution. According to the synthesis method, the acrylic acid is firstly polymerized at the indoor temperature and then neutralized by the aid of the sodium hydroxide solution, triple cross-linking treatment of the surface is performed, so that the water-absorbent resin has high gel intensity and pressurizing absorption capacity, good liquid passing performance and water retention capacity and fundamentally solves the problem that gel intensity and absorption ratio cannot be completely considered, and the synthesized water-absorbent resin is quite excellent in performance and has high infiltration speed, super-low reverse osmosis and super-dry and comfortable surfaces when being applied to paper diapers.

Description

technical field [0001] The invention relates to the field of polymerized functional polymer chemical additives, in particular to a method for synthesizing a water-absorbing resin with a novel structure. Background technique [0002] Water-absorbent resin is a polymer with a three-dimensional network structure. If the grid is large and the molecular freedom is large, the water absorption ratio will be higher. The pressurized absorption rate and liquid permeability will also be relatively poor, so the water absorption rate and gel strength are a pair of contradictions that cannot be achieved at the same time. Most of the water-absorbent resins on the market currently have this problem. At present, when water-absorbent resins are applied to daily hygiene products such as women's sanitary napkins, baby diapers, and adult incontinence diapers, especially when applied to baby diapers, the requirements for surface dryness are getting higher and higher. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L33/02C08K5/053C08K3/36C08F220/06C08F4/40C08J3/24
CPCC08F4/40C08F220/06C08J3/24C08J2333/02C08K3/36C08K5/053C08L33/02
Inventor 荣敏杰李振许永升于庆华荣帅帅
Owner SHANDONG NUOER BIOLOGICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap