A kind of preparation method of automobile carpet material with self-adhesive styrofoam

A technology for car carpets and styrofoam, applied in adhesives, vehicle parts, adhesive types, etc., can solve the problems of secondary air pollution in the car, non-self-adhesive carpet adhesive, etc., reduce safety hazards, and be easy to use , the effect of low density

Active Publication Date: 2018-09-28
CHANGZHOU VOCATIONAL INST OF ENG
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem solved by the present invention is: the current car carpet back glue has no self-adhesiveness, and the foaming material used is chemically foamed, and the residual chemical foaming agent will cause secondary air pollution in the car

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of automobile carpet material with self-adhesive styrofoam

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] First adopt emulsion method to synthesize acrylate emulsion: concrete steps are (1) dissolving of emulsion, under normal temperature in reactor, nonylphenol polyoxyethylene ether, sodium dodecylbenzenesulfonate are dissolved in deionized water, Stir continuously to form an emulsifier solution; (2) Add butyl acrylate, butyl methacrylate, and methacrylic acid monomers to the emulsifier solution, stir quickly and evenly, then start to reduce the stirring speed, and gradually heat up to 80°C, After the solution reacts with blue light, add ammonium persulfate aqueous solution dropwise. After the ammonium persulfate aqueous solution is added dropwise, the temperature rises to 85°C, and the reaction ends after 2 hours of heat preservation; (3) cool the reaction product to 30°C, add ammonia water to adjust When the pH value reaches neutral, the acrylic emulsion can be obtained by discharging.

[0020] The natural rubber emulsion uses sodium pentachlorophenate low-ammonia latex ...

Embodiment 2

[0024] First adopt emulsion method to synthesize acrylate emulsion: concrete steps are (1) dissolving of emulsion, under normal temperature in reactor, nonylphenol polyoxyethylene ether, sodium dodecylbenzenesulfonate are dissolved in deionized water, Stir continuously to form an emulsifier solution; (2) Add butyl acrylate, butyl methacrylate, and methacrylic acid monomers to the emulsifier solution, stir quickly and evenly, then start to reduce the stirring speed, and gradually heat up to 80°C, After the solution reacts with blue light, add ammonium persulfate aqueous solution dropwise. After the ammonium persulfate aqueous solution is added dropwise, the temperature rises to 85°C, and the reaction ends after 2 hours of heat preservation; (3) cool the reaction product to 30°C, add ammonia water to adjust When the pH value reaches neutral, the acrylic emulsion can be obtained by discharging.

[0025] The natural rubber emulsion uses sodium pentachlorophenate low-ammonia latex ...

Embodiment 3

[0029] First adopt emulsion method to synthesize acrylate emulsion: concrete steps are (1) dissolving of emulsion, under normal temperature in reactor, nonylphenol polyoxyethylene ether, sodium dodecylbenzene sulfonate are dissolved in deionized water, Stir continuously to form an emulsifier solution; (2) Add butyl acrylate, butyl methacrylate, and methacrylic acid monomers to the emulsifier solution, stir quickly and evenly, then start to reduce the stirring speed, and gradually heat up to 80°C, After the solution reacts with blue light, add ammonium persulfate aqueous solution dropwise. After the ammonium persulfate aqueous solution is added dropwise, the temperature rises to 85°C, and the reaction ends after 2 hours of heat preservation; (3) cool the reaction product to 30°C, add ammonia water to adjust When the pH value reaches neutral, the acrylic emulsion can be obtained by discharging.

[0030] The natural rubber emulsion uses sodium pentachlorophenate low-ammonia latex...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a car carpet material with a self-adhesive foam adhesive and belongs to the technical field of high polymer materials. The preparation method includes: using acrylate as the main raw material, subjecting the acrylate to polymer blending modification, adding a physical foaming agent and modified nano cellulose to obtain a self-adhesive foam carpet material back adhesive, coating a nonwoven-fiber carpet or a cotton-spun carpet material with the self-adhesive foam carpet material back adhesive, and drying to obtain a self-adhesive carpet product. The carpet material having certain self-adhesive performance is free of low-molecular volatile matter, environmentally friendly, nontoxic, low in density, capable of being tightly adhered to the inner bottom surface of a car, capable of avoiding shifting during use and convenient to use.

Description

technical field [0001] The invention relates to a method for preparing an automobile carpet material with self-adhesive foaming glue, and belongs to the technical field of polymer materials. Background technique [0002] With the rapid development of my country's automobile industry, the amount of carpet materials in automobile interior parts is also increasing. At present, the car carpet materials mainly include PVC carpet, PET needle-punched carpet, EVA composite carpet, PA tufted carpet and so on. Among them, the PVC material carpet does not meet the air quality standards in the car due to the volatilization of toxic and harmful substances such as plasticizers at high temperatures. At present, the carpets sold on the market will shift during use, especially the shift of the carpet under the driver's feet, which will cause potential safety hazards in driving. At present, the weight reduction of automobile materials is an important development direction. As one of the int...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/08C09J133/10C09J107/02C09J11/08C09J11/06C08J9/00C08J9/12B60N3/04
CPCB60N3/042C08J9/0061C08J9/12C08J2333/08C08J2333/10C08J2407/02C08L2203/14C08L2205/03C09J11/06C09J11/08C09J133/08C09J133/10C08L7/02C08L1/02C08K5/20
Inventor 马立波陆红霞高炜斌徐亮成李珊珊张枝苗熊煦李秀华陈晓松王自瑛杨小林薛叙明
Owner CHANGZHOU VOCATIONAL INST OF ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com