Fluororubber-containing modified waterproof coating

A technology of waterproof coating and fluorine-containing rubber, applied in the direction of coating, etc., can solve the problems of unsafe use, safety problems, toxicity, etc., and achieve the effect of simple raw material combination, good film forming effect and long storage time

Inactive Publication Date: 2017-09-01
阎玉珍
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The waterproof coating of the invention has a relatively high proportion of α-methylstyrene linear terpolymer, which is toxic and unsafe to use. If this component is not used, it will affect the base adhesion of the waterproof coating
[0006] In summary, the exis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example 1

[0025] A modified waterproof coating of fluorine rubber, in kg, each component is:

[0026] Fluororubber: a copolymer of hexafluoropropylene, tetrafluoroethylene and ethylene totaling 35kg. The preparation method of fluororubber is to add hexafluoropropylene, tetrafluoroethylene and ethylene to an internal mixer in sequence and melt for 2h at 140℃;

[0027] Film-forming agent: 35kg of polymer modified asphalt, the preparation method of polymer modified asphalt is 90 # Asphalt and vacuum three-line oil are mixed in a ratio of 3:1, heated to 150°C, swelled for 45 minutes, grind with a colloid mill for 60 minutes, and finally fly ash is added and stirred at high speed for 30 minutes;

[0028] Natural surfactant: sorbitan monooleate 2kg;

[0029] High temperature improver: polypropylene 15kg;

[0030] Filling material: silica fume 10kg;

[0031] Flame retardant: 4.5kg of zinc borate, 4.5kg of barium borate;

[0032] pH adjuster: NaOH solution 4kg;

[0033] The balance is an a...

Example Embodiment

[0036] Example 2

[0037] A modified waterproof coating of fluorine rubber, in kg, each component is:

[0038] Fluorine rubber: a total of 45kg of copolymer of hexafluoropropylene, tetrafluoroethylene and ethylene. The preparation method of fluororubber is to add hexafluoropropylene, tetrafluoroethylene and ethylene to an internal mixer in sequence, and melt at 160℃ for 1h;

[0039] Film-forming agent: 25kg of polymer modified asphalt, the preparation method of polymer modified asphalt is 90 # Asphalt and vacuum three-line oil are mixed at a ratio of 3:1, heated to 160°C, swelled for 30 minutes, grind with a colloid mill for 120 minutes, finally added fly ash, and stirred at high speed for 30 minutes;

[0040] Natural surfactant: 5kg of sorbitan monooleate;

[0041] High temperature improver: polypropylene 10kg;

[0042] Filling material: light calcium 15kg;

[0043] Flame retardant: 3kg of zinc borate, 3kg of barium borate;

[0044] pH adjuster: NaOH solution 4kg;

[0045] The balance is a...

Example Embodiment

[0048] Example 3

[0049] A modified waterproof coating of fluorine rubber, in kg, each component is:

[0050] Fluororubber: a copolymer of hexafluoropropylene, tetrafluoroethylene and ethylene totaling 40kg. The preparation method of fluororubber is to add hexafluoropropylene, tetrafluoroethylene and ethylene to an internal mixer in sequence, and melt for 1.5h at 155℃ ;

[0051] Film-forming agent: 30kg of polymer modified asphalt, the preparation method of polymer modified asphalt is 90 kg # Mix asphalt and vacuum three-line oil in a ratio of 3:1, heat to 150℃, swell for 40 minutes, grind with a colloid mill for 80 minutes, add fly ash, and stir at high speed for 30 minutes;

[0052] Natural surfactant: sorbitan monooleate 3.5kg;

[0053] High temperature improver: polypropylene 12kg;

[0054] Filling material: light calcium 13kg;

[0055] Flame retardant: zinc borate 4kg, barium borate 4.5kg;

[0056] pH adjuster: NaOH solution 1.5kg;

[0057] The balance is an aqueous solution containi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Bond strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a fluororubber-containing modified waterproof coating which is prepared from the following components in percentage by weight: 35-45 percent of fluororubber, 25-35 percent of a film forming agent, 2-5 percent of a natural surfactant, 10-15 percent of a high temperature improving agent, 10-15 percent of a filler, 6-9 percent of a flame retardant and 1-4 percent of a pH regulator. The invention also discloses a preparation method of the waterproof coating. The preparation method comprises the following steps: adding the fluororubber, the film forming agent, the natural surfactant and the flame retardant in a sealed reaction kettle, continuously adding the filler for reaction for 1-3h under the condition with the temperature being 80-100 DEG C, cooling to 40-50 DEG C, adding the pH regulator, and carrying out continuous reaction to obtain the fluororubber-containing modified waterproof coating. As for the fluororubber-containing modified waterproof coating, by using the fluororubber, the formation of the waterproof coating is promoted, the adhesion performance of the waterproof coating to an interface is improved, the waterproof effect is better, and the waterproof coating is safe and environmentally friendly to use and cannot bring negative effects.

Description

technical field [0001] The invention relates to a waterproof coating, in particular to a modified waterproof coating of fluorine-containing rubber. Background technique [0002] There are two types of waterproof materials on the market: one is polyurethane waterproof coatings. Such materials are generally made of polyurethane and coal tar as raw materials. The tar gas it volatilizes is highly toxic and not easy to remove, so it was banned in China in 2000. The polyurethane waterproof coating that is still on sale uses asphalt instead of coal tar as a raw material. However, when using this kind of coating, it is generally diluted with organic solvents such as toluene and xylene, so it also contains toxicity; the other type is polymer cement-based waterproof coating. It is composed of a variety of water-based polymer emulsions and high-quality cement mixed with various additives. The flexibility of the polymer (resin) and the rigidity of the cement are integrated, making ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D127/20C09D7/12
CPCC09D127/20C08K2003/2241C08K2003/265C08K2003/387C08K2201/014C08L2205/035C08L95/00C08L91/00C08L23/12C08K13/02C08K3/38C08K5/103C08K3/34C08K3/26C08K3/36C08K3/22
Inventor 阎玉珍
Owner 阎玉珍
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap